Effects of finish rolling temperature on the microstructure and mechanical properties of X80 high deformability pipeline steel

ZHENG Xiao-fei1),KANG Yong-lin1),MENG De-liang1),AN Shou-yong2),XIA Dian-xiu2)1) School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China2) Jinan Iron and Steel Group Co., Jinan 250101, China  
The finish rolling temperature was determined at 830, 800 and 775 ℃ to investigate its effect on the microstructure and mechanical properties of high deformability pipeline steel. The grain size and volume fraction of ferrite and M/A islands in the steels were measured by metallographic microscopy and image processing software. Electron backscatter diffraction (EBSD) analysis was conducted to ascertain the effective grain size and the volume fraction of high angle grain boundaries. The M/A island forms were observed by transmission electron microscopy (TEM). A quasi-static tensile testing machine was used to test the yield strength, tensile strength and uniform elongation of the three steels. It is indicated that when the finish rolling temperature is 800 ℃, the steel has the best mechanical properties and can meet the requirements of X80 high deformability pipeline steel.
【CateGory Index】: TG335.1
Download(CAJ format) Download(PDF format)
CAJViewer7.0 supports all the CNKI file formats; AdobeReader only supports the PDF format.
【Citations】
Chinese Journal Full-text Database 1 Hits
1 JIAO Duotian,CAI Qingwu,WU Huibin National Engineering Research Center for Advanced Rolling Technology,University of Science and Technology Beijing, Beijing 100083;EFFECTS OF COOLING PROCESS AFTER ROLLING ON MICROSTRUCTURE AND YIELD RATIO OF HIGH-STRAIN PIPELINE STEEL X80[J];Acta Metallurgica Sinica;2009-09
【Secondary Citations】
Chinese Journal Full-text Database 3 Hits
1 LI Long~1 DING Hua~(1,2) WEN Jinglin~2 SONG Hongmei~3 ZHANG Pijun~3 1.School of Materials and Metallurgy,Northeastern University.Shenyang 110004 2.The State Key Lab.of Rolling and Automation of Northeastern University,Shenyang 110004 3.Baosteel Technology Center,Baoshan Iron & Steel Group Co.,Shanghai 201900;Mechanical behaviors of a low carbon steel with a duplex microstructure of bainite and ferrite[J];Chinese Journal of Materials Research;2007-05
2 YU Qing-bo1,2,3,ZHAO Xian-ping4,SUN Bin4, YU Ai-min4,CHEN Bo4(1.Mechanical and Electronic Department,Xuzhou Institute of Technology,Xuzhou 221008,Jiangsu,China;2.Materials Science and Engineering Postdoctoral Working Station,Harbin Institute of Technology,Harbin 150002,Heilongjiang,China;3.College of Mechanical Engineering,Qiqihar University,Qiqihar 161006,Heilongjiang,China; 4.Technology Center,Anyang Iron and Steel Group Corp.,Anyang 455004,Henan,China);Yield-Strength Ratio of Steel Plate for High-Rise Building[J];Iron & Steel;2007-11
3 LI He-lin,LI Xiao,JI Ling-kang,CHEN Hong-da;Strain-based Design for Pipeline and Development of Pipe Steels with High Deformation Resistance[J];Welded Pipe and Tube;2007-05
©2006 Tsinghua Tongfang Knowledge Network Technology Co., Ltd.(Beijing)(TTKN) All rights reserved