Cast Microstructures and Mechanical Properties of Mg-Nd-Gd-Zn-Zr Magnesium Alloys

Li Jiehua,Jie Wanqi,Yang Guangyu (Northwestern Polytechnical University,Xi’ an 710072,China)  
With the method of orthogonal experiment,nine kinds of Mg-Nd-Gd-Zn-Zr magnesium alloys with different composition were prepared by sand casting.The cast microstructures and mechanical properties of Mg-Nd-Gd-Zn-Zr magnesium alloys were investigated,and the effects of Gd and Nd element on mechanical properties at room temperature were also studied by analyzing experiment results of mechanical properties.It is found that the as-cast microstructure of Mg-Nd-Gd-Zn-Zr alloys consists of α-Mg grains with Mg12Nd phase in the grain boundary.After the solid solution treatment,almost all of the phases in the grain boundary dissolved in the matrix; however,there was still discontinued Mg12Nd phase in the boundary.The increasing Gd content results in higher ultimate strength,yield strength and elongation.With increasing Nd content,the ultimate strength,the yield strength and the elongation increase.However,the elongation decreases when Nd is over 2.85 wt%.The effects of Nd content on the ultimate strength and yield strength of Mg-Nd-Gd-Zn-Zr alloy at room temperature are more significant than that of Gd.When Zn content is increased,the yield strength increases,but the ultimate strength and the elongation decreases.And Zn content has the greatest impact on elongation.
【Fund】: 国家重点基础研究发展计划“973”项目(2006CB605202);; 西北工业大学博士论文创新基金资助(CX200705)
【CateGory Index】: TG136.1
Download(CAJ format) Download(PDF format)
CAJViewer7.0 supports all the CNKI file formats; AdobeReader only supports the PDF format.
【Co-citations】
Chinese Journal Full-text Database 10 Hits
1 MA Wen-lai1,XING Lin-lin1,XUE Hong-fang2 (1.Flying College,Binzhou University,Binzhou 256603,China;2.Department of Computer Science and Technology,Binzhou University,Binzhou 256603,China);The Development and Prospect of Control Technology of Electric Melting Furnace for Magnesia[J];Journal of Binzhou University;2007-06
2 ZHANG Shuyan1,2,JIANG Fusong1,DING Wenbin2,ZHAO Dongyan2(1 Key Laboratory for Ultrafine Materials of Ministry of Education,School of Materials Science and Engineering,East China University of Science and Technology,Shanghai 200237;2 China Offshore Oil Engineering Co.Ltd.,Tianjin 300451);Preparation and Properties of Surface Composite Layer Reinforced by Nano SiC Ceramic Particles[J];Materials Review;2008-08
3 SU Lin,XIE Fa-qin,WU Xiang-qing,JI Lu-ming(School of Aeronautics,Northwestern Polytechnical University,Xi'an 710072,China);Micro-Arc Oxidation of Ti-Al Alloys in Mixed Solution System[J];Electroplating & Pollution Control;2008-04
4 Wang Feng,Wang Zhi,Liu Zheng,Mao Pingli(Shenyang University of Technology,Shenyang 110023,China);Effects of Heat Treatment on Microstructure and Mechanical Properties of Die-Cast Mg-8Gd-3Y-0.5Zr Magnesium Alloy[J];Rare Metal Materials and Engineering;2010-03
5 Chen Dongchu,Li Wenfang,Jie Jun,Peng Jihua (South China University of Technology,Guangzhou 510640,China);Micro-structure and Composition of Ceramic Coating on AZ91D Magnesium Alloy Prepared by Micro-Arc Oxidation[J];Rare Metal Materials and Engineering;2009-S2
6 LI Xue-zhe1,2,CHEN Li-jia1,ZHAO Bo1,CHE Xin1,WU Wei1 (1.School of Materials Science and Engineering,Shenyang University of Technology,Shenyang 110023,China;2.Shenyang Polytechnic College,Shenyang 110045,China);Fatigue deformation and fracture behavior of as-extruded AZ81 magnesium alloy[J];Journal of Shenyang University of Technology;2007-06
7 LI Xue-zhe1,2,WANG Xin1,CHEN Li-jia1,WU Wei1 (1.School of Materials Science and Engineering,Shenyang University of Technology,Shenyang 110023,China;2.Department of Mechanical Equipments,Shenyang Polytechnology College,Shenyang 110045,China);Low-cycle fatigue behavior of as-extruded Mg-Mn-ZnCe magnesium alloy[J];Journal of Shenyang University of Technology;2008-02
8 CHEN Li-jia,MAO Liang,ZHANG Si-qian,MA Chun-yan,LI Feng(School of Materials Science and Engineering,Shenyang University of Technology,Shenyang 110178,China);Tensile deformation behavior of hot-extruded AZ81 magnesium alloy[J];Journal of Shenyang University of Technology;2008-04
9 CHEN Li-jia,LIU Yang,WANG Xin,ZHANG Yue,MENG Xian-lin,CHEN Tao,XIONG Jian(School of Materials Science and Engineering,Shenyang University of Technology,Shenyang 110870,China);Plastic deformation behavior of AZ61 magnesium alloy processed by equal channel angular pressing[J];Journal of Shenyang University of Technology;2009-05
10 WANG Feng,LIU Zheng,WANG Zhi,WANG Yue (School of Materials Science and Engineering,Shenyang University of Technology,Shenyang 110870,China);Microstructure and mechanical properties of cold mold die-cast Mg-8Gd-3Y-0.5Zr magnesium alloy[J];Journal of Shenyang University of Technology;2009-06
China Proceedings of conference Full-text Database 3 Hits
1 Chen LiJia Wang Xin Ma Chunyan Xu Yanwu Li Feng (School of Materials Solute and Engineering,Shenyang University of Technology,Shenyang 110023,China);Tensile deformation behavior of hot-extruded Mg-6% Al-3% Ni magnesium alloys[A];[C];2008
2 Wang Xi Chen Lijia Zhi Ying Xu Yanwu (School of Materials Science and Engineering,Shenyang University of Technology,Shenyang,China);Low-cycle Fatigue Behavior of As-Extruded Mg-x%Al-3%Ni Alloys[A];[C];2008
3 Gao Bo Zhao Tiejun Tian Xiaomei Tu Ganfeng Chen Lei Hao Shengzhi Dong Chuang (School of Materials and Metallurgy, Northeastern University, Shenyang, 110004, P. R China; State Key Lab. of Materials Modification by Laser, Ion and Electron Beams, Dalian University of Technology, Dalian 116024, P. R. China);Investigation on Microstructure of the Surface Modified Layers of a HCPEB- treated Pure Mg and Mg Alloy AZ91HP[A];[C];2007
©2006 Tsinghua Tongfang Knowledge Network Technology Co., Ltd.(Beijing)(TTKN) All rights reserved