Galvanic Corrosion Resistance of Magnesium Alloy with Microarc Oxidation Film and Coating

WANG Ling, ZHANG Wei, LI Jiuqing(Corrosion and Protection Center, School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China)Cailiao Baohu 2005, 38(4),12~14(Ch).  
The magnesium alloy coupled with carbon steel experiences serious corrosion in atmosphere environment. Fortunately, it is simple and effective to increase the corrosion resistance of the Mg alloy by combining microarc oxidation (MAO) with coating. Thus the galvanic corrosion resistance of the Mg alloy treated by MAO and organic coating was studied making use of neutral salt spray test, humidity cabinet test, and simulated wet industrial atmosphere test. The corrosion resistance of various organic coating systems was compared as well. It was found that the combined system of MAO film/organic coating had good galvanic corrosion resistance for the Mg alloy. The increase in the corrosion resistance of the Mg alloy was closely related to the characteristics of the MAO film having good adsorption and interlocking effect with the organic coating. However, further work is needed to realize the satisfactory protection of the Mg alloy in severe corrosive environment by combining the MAO film and organic coating.
【Fund】: 国家自然科学基金资助项目(50122115)
【CateGory Index】: TG174.451;TG174
Download(CAJ format) Download(PDF format)
CAJViewer7.0 supports all the CNKI file formats; AdobeReader only supports the PDF format.
【References】
Chinese Journal Full-text Database 3 Hits
1 ZHA Ji-li1, LONG Si-yuan1, SONG Dong-fu1, LIN Wei-hong2 , SHI Yong-jing (1. College of Material Science and Engineering, Chongqing University, Chongqing 400044, China; 2. Dongguan Yian Electrical Products Company Ltd.,Dongguan 523000, China);Effects of Pretreatments on Corrosion Resistance of Magnesium Alloy Organic Coatings[J];Materials Protection;2010-07
2 ZENG Rongchang CHEN Jun ZHANG Jin (School of Material Science and Engineering,Chongqing Institute of Technology,Chongqing 400050);Research and Progress of Galvanic Corrosion of Magnesium Alloys[J];Materials Review;2008-01
3 ZHANG Rong-fa1,WANG Fang-yuan2,HU Chang-yuan1,LI Wenkui1,XIANG Jun-huai1,DUO Shu-wang1,LI Ming-sheng1,HE Xiang-ming1(1 Jiangxi Key Laboratory of Surface Engineering,Jiangxi Science and Technology Normal University,Nanchang 330013,China;2 Jinhua College of Profession and Technology,Jinhua 321007,Zhejiang,China);Research Progress in Sealing Treatment of Anodic Coatings Formed on Magnesium Alloys[J];Journal of Materials Engineering;2007-11
【Citations】
Chinese Journal Full-text Database 5 Hits
1 ZHANG Yong\|jun, YAN Chuan\|wei, WANG Fu\|hui, CAO Chu\|nan (State Key Laboratory for Corrosion and Protection, Institute of Metal Research, The Chinese Academy of Sciences, Shenyang 110016, China);Application, Corrosion and Protection of Magnesium and Its Alloys[J];Materiais Protection;2002-04
2 TU Yun-hua, GAO Jin (Beijing Key Laboratory of Corrosion, Erosion and Surface Technology, School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China);Application and Development of Organic Protection Coating for Magnesium Alloys[J];Materials Protection;2003-12
3 HE Ji quan,WANG Zhan,ZHANG Wei,JIANG Jia nan,YANG Zhen bo,LI Jiu qing Material Science and Engineering School,USTB,Beijing 100083,China;GALVANIC CORROSION FOR MAGNESIUM ALLOY COUPLED WITH DISSIMILAR METALLIC MATERIALS DURING SALT SPRAY AND HUMIDITY CYCLE TEST[J];Corrosion Science and Technology Protection;2004-03
4 ZENG Rongchang, KE Wei, XU Yongbo, HAN Enhou, ZHU Ziyong (State Key Laboratory for Corrosion and Protection, Institute of Metal Research, The Chinese Academy of Sciences, Shenyang 110016;RECENT DEVELOPMENT AND APPLICATION OF MAGNESIUM ALLOYS[J];Acta Metallrugica Sinica;2001-07
5 JIANG Bailing,ZHANG Shufen,WU Guojian (Xi'an University of Technology,Xi'an 710048);THE STUDY OF THE CORROSION RESISTANCE OF THE CERAMIC COATINGS FORMED BY MICRO-ARC OXIDATION ON THE Mg-BASE ALLOY[J];Journal of Chinese Society For Corrosion and Protection;2002-05
【Co-citations】
Chinese Journal Full-text Database 10 Hits
1 WANG Wei-qing,PAN Fu-sheng,ZUO Ru-lin(College of Materials Science and Engineering,Chongqing University,Chongqing 400030,China);Recent development on corrosion and protective measures of magnesium alloys[J];Ordnance Material Science and Engineering;2006-02
2 KUANG Jun1,LI Gang1,HAO Shengzhi2,XIANG Jun1,QIU Xingwu1,QIU Ling1(1.School of Material Science and Engineering,Liaoning Technical University,Fuxin 123000,China;2.State Key Laboratory of Material Modification by Laser,Ion and Electron Beams,Dalian 116024,China);Corrosion property of magnesium alloy AZ31[J];Ordnance Material Science and Engineering;2009-01
3 CHEN Dongchu 1,2,WU Jianfeng1,GONG Weihui2,LI Wenfang2,XU Dongming1 (1.Foshan University,Foshan 528000,China;2.South China University of Technology,Guangzhou 510640,China);Optimization of the preparing process for the phytic acid based conversion coating on AZ91D magnesium alloy by orthogonal experiment[J];Ordnance Material Science and Engineering;2009-02
4 WANG Jingfeng1,2,LING Chuang1,2,PAN Fusheng1,TANG Aitao1,2,DING Peidao1(1.National Engineering Research Center for Magnesium Alloys,Chongqing University,Chongqing 400044,China;2.College of Materials Science and Engineering,Chongqing University,Chongqing 400044,China);Research progress in influence of alloying elements on damping properties of magnesium alloys[J];Ordnance Material Science and Engineering;2009-03
5 CHENG Zhe1,GUO Xuefeng2,YANG Wenpeng1,XU Chunjie1(1.School of Materials Science and Engineering,Xi′an University of Technology,Xi′an 710048,China; 2.School of Materials Science and Engineering,Henan Polytechnic University,Jiaozuo 454000,China);Microstructure and mechanical properties of severely deformed AZ31-1%Si-0.5%Sb alloy[J];Ordnance Material Science and Engineering;2011-01
6 XIAO Bing2,KANG Feng1,2,HU Chuankai1,2,SHU Dayu1,2,HUANG Shuhai1,2,NING Haiqing1,2(1.National Research and Application Center of Precise Forming,Chongqing 400039,China; 2.No.59 Research Institute of China Ordnance Industry,Chongqing 400039,China);Application of the light structure material in the defense industry abroad[J];Ordnance Material Science and Engineering;2011-01
7 ZHOU Lingzhan,ZHAO Guotian,ZHANG Lijun,XU Yongdong,ZHU Xiurong, SONG Yunkun,ZHANG Hua,CHEN Yun(Ningbo Branch of China Academy of Ordnance Science,Ningbo 315103,China);Influence of Gd on the surface film and corrosion characteristic of Mg-Zn alloy[J];Ordnance Material Science and Engineering;2011-02
8 LIU Yuangang, ZHANG Wei, GAO Jin, TU Yunhua, LI Jiuqing Materials Science and Engineering School, University of Science and Technology Beijing, Beijing 100083, China;Painting of magnesium alloys based on microarc electrodeposition[J];Journal of University of Science and Technology Beijing;2005-02
9 ZHANG Jixin ZHANG Wei LI Jiuqing Corrosion and Protection Center,Materials Science and Engineering School,University of Science and Technology Beijing,Beijing 100083,China;Inhibitor and the corroding behavior for a magnesium alloy in an ethylene glycol solution system[J];Journal of University of Science and Technology Beijing;2006-03
10 XIAO Kui1,2),DONG Chao-fang1,2),LI Xiao-gang1,2),WEI Dan3)1) Corrosion and Protection Center,University of Science and Technology Beijing,Beijing 100083,China 2) Beijing Key Laboratory for Corrosion-Erosion and Surface Technology,University of Science and Technology Beijing,Beijing 100083,China 3) Society Service Center,China Association for Science and Technology,Beijing 100081,China;Galvanic corrosion evaluation of magnesium alloys coupled with brass alloys studied by scanning Kelvin probe technology[J];Journal of University of Science and Technology Beijing;2010-08
China Proceedings of conference Full-text Database 10 Hits
1 Dong Guo,Zhongdong Yang,Zhanguo Fan (School of Materials and Metallurgy,Northeastern University,Shenyang 110004,China);Electroless Plating of Ni - P Coatings on Surface Metallization for Magnesium Alloys[A];[C];2007
2 WANG Feng~1,LIU Jing~1,LI Chen-xi~1,LV Dan~2,MAO Ping-li~1,LIU Zheng~1 (1.School of Materials Science and Engineering,Shenyang University of Technology, Shenyang 110870,Liaoning,China; 2.School of Science,Shenyang University of Technology,Shenyang 110870,Liaoning,China);Effect of Ca and Y Alloying on Microstnicture and Properties of Die Cast AZ91 Magnesium Alloy[A];[C];2011
3 YANG Qin~1 JIANG Bin~(1,2) (1 College of Materials Science and Engineering,Chongqing University,Chongqing 400044;2 Chongqing Engineering Research Center for Magnesium Alloys,Chongqing 400044);Progress in the Research of Corrosion and Protection of Magnesium Alloys[A];[C];2007
4 YANG Xu~(1,2) PAN Fusheng~1 ZHANG Dingfei~1 (1 College of Materials Science and Engineering,Chongqing University,Chongqing 400044;2 Department of Chemistry,the Third Military Medical University,Chongqing 400038);Surface Protection Technology for Corrosion on Magnesium Alloy with Organic Compounds[A];[C];2007
5 WU Haidong FAN Peigeng CAO Pengjun LIU Xiaowei (Chongqing University of Science and Technology,Chongqing 400050);Study on Chromium Phosphating Technology for Magnesium Alloy[A];[C];2007
6 ZHANG Dingfei DING Peidao PAN Fusheng PENG Jian(College of Materials Science and Engineering, Chongqing University, Chongqing 400044);Status Quo and Suggestion of Magnesium Alloy Research and Industrialization in Chongqing[A];[C];2004
7 Bo Yin,Liang Fang,Jia Hu,An-qiong Tang,Wen-hou Wei,Jiang He (1.Department of Applied Physics,Chongqing University,Chongqing,400044,P.R.China) (2.National Engineering Research Center for Magnesium Alloys,Chongqing University,Chongqing,400044,P.R.China);Preliminary Study on Improvement of Corrosion Resistance of Magnesium Alloy by Super-hydrophobic Coating Technology[A];[C];2010
8 HU Xiao-shi, ZHANG Yong-kun, ZHENG Ming-yi, WANG Yan-qiu, WU Kun (School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China);Study on damping capacity of AZ91D magnesium alloys[A];[C];2004
9 Han Xiaoying, Zhang Yanghuan, Wang Xinlin, Wang Guoqing ( Department of Functional Material Research , Central Iron & Steal Research Institute , Beijing 100081 , China);Application of Rare Earth on Mg-Based Hydrogen Storage Alloys[A];[C];2005
10 Xu Guangming, Bao Weiping, Zheng Jiawei, Zuo Yubo, Cui Jianzhong (Key Laboratory of National Education Ministry for Electromagnetic Processing of Materials , Northeastern University, Shenyang 110004, China);Solidification of Magnesium Alloy AZ61 under Magnetostatic Field[A];[C];2004
【Co-references】
Chinese Journal Full-text Database 10 Hits
1 TANG Quan-bo1, HUANG Shao-dong2, WU Tai-bin1 ( 1. Chongqing Technology and Business University, Chongqing 400067, China; 2. No.59 Institute of China Ordnance Industry, Chongqing 400039 , China);Application analysis of magnesium alloys in weapon components[J];Ordnance Material Science and Engineering;2007-02
2 Dai Changsong, Wu Yiyong, Wang Dianlong, Hu Xinguo;ELECTROLESS NICKEL PLATING ON MAGNESIUM AND MAGNESIAN ALLOYS[J];ORDNANCE MATERIAL SCIENCE AND ENGINEERING;1997-04
3 Li Yihong Zhu Liqun Liu Huicong Chen Yichi(School of Materials Science and Engineering,Beijing University of Aeronautics and Astronautics,Beijing 100083,China);Behavior of silica sol during the anodizing process of magnesium alloy[J];Journal of Beijing University of Aeronautics and Astronautics;2008-02
4 LIU Yuangang, ZHANG Wei, GAO Jin, TU Yunhua, LI Jiuqing Materials Science and Engineering School, University of Science and Technology Beijing, Beijing 100083, China;Painting of magnesium alloys based on microarc electrodeposition[J];Journal of University of Science and Technology Beijing;2005-02
5 LI Jun1), DONG Chaofang1), LI Xiaogang1,2) 1) Materials Science and Engineering School, University of Science and Technology Beijing, Beijing 100083, China 2) The State Key Laboratory for Corrosion and Protection, Shenyang 110016, China;Effect of pH value on the galvanic corrosion behaviour of Q235-304L couples in sulfur environment[J];Journal of University of Science and Technology Beijing;2006-01
6 ZHANG Jixin ZHANG Wei LI Jiuqing Corrosion and Protection Center,Materials Science and Engineering School,University of Science and Technology Beijing,Beijing 100083,China;Inhibitor and the corroding behavior for a magnesium alloy in an ethylene glycol solution system[J];Journal of University of Science and Technology Beijing;2006-03
7 ZHANG Jixin, ZHANG Wei, LI Jiuqing,MA Zheng, ZENG Guizhi Corrosion and Protection Center, Materials Science and Engineering School, University of Science and Technology Beijing, Beijing 100083, China;Galvanic corrosion of magnesium alloys in atmospheric environment[J];Journal of University of Science and Technology Beijing;2006-05
8 CHANG Shu-fen,ZHANG Xian-feng,JIANG Bai-ling (1.Guangzhou municital comstructive school, Guangzhou 510500; 2.School of Materials Science and Engineering, Xi抋n University of Technology, Xi抋n 710048, China);The Study on Mechanism of Formation and Growth of Ceramic Coating Prepared by Micro-arc Oxidation on Magnesium Alloy[J];China Surface Engineering;2004-01
9 JIANG Bai-ling,YUAN Fang,YUAN Sen,SHI Hui-ying,YUAN Bing(Xi'an University of technology,Shannxi,Xi'an,710048);Study on Junction Corrosion of Magnesium Alloy Coupled With Aluminum Alloy and Protection Effects of Different Surface Treatment[J];China Surface Engineering;2005-05
10 CHEN Xian-ming,LUO Cheng-ping,LIU Jiang-wen,LI Wen-fang(College of Mechanical Engineering,South China University of Technology,Guangzhou 510641 China);Discussion of Growth Process of Micro-arc Oxidation Film on Magnesium Alloys[J];China Surface Engineering;2006-05
【Secondary References】
Chinese Journal Full-text Database 10 Hits
1 ZHANG Ya-jun,YAO Zhong-ping,XIA Qi-xing,QI Su-fang,JIANG Zhao-hua(School of Chemical Engineering and Technology,Harbin Institute of Technology,Harbin 150001,China);Corrosion Resistance of Micro-Arc Oxidation/Air Sprayed Composite Coatings on Magnesium Alloy[J];Materials Protection;2011-06
2 SUN Fanghong1,MA Zhuang2,DONG Shizhi2,ZHAO Bin2 (1 Center of Training and Experimentation,Liaoning Technical University,Fuxin 123000;2 College of Materials Science and Engineering,Liaoning Technical University,Fuxin 123000);Progress in Research on Metal Ceramic Coatings for AZ91 Magnesium Alloy[J];Materials Review;2011-S2
3 YANG Xiao-wei,WANG Gui-xiang,DONG Guo-jun,GONG Fan(Key Laboratory of Superlight Material & Surface Technology,College of Materials Science & Chemical Engineering,Harbin Engineering University,Harbin, 150001,China);A Study of Sealing Technology for Anodic Films on Mg-Li Alloy[J];Electroplating & Pollution Control;2010-03
4 LI Zhi School of Pharmacology,Chengdu Medical College,Chengdu 610083,China;Research progress of biomedical ceramic coatings obtained by micro-arc oxidation on the surface of magnesium-based materials[J];Electroplating & Finishing;2011-06
5 SONG Dongfu 1,NONG Deng 1,QI Wenjun 1,LONG Siyuan 2,TAO Jun 2 1.Guangzhou Research Institute of Non-ferrous Metals,Guangzhou 510650,China;2.Material Science and Engineering College,Chongqing University,Chongqing 400030,China;Research status and prospects of complex organic coating on magnesium alloy[J];Materials Research and Application;2012-02
6 WANG Ming,SHAO Zhong-cai,TONG Shuai(School of Environment and Chemical Engineering,Shenyang Ligong University,Shenyang 110159,China);Research Advances of Surface Treatment for Magnesium Alloys[J];Plating & Finishing;2013-06
7 GU Yan-hong1,CAI Xiao-jun1,NING Cheng-yun2,XIONG Wen-ming3,ZHANG Jian-jun1,ZHAO Jie1(1.Department of Mechanical Engineering,Beijing Institute of Petrochemical Technology,Beijing 102617,China;2.College of Materials Science and Engineering,South China University of Technology,Guangzhou 510640,China;3.Technology Research Center,Xinyu Iron and Steel Group Company Ltd.,Xinyu 338001,China);Residual Stress Analysis of Micro-Arc Oxidation Coatings Prepared on Magnesium Alloy Substrate at Different Duration[J];Materials Protection;2013-04
8 SONG Gang,SHEN Qingxi,LIU Liming(Dalian University of Technology,Key Laboratory of Liaoning Advanced Welding and Joining Technology,Dalian 116023,China).;Preparation and analysis of Al-Mg intermetallic coating[J];Transactions of the China Welding Institution;2011-06
9 SONG Yu-lai1,2,LIU Yao-hui1,2,ZHU Xian-yong1(1.School of Materials Science and Engineering,Jilin Univ,Changchun,Jilin 130022,China; 2.Key Laboratory of Automobile Materials of Ministry of Education,Jilin Univ,Changchun,Jilin 130022,China);Influence of Neodymium on Density and Distribution of Galvanic Corrosion Currents in Magnesium Alloys[J];Journal of Hunan University(Natural Sciences);2012-04
10 LI Hua(Heilongjiang Institute of Chemical Engineering,Harbin 150078,China);Effects of hot water sealing on corrosion resistance of anodic films on Mg alloy[J];Chemical Engineer;2008-07
【Secondary Citations】
Chinese Journal Full-text Database 10 Hits
1 ZHU Li-qun\+1, LI Xue-yuan\+2, WU Jun\+1, DAI Si-min\+3 (1. Department of Materials Science and Engineering, Beijing University of Aeronautic and Astronautics, Beijing 100083; 2. Machinery Manufacturing Technology, China Academy of Engineering Physics, M;Protective Coating of Modified Silicon Sol on the surface of Magnesium Alloy in Aircraft Engine[J];Materiais Protection;2002-02
2 ZHANG Yong\|jun, YAN Chuan\|wei, WANG Fu\|hui, CAO Chu\|nan (State Key Laboratory for Corrosion and Protection, Institute of Metal Research, The Chinese Academy of Sciences, Shenyang 110016, China);Application, Corrosion and Protection of Magnesium and Its Alloys[J];Materiais Protection;2002-04
3 ;Recent Progress in Inorganic-Organic Hybrid Material[J];Materials Review;1997-02
4 Wang Qudong Lu Yizhen Zeng Xiaoqin Ding Wenjiang Lu ChenThe Open Laboratory of Education Ministry for High Temperature Materials and Tests, Shanghai Jiaotong University, Shanghai 200030;Current Application of Magnesium Alloy in Manufacturing Electronic Equipment[J];Materials Review;2000-06
5 Xue Wenbin 1 Lai Yongchun 1 Deng Zhiwei 1 Chen Ruyi 1 Liu Gao 2 1 Institute of Low Energy Nuclear Physics, Beijing Normal University, 2 Beijing Physical and chemical Analysis Center);The Properties of Coating Formed by Microplasma Oxidation on Magnesium Alloy[J];MATERIAL SCIENCE AND TECHNOLOGY;1997-02
6 LIU Zheng; WANG Yue; WANG Zhongguang; LI Feng; SHEN Zhiyong State Key Laboratory for Fatigue and Fracture of Materials, Institute of Metal Research, The Chinese Academy of Sciences School of Materials Science and Engineering, Shenyang University of Tech;DEVELOPING TRENDS OF RESEARCH AND APPLICATION OF MAGNESIUM ALLOYS[J];CHINESE JOURNAL OF MATERIAL RESEARCH;2000-05
7 WANG Fengping, ZHANG Xueyuan, DU Yuanlong (State Key Laboratory for Corrosion and Protection, Institute of Corrosion and Protection of Metals, The Chinese Academy of Sciences, Shenyang, 110015);THE REVIEW OF ATMOSPHERIC CORROSION RESEARCH[J];CORRSION SCIENCE AND TECHNOLOGY PROTECTION;2000-02
8 Zeng Aiping Xue Ying Qian Yufeng Wang Zhijie Huang Yuanwei Chen Ying (Shanghai Institute of Metallurgy, Chinese Academy of Sciences, Shanghai 200050);CHEMICAL SURFACE TREATMENT FOR MAGNESIUM ALLOYS[J];CORROSION & PROTECTION;2000-02
9 ZHAI Chun quan, ZENG Xiao qin, DING Wen jiang, WANG Qu dong, LU Yi zhen, XU Xiao ping (Shanghai Jiaotong University,Shanghai 200030,China);Development and Application of Magnesium Alloys in China[J];Materials For Mechanical Engineering;2001-01
10 Lin Shiyou(Beijing General Research Institute or Nonferrous Metals,Beijing 100088);Development of Magnesium Industry and its Application and Manufacturing[J];SHANGHAI NONFERROUS METALS;1995-06
©2006 Tsinghua Tongfang Knowledge Network Technology Co., Ltd.(Beijing)(TTKN) All rights reserved