Fabrication and property of electroless co deposited diamond composite coatings
WU Yu cheng 1, YE Min 1, WANG Wen fang 1, ZHANG Yong 1, HUANG Xi min 1, DENG Zong gang 1, ZHANG Xinyi 2 (1. Department of Materials Science and Engineering, Hefei University of Technology, Hefei 230009, China; 2. Anhui Industry College of Arc
The fabrication technology and property of electroless co deposited diamond composite coatings have been researched in this paper. When the addition of diamond was kept at 15-25 g/L, the co deposition rate attained higher value and the fraction of diamond in the composite increased. When diamond is well distributed, matrix is strengthened and gets stronger with the increase of the fraction of diamond. The composite coatings possesses higher wear resistance than nickel phosphorus, hard chromium plating and surfacehardening.