《RARE METAL MATERIALS AND ENGINEERING》 1998-04
Add to Favorite Get Latest Update

Microstructure of Superplastical Deformation of Hotrolled TiAl Intermetallic Compound

Zhang Di, Qin Jining, Shi Xinghua, Zhang Guoding(Shanghai Jiao Tong University, Shanghai 200030)  
The superplastic deformation of the TiAl intermetallic compound has been investigated It is shown that under hot roling TiAl exhibits superplastic deformation at T=1100℃ and ε.=5×10-4s-1, and its maximum elongation is 340% The strain rate sensitive exponent changes within the range of 04~07 during the superplastic flow Analysis by optical microscopy and transmission electron microscopy show that the superplastic mechanism under hot rolling is dynamic recrystallization
【Fund】: 国家自然科学基金
【CateGory Index】: TG146,TG146
Download(CAJ format) Download(PDF format)
CAJViewer7.0 supports all the CNKI file formats; AdobeReader only supports the PDF format.
©2006 Tsinghua Tongfang Knowledge Network Technology Co., Ltd.(Beijing)(TTKN) All rights reserved