Fatigue crack growth rate of aluminum alloys under Ⅰ-Ⅲ combined loading
WANG Jian-guo Wingdingsj,LI Lu,WANG Lian-qing,WANG Hong-yingState Key Laboratory for Advanced Metals and Materials,University of Science and Technology Beijing,Beijing 100083,China
Fatigue crack propagation laws of aluminum alloys under Ⅰ-Ⅲ combined loading were investigated by finite element simulation and fatigue crack growth experiment,and the stress intensity factors under various loading conditions,the energy field around the crack front and the radius of the plastic zone were obtained.The effects of mode Ⅲ loading on the energy field around the crack front and the stress intensity factor under mode Ⅰ loading were analyzed on the basis of studies on mode Ⅰ loading.Numerical results show that under the condition of Ⅰ-Ⅲ combined loading,the stress intensity factor decreases with the increasing of mode Ⅲ loading,but the radius of the plastic zone near the crack increases.Mode Ⅲ static loading can slow down fatigue crack propagation,and to some extent,the fatigue crack growth rate under combined Ⅰ-Ⅲ loading decreases with the increasing of mode Ⅲ static loading.Mode Ⅲ cyclic loading can speed up fatigue crack propagation,and to some extent,the fatigue crack growth rate under Ⅰ-Ⅲ combined loading increases with the increasing of mode Ⅲ loading.
CAJViewer7.0 supports all the CNKI file formats; AdobeReader only supports the PDF format.