Hot Corrosion Behavior of an Ion Plating NiCrAlY Coating with Aluminizing

REN Xin (Department of Materials Science and Engineering,Liaoning Technical University,Fuxin 123000,China)  
A NiCrAlY coating was deposited on a Ni-based superalloy by ion plating.Post-aluminizing was performed on the coating to improve the corresponding high-temperature properties.Hot corrosion behaviors in the presence of 75%Na2SO4+25% NaCl film at 850℃ of the coatings with and without aluminizing have been investigated.In 25%NaCl+75%Na2SO4 molten salt at 850℃,Cr2O3 scale formed on NiCrAlY coating at 40h,while at the same time a single layer of α-Al2O3 scale formed on the coating with post-aluminizing.The main oxide of Al2O3 remained on the surface of the coating with post-aluminizing,which obviously increased the resistance to hot corrosion of the coating.
【Fund】: 辽宁省教育厅资助项目(2005196)
【CateGory Index】: TG174.444
Download(CAJ format) Download(PDF format)
CAJViewer7.0 supports all the CNKI file formats; AdobeReader only supports the PDF format.
【Citations】
Chinese Journal Full-text Database 2 Hits
1 LIU Peng-fei,TAO Kai,ZHOU Xiang-lin,ZHANG Ji-shan(State Key Laboratory for Advanced Metals and Materials,Beijing University of Science and Technology,Beijing 100083,China);Research Progress in Wear and Corrosion Resistance Coating of Boiler Tubes[J];Surface Technology;2007-01
2 SHU Yonghua; WANG Fuhui; ZHOU Longjiang; WU Weitao (State Key Laboratory for Corrosion and Protection, Institute of Corrosion and Protection of Metals, The Chinese Academy of Sciences, Shenyang 110015);CORROSION BEHAVIOR OF A STEEL 1Cr_(11)Ni_2W_2MoV COATED WITH NaCl IN WATER VAPOR AT 500-700℃[J];ACTA METALLRUGICA SINICA;1998-05
【Co-citations】
Chinese Journal Full-text Database 10 Hits
1 XU Jin-yong1,2,TANG Wan-xing1,XU Min1,DU Li1,Gao Yuan2,XU Zhong2(1.Guilin University of Electronic Technology,Guilin 541004,China;2.Taiyuan University of Technology,Taiyuan 030024,China);Study on plasma surface metallurgy Mo-Cr alloy layer of mild steel[J];Ordnance Material Science and Engineering;2006-02
2 XU Jin-yong~(1,2),SONG Yi-mei~1,GAO Yuan~1,YU Yun-jiang~1,XU Zhong~2(1.Guilin University of Electronic Technology,Guilin 541004,Guangxi,Chain;2.Taiyuan University of Technology,Taiyuan 030024,Shanxi,Chain);Investigation on Microstructure and Property of Low-carbon Steel Surface Strengthened Layer[J];Acta Armamentarii;2006-06
3 Meng Bo1 Wang kai2(1.Department of Mechanical Engineering,Beijing Institute of Petro-chemical Technology,Beijing 102617;2.China Petroleum Pipeline Engineering Corporation,Shenyan 110045);Corrosion Behavior of 1Cr11Ni2W2MoV Stainless Steel in Acid Environment[J];Journal of Beijing Institute of Petro-Chemical Technology;2008-01
4 LIU Peng-fei,TAO Kai,ZHOU Xiang-lin,ZHANG Ji-shan(State Key Laboratory for Advanced Metals and Materials,Beijing University of Science and Technology,Beijing 100083,China);Research Progress in Wear and Corrosion Resistance Coating of Boiler Tubes[J];Surface Technology;2007-01
5 QU Yan-ping1,REN Gong-nian1,CHEN Tao2,XIAO Li1,GENG Xin1,HAO Jun-hong1(1.Shenyang University of Technology,Shenyang 110023,China;2.Liaoning Province Science Research Institute of Light Industry,Shengyang 110023,China);Study on Oxidation Resistance of Al-Si-Y Coating Fabricated by Arc Ion Plating[J];Surface Technology;2007-05
6 WANG Li-yan,ZHAO Ping(Xihua University,Chengdu 610039,China.);Corrosion about Hydrogen Permeation Barrier on Zirconium Hydride in High Temperature and Dioxide Environment[J];Surface Technology;2007-05
7 WANG Guo-fan,MIAO Lei,LUO Hui,ZHANG Wei-yi(College of Materials Science and Engineering,Shandong Jianzhu University,Jinan 250101,China);Oxidation Resistance of Aluminized Layer on Red Copper at Hight Temperature[J];Surface Technology;2008-03
8 ZHANG Zhong-li, LI De-yuan, ZHANG Nan-nan(College of Materials Science and Engineering, Shenyang University of Technology, Shenyang 110023, China);Interface Diffusion of Aluminum and Chromium in Electric Arc Spraying Coating at Elevated Temperature[J];Materials Protection;2005-08
9 XU Xiang-rong, HUANG Na-can, YANG Shao-min(Faculty of Material and Energy Sources, Guangdong University of Technology, Guangzhou 510643, China);Effect of Rare Earth in Surface Modification on High Temperature Oxidation Resistance and Corrosion Resistance of Materials[J];Materials Protection;2005-08
10 YANG Wen-dong a,HUANG Jian-feng b,CAO Li-yun b,XIA Chang-kui b(a.School of Chemistry and Chemical Engineering,b.School of Material Science and Engineering,Shanxi University of Science and Technology,Xi' an 710021,China);Research Progress and Development Trend of High Temperature Protective Coatings[J];Materials Protection;2009-01
China Proceedings of conference Full-text Database 6 Hits
1 LIU Jie Jiang Jincheng Xu Zhenxing Liu Junyou (1.Beijing.BKDR Metallurgy Engineering & Technology CO.LTD.,Beijing 100083;2.Material School,University of Science and Technology Beijing,Beijing 100083);Characteristic Analysis on High-temperature oxide film of Grid Plate of Grate-kiln[A];[C];2008
2 ZENG Gang~(1,2) LI Ming-wei~(1,3) HAN Jie-cai~2 HE Xiao-dong~2 (1.School of Material Science and Engineering,Harbin Institute of Technology,Harbin 150001,China; 2.Center for Composite Materials,Harbin Institute of Technology,Harbin 150001,China; 3.ChengDu Aircraft Design and Research Institute,Chengdu 610041,China);Oxidation behavior of microcrystalline Ni-11.5Cr-4.5Co-0.5Al superalloy sheet fabricated by electron beam physical vapor deposition (EB-PVD) at 800℃[A];[C];2007
3 CHEYan-min, ZHANG Hua-ming, CHENQi-an, ZHU Tao, MA Yu-ping, WANG Xiao-yan, WANGYing (Central Iron and Steel Research Institute, Beijing 100081, China;Kunming University of Science and Technology, Kunming 6500933, China;Maanshan Iron and Steel Co. Ltd. Technical Center, Maanshan 243000, China);An Investigation on Scale on SPHC Coil Rolled by CSP Processing[A];[C];2005
4 Gu chun yang~1 Shi xiao guang~2 Xu yan song~1 Zhang zi yin~2 Han bin~2 1.Hot Strip Mill; 2.Technology Center of AnGang Steel Co.Ltd;The Development of Hot Rolled Black Surface 355L Beam Steel Plates for Automobiles[A];[C];2008
5 REN Rui-ming CHEN Chun-huan LUAN Wei-zhi YANG De-xin (School of Materials Science & Engineering,Dalian Jiaotong University,Dalian 116028,China);The effect of surface nanocrystallization on oxidation resistance of 1Cr17 stainless steel[A];[C];2007
6 LI Chong, REN Zheng-yi, TONG Yong-xiang, LI Qing-fen, ZHU Chun-cheng, HE Xiao-dong (Center for Engineering Training, Harbin Engineering University, Harbin 150001, China);High temperature oxidation resistance of coating with hot-dipped Al-Si-RE[A];[C];2005
【Secondary Citations】
Chinese Journal Full-text Database 10 Hits
1 Xie Junquan;Song Shihui(Department of Materials Science and Engineering,USTB,Beijing 100083,PRC);Kinetic of Oxidation of Ni-Cr Low Alloying Steel under Vapour Atmosphere[J];JOURNAL OF UNIVERSITY OF SCIENCE AND TECHNOLOGY BEIJING;1996-06
2 ZHOU Song,CHEN Ben-rong,LIU Yong-zhong,ZHANG Hong-yan (Electric Power Experimental Research Institute, Chengdu, Sichuan 610071);Anti-wear and Anti-corrosion Treatment of Cooling Tubes for the Power Plant Boilers[J];China Surface Engineering;2003-01
3 ZHANG Ge~1,ZHOU Xiang-lin~(1,2),ZHANG Ji-shan~(1,2),SUN Dong-bai~2 g University of Science and Techology, Beijing 100083,China;2. Beijing Nano Surface Technology and Engineering Research Center, Beijing 100083,China);Synthesis of High Wear and Corrosion Resistance Coating for Hydraulic Turbine Transition Parts[J];Surface Technology;2004-01
4 FAN Zi-shuan,SUN Dong-bai,YU Hong-ying,et al(Beijing Surface Engineering Center of Nanometer Technology,University of Science and Technology Beijing,Beijing 100083,China).;Development of Hypersonic Flame Spraying Technology[J];Materials Protection;2004-09
5 JING Yong-wei~1, LIU Shao-guang~2(1. General Cogeneration Power Plant of Shanghai Petrochemical Co. Ltd., Shanghai 200540, China; 2. Zhejiang University, Hangzhou 310027, China);A Study on Erosion and Protective Methods of Water Wall Tubes of CFB Boilers[J];Power Engineering;2005-05
6 QI Huibin,GUO Yingzuo,HE Yedong,WANG Deren (Corrosion and Protection Center,Key Lab. of Corrosion,Erosion and Surface Tehcnology of Beijing, University of Science and Technology Beijing,Beijing 100083);HIGH TEMPERATURE CORROSION IN BOILERS OF COAL FIRED POWER PLANTS[J];Corrsion Science and Technology Protection;2002-02
7 XU Hai-yan~1, ZHOU Hui-di~1, CHEN Jian-min~1, FENG Zhi-zhong~1, ZHANG Cui-fang~2 Chemical Physics, Chinese Academy of Science, Lanzhou730000, China;2. Nanjing Engineering School, Nanjing211135, China );Investigative progression of thermo-sprayed high-performance ceramic composite coatings[J];;2004-06
8 XU Lian-yong, JING Hong-yang, HUO Li-xing, ZHANG Yu-feng The Material Science & Engineering Institute of Tianjin University, Tianjin 300072.China;Application of Hot Spraying Technology in Anti-corrosion for "Four Kinds of Piping" in Power Plant Boilers[J];Hubei Electric Power;2003-02
9 ZHANG Hui,HE Yi-zhu(School of Materials Science and Engineering,Anhui University of Technology,Ma'anshan 243002,China);Research Progress on Nano-particle Reinforced Metal Matrix Composite Coatings[J];Journal of Anhui University of Technology(Natural Science);2006-01
10 CHEN Guofeng, LOU Hanyi (State Key Laboratory for Corrosion and Protection, Institute of Corrosion and Protection of Metals, The Chinese Academy of Sciences, Shenyang 110015) Correspondent: CHEN Guofeng, Tel: (024)23915908, Fax: (024)23894149, E-mail: gu;OXIDATION BEHAVIOR OF THE SPUTTERED Ni-8Cr-3.5Al NANOCRYSTALINE COATING[J];ACTA METALLRUGICA SINICA;2000-01
©2006 Tsinghua Tongfang Knowledge Network Technology Co., Ltd.(Beijing)(TTKN) All rights reserved