《Journal of Materials Engineering》 2011-05
Add to Favorite Get Latest Update

Three-point Bending Test of 2A50 Forging Aluminum and Analysis by High-resolution Computed Tomography

AO Bo,DENG Cui-zhen,WU Guan-hua(Key Laboratory of Nondestructive Testing(Ministry of Education),Nanchang Hangkong University,Nanchang 330063,China)  
Three-point bending test of notched specimens of 2A50 forging aluminum was carried out by high frequency fatigue tester,specimens of computed tomography(CT) which contain fatigue crack were obtained.Fatigue specimen was reconstructed by high-resolution CT,CT images of crack were analysed;a reference plane was introduced,crack was projected on the reference plane in all CT images,and a damage risk factor was proposed.Results show that the damage of fatigue is uneven in different regions,the three-dimensional(3D) morphology of crack is visualized;the value of damage risk factor is 0.34,the defect area is 2.1 times the size of the most serious damage cross section,the damage risk factor is synchronized varying according to the fatigue cycles,it can be used to characterize damage of fatigue.
【Fund】: 航空科学基金资助项目(20090756001)
【CateGory Index】: TG115
Download(CAJ format) Download(PDF format)
CAJViewer7.0 supports all the CNKI file formats; AdobeReader only supports the PDF format.
【Citations】
Chinese Journal Full-text Database 3 Hits
1 DUAN Li-minga,ZHOU Yu-qinga,b(a.ICT Research Center;b.College of Mechanical Engineering,Chongqing University,Chongqing 400030,P.R.China);Prediction of material fatigue life based on industrial CT images[J];Journal of Chongqing University;2008-08
2 LIU Xin-ling, ZHANG Wei-fang, TAO Chun-hu (Failure Analysis Center of Aviation Industries of China, Beijing 100095, China);Fatigue Quantitative Analysis and Failure Estimation[J];Failure Analysis and Prevention;2006-01
3 WANG Hong, ZUO Hua-fu, HE Xun, LIN Qi-hui, HU Xiang-song(China National South Aviation Industrial Corporation Ltd, Zhuzhou 412002, China);Failure Analysis of 3rd Turbine Blade of Aero-engines[J];Failure Analysis and Prevention;2007-01
【Co-citations】
Chinese Journal Full-text Database 10 Hits
1 LIU Xin-ling,ZHANG Wei-fang,TAO Chun-hu(Failure Analysis Center,AVIC,Beijing Institute of Aeronautical Materials,Beijing 100095,China);Comparison between Two Models for Quantitative Fractography Analysis of Fatigue Life[J];Materials for Mechanical Engineering;2008-05
2 Tang Haijun,Cao Dashu,Yao Hongyu(Center of Aviation Safety Technology,Civil Aviation Administration of China,Beijing 100028,China);Failure Analysis on In-flight Shutdown of an Aero Engine[J];Acta Aeronautica Et Astronautica Sinica;2010-02
3 Chen Gang1 Li Xiangfeng1 Zuo Dunwen1 Wang Hongyu1,2 Zhang Min1(1College of Mechanical Engineering,Nanjing University of Aeronautics and Astronautics,Nanjing,Jiangsu 210016,China2School of Mechanical Engineering,Jiangsu University,Zhenjiang,Jiangsu 212013,China);Simulation on Substrate Relative Dilution Ratio for GH4033[J];Laser & Optoelectronics Progress;2011-01
4 YANG Sheng~(1,2),LI Chun-guang~1,LIU Chang-kui~1,LIU Li-yu~1,XIA Mei-ling~2 (1.Beijing Institute of Aeronautical Materials,Beijing 100095,China; 2.Nanchang Hangkong University,Nanchang 330063,China);Fracture Analysis of 0Cr12Mn5Ni4Mo3Al Steel Spring[J];Physical Testing and Chemical Analysis(Part A:Physical Testing);2010-05
5 YAN Xiao-jun,SUN Rui-jie,DENG Ying,LIU Zhi-na,NIE Jing-xu(School of Jet Propulsion,Beijing University of Aeronautics and Astronautics,Beijing 100191,China);Experimental study on fatigue curve law of turbine blade under combined high and low cycle loading[J];Journal of Aerospace Power;2011-08
6 LIU Xin-ling, JIANG Tao(Failure Analysis Center of Aviation Industries of China, Beijing Institute of Aeronautical Materials, Beijing 100095, China);Fracture Analysis on 4th Compressor Disc of an Engine[J];Failure Analysis and Prevention;2007-01
7 GUO Yong1,QI Ye2,LI Wei3,YU Duo-kui1(1.Shenyang Aero Engine Research Institute,Shenyang 110015,China;2.The CPLA Plant Representative Office of Shenyang Liming Aero Engine(Group)Co.Ltd.,Shenyang 110043,China;3.Shenyang Liming Aero Engine(Group)Co.Ltd.,Shenyang 110043,China);Analysis on Cracks at Plate of High Pressure Turbine Disk in an Aeroengine[J];Failure Analysis and Prevention;2008-03
8 ZHANG Jun,LI Ming,LU Yu-ming,YANG Xiao-qin(Key Laboratory of Nondestructive Test(Nanchang HangKong University),Nanchang 330063,China);Fatigue Fracture Image Segmentation Based on BEMD[J];Failure Analysis and Prevention;2011-02
9 JIA Na,LI Jia-lu(Key Laboratory of Advanced Textile Composite Materials of Ministry of Education,Tianjin Polytechnic University,Tianjin 300160,China);Research progress of flexural properties of composites at different temperatures[J];Journal of Tianjin Polytechnic University;2011-04
10 MA Xiao-ming,LIU Zhi-wei(School of Mechanical and Automotive Engineering, South China University of Technology,Guangzhou 510640,China);Finite element analysis of large cast stainless steel body based on ANSYS[J];Modern Manufacturing Engineering;2011-03
【Secondary Citations】
Chinese Journal Full-text Database 10 Hits
1 ZHANG Yi,ZHANG Wenfeng,YAN Hai (Institute of Aeronautical Materials,Beijing 100095,China);Quantitative Analysis in Evaluating Fatigue Lives of Components[J];JOURNAL OF MATERIALS ENGINEERING;2000-04
2 XU Xia-gang,ZHAO Xin-bo,ZHANG Ding-hua,AO Bo(The Key Laboratory of Contemporary Design and Integrated Manufacturing Technology,Ministry of Education,Northwestern Polytechnical University,Xi'an 710072);A Novel Testing Way for Collective Short Cracks by Industrial CT[J];Computerized Tomography Theory and Applications;2006-01
3 LU Wen ge (Guangdong University of Technology, Guangzhou 510643, China);Predicting Fatigue Life Based on the Behavior of Short Fatigue Crack[J];Materials For Mechanical Engineering;2001-02
4 LIU Xin-ling~1,ZHOU Jia-sheng~2,ZHONG Pei-dao~1,ZHANG Wei-fang~1(1.Failure Analysis Center of Aviation Industries of China,Beijing 100095,China;2.Military Representative Office of PLA 2nd Artillery in Beijing,Beijing 100039,China);Fracture Failure Analysis of the Third Class Turbine Vanes in Some Engine[J];Materials For Mechanical Engineering;2005-08
5 XIE Ming li XI Nian sheng TAO Chun hu(Institute of Aeronautical Materials, Beijing 100095,China)[KH3/4D];Study of fractographic retroestimation of fatigue stress amplitude[J];Journal of Aeronautical Materials;2000-04
6 WU Xue-ren, LIU Jian-zhong(Beijing Institute of Aeronautical Materials, Beijing 100095, China);Total Fatigue Life Prediction for Aeronautical Materials by Using Small-Crack Theory[J];Acta Aeronautica Et Astronautica Sinica;2006-02
7 ZHANG Weifang GAO Wei ZHAO Aiguo LIU Gaoyuan TAO Chunhu (Beijing Institute of Aeronautical Materials, Beijing 100095, China);FATIGUE STRESS ESTIMATION FOR TITANIUM ALLOY BY FATIGUE CRACK STRIATION[J];Journal of Mechanical Strength;2003-04
8 HE XueHong DONG GuangCheng HUI Li (School of Mechanical and Automation, Northeast University, Shenyang 110004,China);SIMULATION OF THE MULTI-MICRO CRACKS’ EVOLUTION UNDER THE METHOD OF MONTE CARLO[J];Journal of Mechanical Strength;2005-05
9 JIANG Longping XU Kejun (Aviation Mechanism Department, Qingdao Branch of Navy Aviation Engineering Institute, Qingdao 266041);PREDICTION FOR THREE-DIMENSION FATIGUE CRACK DYNAMIC GROWTH BY GRAY SYSTEM PREDICTION MODEL[J];Chinese Journal of Mechanical Engineering;2006-01
10 FU Guo-ru~1, YU Zhe-ming~2, WANG Hong-wei~1 (1. Beijing Aeronautical Technology Research Center, Beijing 100076, China; 2. Factory No.5713 of PIA , Hubei 470000, China);Main Failure Attributes and Rule of Compressor-blades in Aero-engines[J];Failure Analysis and Prevention;2006-01
©2006 Tsinghua Tongfang Knowledge Network Technology Co., Ltd.(Beijing)(TTKN) All rights reserved