New Preparation Process of Long Afterglow Phosphor Eu and Dy Co-doped SrAl_2O_4

HU Jin~(1,2),SUN Jia-lin~(1,2),LIU Jian-liang~(1,2),SHI An~2,XU Mao~2,GAO Qin-qin~2(1.Kunming University of Science and Technology,Kunming 650093,China;2.Kunming Institute of Precious Metals,Kunming 650221,China)  
The activated Al-Sr alloy powder was put immediately into boiling pure water,with liquid-solid(ratio) of 4 ∶1.The system was kept isothermal and stirred until white hydrolysates appears.The hydrolysates contain the mixture of Sr(OH)_2·8H_2O and Al(OH)_3 in main,included a little Al(OH)_3,AlOOH,SrCO_3,and 3SrO·Al_2O_3· 6H_2O.After heat treatment at 700 ℃ for 1 h,the mixture of SrO and α-Al_2O_3,γ-Al_2O_3 were formed.As a precursor,the hydrolysates after heat treatment had been used to prepare long after phosphor Eu,Dy co-doped SrAl_2O_4 at 1 300 ℃ for 1 h.The crystal structure of hydrolysates and Eu,Dy co-doped SrAl_2O_4 were analyzed by XRD.The luminescent properties of long afterglow material were studied.The(results) showed that the crystal structure of phosphor is β phase SrAl_2O_4,the emission spectra of Eu and Dy co-doped SrAl_2O_4 lied near 520 nm,resulted from the character transition of 4f5d-4f of Eu~(2+) ion.The method can improve afterglow properties dramatically.The initial luminescent intensity of long afterglow material reached 18 cd/m~2,and the duration time lasted 46 h.The improved properties are related to precipitation mechanism of AlSr alloy hydrolysates.With this procedure,SrO and Al_2O_3 will disperse evenly to effectively enlarge the contact area of the components,shorten the diffusive distance.As a result the sintering temperature could be decreased,while the reaction speed and the long afterglow fluorescent properties of the materials could be improved.
【Fund】: 云南省科研院所技术开发研究专项基金资助项目(2003KFZX-14)
【CateGory Index】: O482.31
Download(CAJ format) Download(PDF format)
CAJViewer7.0 supports all the CNKI file formats; AdobeReader only supports the PDF format.
Chinese Journal Full-text Database 3 Hits
1 Liu Yanhui,Zhao Ying(Department of Chemistry and Chemical Engineering,Hunan Institute of Science and Technology,Yueyang 414000,China);Development of Long-lasting Phosphorescent Materials of Aluminates Hosts[J];Guangdong Chemical Industry;2009-05
2 Hu Jin1,2,Sun Jialin1,2,Liu Jianliang1,2,Shi An1,Xu Mao1,Wang Kaijun1 (1.College of Materials Science and Metallurgy Engineering,Kunming University of Science and Technology,Yunnan Kunming 650093,China;2.Kunming Institute of Precious Metals);Research on heat treatment and preparation of Al(OH)_3 and Sr(OH)_2 composite powder[J];Inorganic Chemicals Industry;2007-02
3 Duan Haiting*,Zhao Fang,Liu Jianguo,Tan Meijun,Wang Zhengxiang(Key Laboratory of New Packaging Material and Technology,Hunan University of Technology,Zhuzhou 412007,China);Effects of Activated Carbon on Luminescent Properties of Long Afterglow Phosphors SrAl_2O_4:Eu~(2+),Dy~(3+)[J];Chinese Journal of Rare Metals;2009-02
Chinese Journal Full-text Database 10 Hits
1 ZHAO Jun-wu, QI Xiao-xia(Science College,Xi'an Jiaotong University,Xi'an 710049,CHN);Research Progress on Long Persistence Phosphors[J];Semiconductor Optoelectronics;2005-04
2 QI Xiao-xia,ZHAO Jun-wu(College of Sciences,Xi'an Jiaotong University,Xi'an 710049,CHN);Preparation and Luminous Performances of SrAl_2O_4∶Eu~(2+),Dy~(3+) Luminous Materials[J];Semiconductor Optoelectronics;2006-05
3 ZENG Qing-xuan, ZHOU Cong-zhang, FENG Chang-gen, LI Yong-chun (School of Mechano-Electronics Engineering, Beijing Institute of Technology, Beijing100081, China);Combustion Synthesis of SrAl_2O_4∶Eu,Dy Long Persistence Phosphors[J];Journal of Beijing Institute of Technology;2002-05
4 ZHANG Junying ZHANG Lin WANG Tianmin Zhang Zhongtai ( School of Science,Beijing University of Aeronautics and Astronautics,Beijing 100083; Human Resource Department,University of Science and Technology Beijing,Beijing 100083; Department of Materials Science and Engineering,Tsinghua University,Beijing 100084);Progress in Study of Long-lasting Phosphorescent Glass[J];Materials Review;2003-04
5 Yuan Ximing Xu Yongsheng Yu Jiangbo Wang Hongmei Yu Qiyu (China University of Geosciences, Engineering Faculty, Wuhan 430074,China);Sol-gel Synthesis of SrAl_2O_4:Eu~(2+), SrAl_2O_4:Eu~(2+), Dy~(3+) Long Afterglow Materials[J];Development and Application of Materials;2002-05
6 ZHOU Chuan-cang, LU Zhong-yuan, DAI Ya-tang, WANG Bing(School of Material Science and Engineering, Southwest University of Science and Technology, Mianyang 612010,China);Combustion Synthesis of SrAl_2O_4 :Eu,Dy Long Persistence Phosphors[J];Development and Application of Materials;2005-01
7 Zhang Xiyan 1 ,Bai Zhaohui 1 ,Guan Xin 1 ,Wang Xiaochun 1 ,Wang Weizhong 1 ,Sun Hongzhi 1 ,Cao Zhifeng 1 ,Du Jinxiu 2 ,Guo Yu 1 (1.Changchun Institute of Optical an d Fine Mechanics,Changchun 130022,China)(2.Solectron(Suzhou)Technology Co.,Ltd,Suzhou 215021,China);Preparation of Long Persistent Phosphorescence SrAl_2O_4:Eu~(2+),Dy~(3+) Phosphors by Solid State Reaction and Characterization[J];Rare Metal Materials and Engineering;2003-05
8 Guo Qingjie,Xu Mingxia,Cao Peiling (Tianjin University, Tianjin 300072, China);Progress on Eu~(2+)—Activated Alkaline Earth Aluminates Long Afterglow Phosphors[J];Rare Metal Materials and Engineering;2004-03
9 Wang Huiqin;Zhang Rei;Ma Lin;Hu Jianguo;Xu Yan(Department of Chemistry)Deng Hongmei(Research Center for Measurement);A study on combustion synthesis of strontium aluminates:Eu~(2+) and its luminescence[J];JOURNAL OF FUDAN UNIVERSITY;1997-01
10 Song Qingmei;Chen Jiyao; Wu Zhongya(Department of Material Science)(Department of Physics);A study on luminescence of Mg doped SrAl_2O_4:Eu phosphor[J];;1995-01
【Secondary References】
Chinese Journal Full-text Database 1 Hits
1 YANG Dajin(Technology Center of Yunnan Metallurgy Group Co.Ltd.,Kunming,Yunnan 650031,China);Annual Review of Yunnan Metallurgy in 2007[J];Yunnan Metallurgy;2008-02
©2006 Tsinghua Tongfang Knowledge Network Technology Co., Ltd.(Beijing)(TTKN) All rights reserved