Flow stress behavior of ZK60 and Al_(18)B_4O_(33)w/ZK60 during hot compression deformation at elevated temperature

WANG Chun-yan1,2,WU Kun1,ZHENG Ming-yi1(1.School of Materials Science and Engineering,Harbin Institute of Technology,Harbin 150001,China;2.Dept.of Materials and Chemistry Engineering,Heilongjiang Institute of Technology,Harbin 150050,China)  
Hot compression test of ZK60 magnesium alloy and Al18B4O33w/ZK60 composite with deformation degree 60% and different temperature and strain rates were performed on Gleeble-1500D thermal simulator testing machine.The relationships between flow stress and deformation temperature as well as strain rate were analyzed.Variation of the flow stress and microstructure of the alloy and composite were studied.Strain rate sensitivity coefficient(m) and the deformation activation energy(Q) were calculated on ZK60 magnesium alloy and Al18B4O33w/ZK60 magnesium matrix composite.The conclusions were obtained that strain rate sensitivity coefficient(m) of magnesium alloy was 0.14,where as strain rate sensitivity coefficient of composite was 0.12.Deformation activation energy(Q) of magnesium alloy was 226~254 kJ/mol,while deformation activation energy of composite was 254~283 kJ/mol.
【CateGory Index】: TG115.9;TG146.22
Download(CAJ format) Download(PDF format)
CAJViewer7.0 supports all the CNKI file formats; AdobeReader only supports the PDF format.
©2006 Tsinghua Tongfang Knowledge Network Technology Co., Ltd.(Beijing)(TTKN) All rights reserved