《Journal of University of Science and Technology Beijing》 2011-10
Add to Favorite Get Latest Update

Effect of hot galvanizing processes on the mechanical properties of non-Si and P-added TRIP steel

HUANG Wei,TANG Di,JIANG Hai-tao,DING Wei,XIE Lei-lei Engineering Research Institute of University of Science and Technology Beijing,Beijing 100083,China  
The effect of hot galvanizing processes on the mechanical properties and microstructure of non-Si and P-added TRIP steel was studied by using optical microscopy,transmission electron microscopy,X-ray diffraction and tensile test.It is shown that the steel with tensile strength over 780 MPa and percentage elongation after fracture over 24% can be obtained.The temperatures of intercritical annealing and isothermal bainitic transformation(IBT) have little influence on the mechanical properties,while IBT time plays significant contribution to them.When the IBT time prolongs from 20 s to 60 s,the sample reaches the best performance.Its yielding strength rises by 65 MPa,tensile strength decreases by 45 MPa,and elongation increases obviously from 23.01% to 27.56%,respectively.The microstructure of non-Si and P-added TRIP steel consists of ferrite,bainite,retain austenite and martensite.As the IBT time shortens,the amount and stability of austenite get decreased,the content of martensite increases markedly,and the mechanical characteristics of the steel transform from TRIP steel's to dual-phase steel's gradually.
【Fund】: 国家自然科学基金资助项目(50804005)
【CateGory Index】: TG142.1
Download(CAJ format) Download(PDF format)
CAJViewer7.0 supports all the CNKI file formats; AdobeReader only supports the PDF format.
【Citations】
Chinese Journal Full-text Database 3 Hits
1 XIONG Ziliu1),JIANG Haitao1),CAI Qingwu1),TANG Di1),LIU Rendong2)1)School of Materials Science and Engineering,University of Science and Technology Beijing,Beijing 100083,China 2)Technology center,Angang Steel Company Limited,Anshan 114021,China;Tension test and microstructural mechanism for eliminating the yield platform of TRIP steel[J];Journal of University of Science and Technology Beijing;2008-04
2 JING Cainian1,2),LIU Zaixue1),WANG Zuocheng2),WANG Minggang1),KIM Sungjoon3)1) School of Materials Science and Engineering,Shandong University of Architecture,Jinan 250101,China2) School of Materials Science and Engineering,Shandong University,Jinan 250061,China3) Korea Institute of Machinery and Materials,Changwon 641010,Korea;Effects of intercritical annealing treatment on the phase transformation and mechanical properties of 0.15C-1.5Mn-1.5Al TRIP-aided cold-rolled steel sheets[J];Journal of University of Science and Technology Beijing;2008-06
3 DING Wei,TANG Di,JIANG Hai-tao,HUANG Wei National Engineering Research Center for Advanced Rolling Technology,University of Science and Technology Beijing,Beijing 100083,China;Annealing processing parameters and microstructure evolution of 780MPa hot dip galvanizing TRIP steel[J];Journal of University of Science and Technology Beijing;2010-06
【Co-citations】
Chinese Journal Full-text Database 9 Hits
1 XU Kun1),LIU Guo-quan1,2)1)School of Materials Science and Engineering,University of Science and Technology Beijing,Beijing 100083,China 2)State Key Laboratory for Advanced Metals and Materials,University of Science and Technology Beijing,Beijing 100083,China;Effect of Nb microalloying on the microstructure and mechanical properties of high-Al cold-rolled TRIP steel[J];Journal of University of Science and Technology Beijing;2009-10
2 DING Wei,TANG Di,JIANG Hai-tao,HUANG Wei National Engineering Research Center for Advanced Rolling Technology,University of Science and Technology Beijing,Beijing 100083,China;Annealing processing parameters and microstructure evolution of 780MPa hot dip galvanizing TRIP steel[J];Journal of University of Science and Technology Beijing;2010-06
3 XIONG Zi-liu,CAI Qing-wu,JIANG Hai-tao,TANG Di(Engineering Research Institute,University of Science And Technology Beijing,Beijing 100083,China);Research on Mechanical Stability of Austenite in TRIP Steels[J];Journal of Materials Engineering;2011-03
4 XIONG Zi-liu,CAI Qing-wu,JIANG Hai-tao,TANG Di,MI Zhen-li(Engineering Research Institute,University of Science and Technology Beijing,Beijing 100083,China);Microstructure of TRIP1000 Steel and Deformation Behavior of Different Microstructure[J];Materials for Mechanical Engineering;2010-10
5 XU Kun~1,LIU Guo-quan~(1,2)(1.School of Materials Science and Engineering,University of Science and Technology Beijing,Beijing 100083,China;2.State Key Laboratory for Advanced Metals and Materials,Beijing 100083,China);Effect of isothermal bainite treatment on microstructure and mechanical properties of 0.22C-1.63Mn-1.5Al cold-rolled TRIP steel[J];Transactions of Materials and Heat Treatment;2009-05
6 XIONG Zi-liu,CAI Qing-wu,JIANG Hai-tao,TANG Di,ZHANG Mei,LI Qiang(School of Materials Science and Engineering,University of Science and Technology Beijing,Beijing 100083,China);Heredity of hot rolled microstructure in a high strength TRIP steel[J];Transactions of Materials and Heat Treatment;2010-01
7 XU Kun1,LIU Guo-quan1,2(1.School of Materials Science and Engineering,University of Science and Technology Beijing,Beijing 100083,China;2.State Key Laboratory for Advanced Metals and Materials,Beijing 100083,China);Influence of Al content and heat treatment on microstructure and properties of cold rolled TRIP steel[J];Heat Treatment of Metals;2009-05
8 Zhou Hongyan,Yang Qingyuan,Zhang Hua(Hebei State-controlled Holding Mine Development and Investment Co.,Ltd.,Shijiazhuang,Hebei,050000);STUDY ABOUT INFLUENCE OF AGING TEMPERATURE IN CONTINUOUS ANNEALING ON STRUCTURE AND PROPERTY OF COMPLEX Si-Al TRIP STEEL[J];Hebei Metallurgy;2011-06
9 SUN Tingting,TANG Di,JIANG Haitao,TIAN Zhiqiang (National Engineering Research Center for Advanced Rolling Technology,University of Science and Technology Beijng,Beijing 100083,China);Effect of Over-aging Temperature on Microstructure and Properties of Cold-rolling Dual Phase Steel[J];Hot Working Technology;2009-20
【Secondary Citations】
Chinese Journal Full-text Database 10 Hits
1 ZHANG Yinghui~(1,2)), KANG Yonglin~(1)), YU Hao~(1)), LIU Xiao~(3)), FANG Yuan~(3)) 1) Materials Science and Engineering School, University Science and Technology Beijing, Beijing 100083, China 2) Jiangxi University of Science and Technology, Ganzhou 341000, China 3) Shanghai Baosteel Group, Shanghai 200941, China;Microstructure and mechanical properties of TRIP steel by TSCR process[J];Journal of University of Science and Technology Beijing;2005-06
2 JING Cainian1,2),LIU Zaixue1),WANG Zuocheng2),WANG Minggang1),KIM Sungjoon3)1) School of Materials Science and Engineering,Shandong University of Architecture,Jinan 250101,China2) School of Materials Science and Engineering,Shandong University,Jinan 250061,China3) Korea Institute of Machinery and Materials,Changwon 641010,Korea;Effects of intercritical annealing treatment on the phase transformation and mechanical properties of 0.15C-1.5Mn-1.5Al TRIP-aided cold-rolled steel sheets[J];Journal of University of Science and Technology Beijing;2008-06
3 Qiang Liu1), Di Tang1), Hai-tao Jiang1), Ren-dong Liu2), and Xiao-yong Tang1) 1) National Engineering Research Center for Advanced Rolling Technology, University of Science and Technology Beijing, Beijing 100083, China 2) Research and Development Center, Anshan Iron and Steel (Group) Corp., Anshan 114001, Liaoning, China;Research and development of 780 MPa cold rolling TRIP-aided steel[J];矿物冶金与材料学报(英文版);2009-04
4 <author>I Wen, LI Lin, FU Renyu, GAO Beibei (School of Materials Science and Engineering, Shanghai University, Shanghai 200072);<title>fluence of Intercritical Annealing Temperature on Microstructure and Mechanical Properties in 0.11C-0.6Si-1. 5Mn Cold Rolling TRIP Steel Sheets[J];Iron and Steel;2004-08
5 JIANG Hai-tao1,TANG Di1,LIU Qiang1,LIU Ren-dong2,YAN Ling2(1.National Engineering Research Center for Advanced Rolling Technology,University of Science and Technology Beijing,Beijing 100083,China;2.Technology Centre,Anshan Iron and Steel Group Co.,Anshan 114009,Liaoning,China);Investigation of Retained Austenite and Its Stability in TRIP Steel[J];Iron & Steel;2007-08
6 JING Cai-nian~1,WANG Zuo-cheng~1,KIM SungJoon~2,LEE ChangGil~2,LEE TaeHo~2 (1.School of Materials Science and Engineering,Shandong University,Ji′nan Shandong 250061,China; 2.Korea Institute of Machinery and Materials,Changwon 641010,Korea);Effects of Copper and Annealing Temperature on the Microstructure and Mechanical Properties of TRIP Cold-Rolled Steel Sheets[J];Heat Treatment of Metals;2004-09
7 JING Cai-nian~(1,2),WANG Zuo-cheng~2,HAN Fu-tao~2 (1.Material Department,Shandong Institute of Architecture and Engineering,Ji′nan,Shandong 250014,China; 2.School of Materials Science and Engineering,Shandong University,Ji′nan,Shandong 250061,China);Research Progress of the Influencing Factors on Transformation Induced Plasticity[J];Heat Treatment of Metals;2005-02
8 YIN Yunyang YANG Wangyue School of Materials Science and Engineering,University of Science and Technology Beijing,Beijing 100083 LI Longfei SUN Zuqing WANG Xitao State Key Laboratory for Advanced Metals and Materials,University of Science and Technology Beijing,Beijing 100083;INFLUENCE OF THE PARTIAL SUBSTITUTION OF Si BY Al ON THE MICROSTRUCTURE OF HOT ROLLED TRIP STEELS BASED ON DYNAMIC TRANSFORMATION OF UNDERCOOLED AUSTENITE[J];Acta Metallurgica Sinica;2008-11
9 Zhang Wangfeng,Chen Yumei,Zhu Jinhua (Xi′an Jiaotong University, Xi′an 710049, China);Study on a New Type of Tensile Curve[J];JOURNAL OF XI'AN JIAOTONG UNIVERSITY;1999-10
10 LI Lin1, DE COOMAN B C2, LIU Ren-dong3, VLEUGELS J4, ZHANG Mei1, SHI Wen1(1. School of Materials, Shanghai University, Shanghai 200072, China; 2. Postech Graduate School of Ferrous Technology, Pohang University of Science and Technology, Pohang 790-784, South Korea; 3. Technique Center of Ansteel, Ansteel Company, Anshan 114001, Liaoning, China; 4. Department of MTM, Katholieke Universiteit Leuven, Kasteelpark Arenberg 44 B-3001, Belgium);Design of TRIP Steel With High Welding and Galvanizing Performance in Light of Thermodynamics and Kinetics[J];钢铁研究学报(英文版);2007-06
©2006 Tsinghua Tongfang Knowledge Network Technology Co., Ltd.(Beijing)(TTKN) All rights reserved