STUDY ON PHENOL-FORMALDEHYDE MODIFIED WITH TUNG OIL──CURING BEHAVIOU AND KINETIC ANALYSIS

Yu Gang(Sichuan Academy of Forstry, Chengdu)  
In this paper,the curing behaviors and kinetics of phenolic resins modified with tung oil were investigated by IR,DSC.Experimental results were show that the curing process of these modified resins was divided into three stages:①the volatile endothermal peak was at 100~160 ℃;②the first curing exothermal peak was at 150~240 ℃;③the second curing peak was at 240~260℃.The apparent activation energy in thermal curing was decreased and curing rate was increased as the F/P molar ratio increased, the curing process was tended to reach perfection cured 7~15 min at 160~180℃.Compared with uumodified PF,the curing reaction was taken place at higher temperature for the flexible long branch-chains of tung oil were bonded on the backbones of PF,the collision reaction of phenolic-CH2OH groups was resisted and activation energy of curing reaction was increased.
【Fund】: 林业部专项经费资助
【CateGory Index】: TQ323.1
Download(CAJ format) Download(PDF format)
CAJViewer7.0 supports all the CNKI file formats; AdobeReader only supports the PDF format.
【References】
Chinese Journal Full-text Database 10 Hits
1 Wang Zijin;Tang Liqun;Wen Daijun;Zhong Weiping;Guangdong Chaohua Technology Co., Ltd.;Guilin Electrical Equipment Scientific Research Insititute Co., Ltd.;;Application of Cashew Phenol Modified Phenolic Resin in Paper-based Copper Clad Laminate[J];绝缘材料;2017-03
2 Xiao Na1 Xu Sankui1,2 Peng Jin1 Zou Wenjun1(1.School of Materials Engineering,Henan University of Technology,Zhengzhou 450007;2.Institute of Industrial Catalysis,Zhengzhou University,Zhengzhou 450052);New progress of research on heat-resistant phenolic resin modification[J];化工新型材料;2009-10
3 PU Xia,GE Jian-fang,MU Xiao-mei (College of Chemistry and Chemical Engineering,Zhongkai University of Agriculture and Engineering,Guangzhou 510225,China);Synthesis and characterization of tung-styrene oil thermosetting plastics lased on tung oil oxidization[J];仲恺农业工程学院学报;2009-02
4 HUANG Kun,XIA Jianling ( Institute of Chemical Industry of Forest Products,Chinese Academy of Forestry,Key Open Lab of Forest Chemical Engineering,State Forestry Administration,Nanjing 210042,Jiangsu,China);Progress of modification of tung oil and its derivatives in the application of polymer materials[J];化工进展;2008-10
5 Yu Jihong Deng Sulan(College of Resource and Planning Science,Jishou University,Zhangjiajie,427000);Study on the Synthesis Optimization of Anhydride and Eleostearic Acid Anhydride in Tung Oil[J];安徽农学通报;2007-06
6 HUANG Qin,XIE Zhi-ping,ZHOU Yuan-kang,FENG Yu,LI Yi;The Study of the Laser Processing Improving the Early Performance of Weave Rubbing Material[J];现代机械;2007-01
7 Zhou Yuankang1 Shu Da1 Li Yi1 Wang Manli2(1 College of Mechanical Engineering & Automation,Guizhou University;2 College of Chemical Engineering,Guizhou University,Guiyang Guizhou 550003);Study on Performance of Weave Friction Material Improved by Double Modified Resin[J];非金属矿;2006-04
8 HU Ping,YU Zhong-xin,YANG Ke,LI Yong-qiang,GONG Zhi-hai,LIU Jie,WANG Le (Chemical Engineering College,Wuhan University of Technology,Wuhan Hubei 430070,China);Research on Properties of Carbon Fiber Reinforced Composites Used for Automotive Synchronizing Ring[J];汽车工艺与材料;2005-05
9 Yu Zhongxin1 Hu Ping1 Zhang Tao2 Cheng Hao3 Gong Zhihai1(1.Department of Chemical Engineering,Wuhan University of Technology,Wuhan 430070,China;2.Wuhan Architecture Material Mechanical Factory,Wuhan 430070,China;3.Insitute of Mechanical & Electronic Engineering,Wuhan University of Technology,Wuhan 430070,China);Characterization of Modified Phenolic Resin of Automobile Synchronizing Ring Friction Materials[J];润滑与密封;2005-02
10 WANG Manli,ZHOU Yuankang,WU Yinghua(College of Chemical and Biological Eng,Guizhou University of Technology,Guiyang 550003,China);Study on oil-soluble boron phenolic resins[J];化学研究与应用;2003-01
【Co-references】
Chinese Journal Full-text Database 10 Hits
1 CHEN Xiao-peng;LIU Ming-pei;;Research on epoxy soybean modified phenolic resin to produce paper based CCL[J];印制电路信息;2014-08
2 ;New application and progress of Phenolic resin[J];国外塑料;2013-08
3 XU Li,SITU Yue,HU Jian-feng,ZENG Han-wei,CHEN Huan-qin(School of Chemical and Chemical Engineering,South China University of Technology,Guangzhou,Guangdong 510640,China);Synthesis and properties of doubly modified phenolic resin[J];粘接;2008-10
4 FANG Qun1,2,DU Guan-ben1,CUI Hui-wang3 (1. Southwest Forestry College,Kunming 650224,China;2. Zhejiang Forestry College,Lin’an 311300,China;3. Nanjing Forestry University, Nanjing 210037,China);Application of nano-materials in phenol formaldehyde resin[J];中国胶粘剂;2008-04
5 YIN Wen-hua,CHEN Yao,WU Bi-yao*(School of Material Science and Engineering,Wuhan Institude of Technology,Wuhan Hubei 430074,P.R.China)Received 14 November 2006;revised 20 December 2006;accepted 16 March 2007;Synthetic Process of Tungoil Modified Phenolic Epoxy Resin and the Performance of Room Temperature Cured[J];石油化工高等学校学报;2007-02
6 WU Fa-chao1,DENG Hai-feng2(1.North China Institute of Science and Technology,Yanjiao Beijing-East101601;2.Armed police Beijing direction institute,Beijing100012);Organic boron modified phenolic resin heat of the study[J];华北科技学院学报;2007-02
7 Zhou Yuankang1 Shu Da1 Li Yi1 Wang Manli2(1 College of Mechanical Engineering & Automation,Guizhou University;2 College of Chemical Engineering,Guizhou University,Guiyang Guizhou 550003);Study on Performance of Weave Friction Material Improved by Double Modified Resin[J];非金属矿;2006-04
8 YUAN Xin-hua ~1,SHAO Mei-xiu~1,CHEN Min~2,ZHANG Yan~2,WANG Jian-min~1 (1.School of Material Science and Engineering,Jiangsu University,Zhenjiang,Jiangsu 212013,China;2.School of Chemistry andChemical Engineering,Jiangsu University,Zhenjiang,Jiangsu 212013,China);Preparation and heat-resistant characterization of phenolic resin modified by linseed oil[J];江苏大学学报(自然科学版);2006-03
9 TIAN Jian-tuan,ZHANG Wei,GUO Ya-lin,XUE Shu-kai,ZHOU Yu-xi(Xi′an Aerospace Composite Material Insititute,Xi′an 710025,China);New progress of research on heat-resistant phenolic resin modified[J];热固性树脂;2006-02
10 SHANG Shi-bin,ZHOU Yong-hong,WANG Dan,WANG Ding-xuan Institute of Chemical Industry of Forest Products,CAF,Nanjing 210042,China;THERMAL STABILITY OF BISMALEIMIDE-PHENOLIC RESIN MODIFIED BY TUNG OIL[J];林产化学与工业;2005-S1
【Secondary References】
Chinese Journal Full-text Database 9 Hits
1 ZHANG Li;ZHANG Yi-he;YAO Ya-lin;TIAN Mou-feng;Beijing Key Laboratory of Materials Utilization of Nonmetallic Minerals and Solid Wastes,National Laboratory of Mineral Materials,School of Materials Science and Technology,China University of Geosciences;Beijing Composite Materials Co.,Ltd.;State Key Laboratory of Advanced Fiber Composites;;RESEARCH PROGRESS IN BORON MODIFIED PHENOLIC RESIN AND ITS COMPOSITES[J];玻璃钢/复合材料;2018-03
2 ZHI Hongmei;Henan Vocational College of Applied Technology;;Effect of Curing Conditions on Properties of Color Ultrathin Cutting Wheel[J];河南化工;2017-12
3 ZHANG Haizhao;ZHOU Hongyong;WANG Jiaxi;School of Chemical Engineering, Hebei University of Technology;;Synthesis, characterization and UV curable property of acrylate modified tung oil-based emulsifier[J];化工进展;2017-10
4 LIU Wenzhu;TANG Kehua;LI Shuo;Key Laboratory of Hunan Forest Products and Chemical Industry Engineering,Jishou University;Zhangjiajie Tung Fair Technologies Co.,ltd.;;Prepration of Solid Base Catalyst Added with Tung Shell Ash and Its Application in Methyl Esterification of Tung Oil[J];林产化学与工业;2017-04
5 LI Ke;JIANG Jian-chun;NIE Xiao-an;CHEN Jie;HUANG Jin-rui;SUN Fan;Institute of Chemical Industry of Forest Products,CAF;National Engineering Lab for Biomass Chemical Utilization;Key and Open Lab on Forest Chemical Engineering,SAF;Key Lab of Biomass Energy and Material,Jiangsu Province,SFA;Institute of New Technology of Forest,CAF;College of Chemical Engineering,Nanjing Forestry University;;Preparation and Kinetics of Methyl Esterification of Tung Oil[J];精细化工中间体;2016-04
6 TAN Xiang-lu;DENG Jian-ru;LUO Sai;LONG Li;LIU Miao-e;College of Chemistry and Chemical Engineering,Hunan University;;Preparation and Properties of Tung Oil-based Waterborne UV-curable Resin[J];精细化工;2016-08
7 MA Wen-jie;XIA Yong;YANG Jing;LI Ni;ZHOU Jin-hua;SUN Han-zhou;Key Laboratory of Cultivation and Protection for Non-Wood Forest Trees, Ministry of Education;;Preparation of eleostearic acrylic glyceride[J];中南林业科技大学学报;2016-04
8 Hao Yanmin;Shao Liying;Xiang Kuijia;Yuan Caideng;School of Chemical Engineering and Technology,Tianjin University;;Preparation and Properties of Waterborne Tung-Oil Based Polyurethane Emulsion[J];化学工业与工程;2016-01
9 Chen Hao;an Xiaofeng;Key Laboratory of Cultivation and Protection for Non-Wood Forest Trees of Ministry of Education Key Laboratory of Non-Wood Forest Products of State Forestry Administration Central South University of Forestry and Technology;;Identification of α-Linolenic Acid Metabolism Pathway Based on Transcriptome Data of Vernicia fordii Kernels during Tung Oil Synthesis Stage[J];林业科学;2015-03
©2006 Tsinghua Tongfang Knowledge Network Technology Co., Ltd.(Beijing)(TTKN) All rights reserved