《Rare Metal Materials and Engineering》 2002-01
Add to Favorite Get Latest Update

Burning Interfaces Analysis of Burn resistant Titanium Alloys Ti40 and Alloy C

Zhu Kangying 1,2 , Zhao Yongqing 2, Qu Henglei 2, Wang Xiao 2,Jin Zhihao 1 (1 Xi'an Jiao Tong University, Xi'an 710049,China) (2 Northwest Institute for Nonferrous Metal Research, Xi'an 710016, China)  
DCSB method is used to evaluate the burn resistant properties of Ti 40, Alloy C and Ti 6 4 three atmosphere conditions in this paper. The results show that Ti40 and Alloy C display good burn resistance as compared with Ti 6 4, and that the addition of nitrogen into air can decrease burning rate of titanium alloys. Burning interfaces were observed and analyzed by SEM and EDAX. It is found that which indicates that vanadium is preferentially immigrated to the surface to form V 2O 5 upon Ti40 and Alloy C burning. As a result the surface layer in burning zone is V enriched and Cr leaned, while the burned products and the oxidized layer close to matrix interface are V leaned and Cr enriched. The mixed oxidized layer is very dense, and can inhibite oxygen diffusion into the matrix, and prevent V in the matrix from diffusion into burning zone.Although Al can be preferentially immigrated to the surface to form Al 2O 3 upon Ti 6 4's burning, but it is too less in content to improve the alloy's burn proof ability.
【Fund】: 国家“九五”和“十五”攻关项目资助
【CateGory Index】: TG146.23
Download(CAJ format) Download(PDF format)
CAJViewer7.0 supports all the CNKI file formats; AdobeReader only supports the PDF format.
【References】
Chinese Journal Full-text Database 3 Hits
1 ZHANG Ping-ze, LI Zhong-hou, HE Zhi-yong, XU Zhong, ZHANG Gao-hui, (Surface Engineering Institute, Taiyuan University of Technology, Taiyuan 030024, China);Surface chromizing of Ti-6Al-4V by double glow plasma surface alloying technology[J];Ordnance Material Science and Engineering;2005-01
2 Wang Minmin1,2,Zhao Yongqing2, Zhou Lian2(1.Northeastern University, Shenyang 110006,China)(2.Northwest Institute for Nonferrous Metal Research, Xi'an 710016,China);High Temperature Creep Behavior of Ti40 Alloys[J];Rare Metal Materials and Engineering;2003-02
3 ZHANG Ping-ze, XU Zhong, ZHANG Gao-hui, HE Zhi-yong(Research Institute of Surface Engineering, Taiyuan University of Technology, Taiyuan 030024, China);Preparation of double glow plasma surface metallurgy treated Ti-Cu burn-resistant alloy[J];The Chinese Journal of Nonferrous Metals;2005-01
【Citations】
Chinese Journal Full-text Database 1 Hits
1 Zhao Yongqing1,2, Zhou Lian\+1, Deng Ju\+1 (1Northwest Institute for Nonferrous Metal Research,Xi'an 710016) (2.Northeastern University,Shenyang 110006);Effect of Alloying Element,Cr,on the Burning Behavior of Titanium Alloys[J];RARE METAL MATERIALS AND ENGINEERING;1999-03
【Co-citations】
Chinese Journal Full-text Database 1 Hits
1 Wu Huan1,2,Zhao Yongqing1,2 (1.School of Materials Science and Engineering,Northwestern Polytechnical University,Xi′an 710072,China;2.Titanium Alloy Research Institute,Northwest Institute for Non-Ferrous Metal Research,Xi′an 710016,China);Effect of Temperature on Damage Behaviour of a High Solid Solution Strengthened β Titanium Alloy[J];Chinese Journal of Rare Metals;2011-02
【Co-references】
Chinese Journal Full-text Database 9 Hits
1 Zhao Yongqing, Zhou Lian, Deng Ju, Zhu Kangying, Wang Xiao (Northwest Institute for Nonferrous Metal Research, Xi'an 710016);Burning Behavior of Titanium Alloys in Mixture of Ar and O_2[J];Rare Metal Materials and Engineering;2000-05
2 Zhao Yongqing, Qu Henglei, Zhu Kangying, Wu Huan, Zhou Lian (Northwest Institute for Nonferrous Metal Research, Xi'an 710016);Oxidation and Peel-Off Mechanisms of Oxide Layer of the Highly Stabilized β Type Burn Resistant Alloy Ti40[J];Rare Metal Materials and Engineering;2001-01
3 Zhao Yongqing, Qu Henglei, Zhu Kangying, Wu Huan, Liu Caili, Zhou Lian (Northwest Institute for Nonferrous Metal Research, Xi'an 710016, P.R.China);The Second Phases in A Burn Resistant Alloy-Ti40[J];Rare Metal Materials and Engineering;2001-06
4 Zhao Yongqing, Qu Henglei, Zhu Kangying, Wu Huan, Zhou Lian (Northwest Institute for Nonferrous Metal Research, Xi'an 710016, China);The Second Phases and Their Effects on Properties in Ti40 Burn Resistant Titanium Alloy Thermally Exposed for Long Time[J];Rare Metal Materials and Engineering;2002-02
5 Zhao Yongqing, Zhu Kangying, Qu Henglei, Wu Huan, Liu Caili, Li Yuelu, Zhou Lian (Northwest Institute for Nonferrous Metal Research, Xi'an 710016, China);Thermal Stability of Two Ti-V- Cr Burn Resistant Titanium Alloys[J];Rare Metal Materials and Engineering;2003-08
6 Huang Xu, Cao Chunxiao, Ma Jimin, Wang Bao, Gao Yang(Beijing Institute of Aeronautical Materials, Beijing 100095)Zhou Yaohe(Northwestern Polytechnical University, Xi′an 710072);High Temperature Oxidation Behaviour of a Fire-Resistant Titanium Alloy[J];RARE METAL MATERIALS AND ENGINEERING;1997-06
7 Zhao Yongqing, Zhou Lian, Deng Ju (Northwest Institute for Nonferrous Metal Research, Xi'an 710016);Burning Resistant Behavior and Mechanism of a Ti40 Alloy[J];RARE METAL MATERIALS AND ENGINEERING;1999-02
8 Liu Yuqin, Bai Kewu, Shen Jianyun and Zhang Zhu(General Research Insitute for Nonferrous Metals, Beijing 100088, China);Thermodynamic Analysis of Burnresistance Mechanism for Ti-Cr-V and Ti-Cr-Mo Alloys[J];CHINESE JOURNAL OF RARE METALS;1998-03
9 Zhao Yongqing, Zhao Xiangmiao and Zhu Kangying Northwest Institute for Nonferrous Metal Research, Xi′an 710016, P. R. China;MICROSTRUCTURES OF Ti V Cr BURN RESISTANT TITANIUM ALLOYS[J];THE CHINESE JOURNAL OF NONFERROUS METALS;1998-03
【Secondary References】
Chinese Journal Full-text Database 10 Hits
1 Wei Chunlei(Jiangxi Vocational Technical College of Industry & Trade,Nanchang 330038,China);STUDY ON HIGH TEMPERATURE CREEP PROPERTY OF PEEK COMPOSITE[J];Engineering Plastics Application;2011-07
2 LI Xin~(1,2) ZHAO Wei-gang~2 LU Shi-qiang~2 WANG Ke-lu~2 (1.Institute of Materials Science and Technology,Nanjing University of Aeronautics and Astronautics,Nanjing 210016,China; 2.Institute of Materials Science and Engineering,Nanchang Institute of Aeronautical Technology,Nanchang 330034,China);Investigation on hot deformation behavior and microstructure of TC11 alloy at large strain during β-phase[J];Ordnance Material Science and Engineering;2007-03
3 GAO Yuan1,XU Zhong2 (1. Guilin University of Electronic Technology, Guilin Guangxi 541004; 2. Taiyuan University of Technology, Taiyuan 030024);Effect and Application of Double Glow Discharge Surface Alloying Process[J];China Surface Engineering;2006-04
4 CUI Hong, LUO Xin- yi, ZHANG Yun-lu, ZHENG Ting, SUN Xiao-bin (College of Material Science and Technology, Nanjing University of Aeronautics and Astronautics, Nanjing 210016, China);Preparation of Chromizing Layer on Ti6AI4V Alloy by Double Glow Plasma Surface Metallurgy and Evaluation of Its High-Temperature Oxidation Resistance[J];Materials Protection;2011-08
5 Wang Wenbo1, Xu Zhong1,2, He Zhiyong1, Wang Zhenxia1, Zhang Pingze2 (1. Research Institute of Surface Engineering, Tai yuan University of Technology, Taiyuan 030024, China) (2. Nanjing University of Aeronautics and Astronautics, Nanjing 210016, China);Effect of Niobium Surface Alloying on the Antioxidation of Ti-6Al-4V[J];Rare Metal Materials and Engineering;2007-05
6 HU Meng1,LU Shi-qiang2,LI Xin1,HUANG Xu3,CAO Jing-xia3(1.School of Aeronautical Manufacturing Engineering,Nanchang Hangkong University,Nanchang 330063,China;2.School of Material Science and Engineering,Nanchang Hangkong University,Nanchang 330063,China;3.Beijing Institute of Aeronautical Materials,Beijing 100095,China);Study on constitutive relationship of Ti40 burn-resistant titanium alloy during high temperature deformation[J];Forging & Stamping Technology;2011-02
7 Xu Zhong 1,3 , Zhang Gaohui 1,2 , Zhang Pingze 3, Zhang Yanmei 1, Chi Chengzhong 1, Yuan Qinlong 1 (1. Research Institute of Surface Engineering,Taiyuan University of Technology, Taiyuan 030024, China; 2. Physics Department,Taiyuan University of Technology, Taiyuan 030024, China; 3. Nanjing University of Aeronautics and Astronautics, Nanjing 210016, China);New Development of Double Glow Plasma Surface Metallurgy Technology[J];Engineering Science;2005-06
8 SUN Xiao-bing,LUO Xin-yi,ZHANG Ping-ze,ZHENG Ting,CUI Hong(College of Material Science and Technology,Nanjing University of Aeronautics and Astronautics,Nanjing 210016,China);Preparation of W-Mo Co-penetrated Layer on Ti6Al4V Titanium Alloy Surface by Double Glow Discharge Technique and Its High Temperature Friction and Wear Properties[J];Materials for Mechanical Engineering;2010-10
9 YU Jin-wen,ZHANG Ping-ze,HUANG Jun,LIN Kai(School of Materials Science and Technology,Nanjing University of Aeronautics and Astronautics,Nanjing 210016,China);Microstructure and Properties of Chromized Layer Prepared by High Frequency Induction Heating and Paste Method[J];Materials for Mechanical Engineering;2012-06
10 Zhang Yunlu,Luo Xinyi,He Fei (Nanjing University of Aeronautics and Astronautics,Nanjing 210016,China);Preparation of W-Mo Copenetrated Layer on Ti6Al4V Titanium Alloy Surface by Double Glow Discharge Technique and Its Corrosive-Wear Properties[J];Rare Metal Materials and Engineering;2013-01
China Proceedings of conference Full-text Database 3 Hits
1 ZHAO Yong-qing, WANG Min-min,QU Heng-lei, WU Huan, YANG Hai-ying, LI Qian (Northwest Institute for Nonferrous Metal Research, Xi'an,710016,China);Creep Behavior of Two Kinds of Ti-V-Cr Burn Resistant Titanium Alloy[A];[C];2004
2 ZHANG Gao-hui~1 ZHANG Ping-ze~2 GE Hong-liang~1 CUI Yu-jian~1 JIANG Wei-di~1 XU Zhong~3 (1.China Jiliang University,Hangzhou 310018,China; 2.Nanjing University ofAeronautics & Astronautics,Nanjin 210014,China; 3.Research Institute of Surface Engineering,Taiyuan University of Technology,Taiyuan 030024,China);The preparation processing parameter study of the double glow discharge plasma hydrogen-free carburizing on titanium alloy surface[A];[C];2007
3 HUANG Guo-qing~1 ZHANG Gao-hui~1 ZHANG Ping-ze~2 XU Peng~1 YU Ming-zhou~1 WU Tai-quan~1 CHEN Miao-gen~1 (1.China Jiliang University,Research institute of surfece physics.Hangzhou,310018,China 2.Nanjing University of Aeronautics and Astronautics,Nanjing,210016,China);Fire Resistance Performance Study of Titanium Alloy Surface[A];[C];2009
©2006 Tsinghua Tongfang Knowledge Network Technology Co., Ltd.(Beijing)(TTKN) All rights reserved