《Iron Steel Vanadium Titanium》 2004-04
Add to Favorite Get Latest Update

DEVELOPING TREND OF GALVANNEALED AUTO SHEET STEELS

ZHANG Li-yang~1,LI Jun~2,ZUO Liang~1(1. School of Materials and Metallurgy, Northeastern University, Shenyang 110004,Liaoning, China;2.Baosteel Cold Rolling Mill, Shanghai 200941,China)  
The present development situation of galvannealed automobile sheet steel at home and abroad was introduced. For galvannealed IF steel, traditional strengthening method and new strengthening technology were introduced, and it was pointed out that galvannealed IF steel is developing to high strength when maintaining good formability. The developing situation of 340 MPa galvannealed bake-hardening steel was introduced in detail. It was pointed out that this steel was developing to good formability, good powdering resistance and good anti-aging. Galvannealed low-carbon equivalent type high-strength steel and dual-phase steel were introduced, too. And they are developing to good formability. Furthermore, the present developing situation of galvannealed TRIP steel were introduced too. It was put forward that galvannealed sheet steel, especially high-strength galvannealed sheet steel, for automobile should be paid attention in China.
【Fund】: 高校优秀青年教师教学科研奖励计划
【CateGory Index】: U465
Download(CAJ format) Download(PDF format)
CAJViewer7.0 supports all the CNKI file formats; AdobeReader only supports the PDF format.
【References】
Chinese Journal Full-text Database 7 Hits
1 XU Chun(Department of Material Engineering,Shanghai Institu-te of Technology,Shanghai 200233 China);Peeling Behavior of Hot-Dipped Galvanizing Alloying Coating on Automobile Steel Sheets[J];Materials Protection;2009-01
2 TAN Juan,WANG Jun,GAO Haiyan,SUN Baode(State Key Laboratory of Metal Matrix Composites, Shanghai Jiaotong University,Shanghai 200030);Recent Advances in High Strength Galvannealed Sheet Steels[J];Materials Review;2008-02
3 HUANG Xian-ming1,LIU Li-bin1,HUANG Guo-xing1,JIA Bing-ran1,LI Jun2,ZHANG Li-yang2(1.School of Materials Science and Engineering,Central South University,Changsha 410083,Hunan,China;2.Baosteel Cold Rolling Mill,Shanghai 200941,China);Study on Alloy Phase Forming Process of Plating Surface during Alloying Annealing Process of Hot-dip Galvanized BH Steel Sheets[J];Mining and Metallurgical Engineering;2007-05
4 XU Xiu-Qing,WANG Shun-Xing,ZHOU Xu-Dong (Material Science & Engineering College, Henan University of Science & Technology, Luoyang 471003, China );Study on Oxidation and Reduction Kinetics of Cold-rolled Steel[J];Journal of Henan University of Science & Technology(Natural Science);2007-02
5 KANG Yong-lin1,KUANG Shuang1,YIN Xian-dong1,2,YU Hao1,LIU Ren-dong2(1.College of Material Science and Engineering,University of Science and Technology Beijing,Beijing 100083,China;2.Anshan Iron and Steel Corporation Technology Center,Anshan Liaoning 114001,China);Research on Progress and Development of Dual Phase Steel Sheet for Automobiles[J];Automobile Technology & Material;2006-05
6 PANG Hai-lun1,ZHANG Xue-hui2,3,HONG Yong-chang1(1.School of Materials Science & Engineering,Anhui University of Technology,Ma′anshan 243002,Anhui;2.School of Materials Science and Engineering,University of Science and Technology Beijing,Beijing 100083;3.Wuhan Iron and Steel Co.,Wuhan 430080,Hubei);Effect of Chromium on Microstructure and Property of Cold-rolled Dualphase Steel[J];Heat Treatment;2009-01
7 ZHU Jiu-fa(The R & D Center of WISCO,Wuhan 430080,China);Coating default on hot-dip galvannealed sheet for automobile and its preventive measures[J];Wisco Technology;2009-02
【Co-references】
Chinese Journal Full-text Database 10 Hits
1 HAO Xiao-dong, ZHANG Qi-fu (New Metallurgy Croup,Headquarter Academy of Iron & Steel Research, Beijing100081, China).;Progress in Research of Hot-Galvanizing of Phase Transformation Induced Plasticity Steel[J];Materials Protection;2007-01
2 ZHANG Li-yang~1, LI Jun~2, ZUO Liang~1 (1. School of Materials & Metallurgy, Northeastern University, Shenyang 110004, China; 2. Baosteel Cold Rolling Mill,Shanghai 200941, China. Correspondent: ZUO Liang, E-mail: lzuo?@?mail.neu.edu.cn.);Coating Analysis of Galvannealed High Strength IF Steel[J];JOURNAL OF NORTHEASTERN UNIVERSITY;2005-03
3 ZHU Zheng (Shanghai Baosteel Group Corp.);DEVELOPMENT,APPLICATION ADN PERSPECTIVE OF HIGH STRENGTH STEEL SHEETS FOR AUTOMOBILES[J];Iron and Steel;2000-11
4 ZHANG Qifu LIU Bangjin (Central Iron and Steel Research Institute);RECENT DEVELOPMENT IN STUDY OF EFFECT OF COATING PHASE STRUCTURE OF IF GALVANNEALED STEEL SHEET ON ITS PROPERTIES[J];Iron and Steel;2002-12
5 CAO Tong-you(Department of Planning and Development,WISCO,Wuhan 430080,China);Study on relationship between properties and martensite content and size of dual-phase steel[J];Research on Iron and Steel;2006-04
6 Feng Peihua(Technology Center WISCO);DEVELOPMENT ON STEEL PLATE FOR AUTOMOBILE IN THE VIEW OF STEEL USED IN FORD[J];RESEACH ON IRON AND STEEL;1998-01
7 WANG Dongyan CHEN Weiqing ZHOU Rongzhang LIN Zongcai (University of Science and Technology Beijing, Beijing100083, China);REDUCTION KINETICS OF IRON OXIDE IN CARBON-BEARING PELLETS MADE FROM DUSTS CONTAINING ZINC AND LEAD[J];ENGINEERING CHEMISTRY & METALLURGY;1997-01
8 WEI Xi cheng, LI Lin, FU Ren yu (Shanghai University, Shanghai 200072, China);Review on Relation between Microstructures and Properties of TRIP Steel[J];Journal of Iron and Steel Research;2001-05
9 ZHANG Qi fu, LIU Bang jin, ZHONG Hai feng (Central Iron & Steel Research Institute, Beijing 100081, China);Development Trend of Hot-Dip Galvanizing Technology[J];Journal of Iron and Steel Research;2002-04
10 YU Jin-shan, ZHANG Jin-xu, WU Jian-sheng(School of Material Science and Engineering, Shanghai Jiao Tong University, Shanghai 200030, China)LIU Jun-liang, CHEN Jia-guang(Physical Testing Section of Testing Center, Baosteel Groups, Shanghai 201900, China);THE OVERVIEW OF THE COATING PERFORMANCE OF GALVANIZED SHEET APPLIED IN AUTOMOBILE[J];Physical Testing and Chemical Analysis Part A Physical Testing;2005-07
【Secondary References】
Chinese Journal Full-text Database 10 Hits
1 HUANG Qun-fei,HE Yan-lin,LI Lin(School of Materials Science and Engineering,Shanghai University,Shanghai,200072,China);Study Progress of High Property DP Steel[J];Heat Treatment Technology and Equipment;2007-03
2 TIAN Zhi-qiang,TANG Di,JIANG Hai-tao,MA Xiao-liang,XU Hong-xun(University of Science and Technology Beijing,Beijing 100083,China);Research and Production Status of Dual Phase Steels for Automobiles[J];Materials for Mechanical Engineering;2009-04
3 ZHANG Xue-hui 1,2,ZHU Guo-hui 1,3, MAO Wei-min 1(1.School of Materials Science and Engineering,University of Science and Technology Beijing,Beijing 100083,China;2.Wuhan Iron and Steel Co.,Ltd.,Wuhan 430083,Hubei,China;3.School of Materials Science and Engineering,Anhui University of Technology,Ma'anshan 243002,Anhui,China);Effect of Interaction Between Recrystallization and Transformation on Microstructure of Dual Phase Steel[J];Iron & Steel;2009-09
4 JIN Guang-can1),ZHAO Zheng-zhi1),XU Gang1),ZHAO Ai-min1),LIU Guang-ming2)1)Research Institute of Metallurgy Engineering,University of Science and Technology Beijing,Beijing 100083,China 2)Shougang Research Institute of Technology,Beijing 100039,China;Microstructure and fracture mechanism of 1000 MPa hot dip galvanized dual phase steel[J];Journal of University of Science and Technology Beijing;2009-10
5 XU Shi-hang1,WANG Min1,SHI Tian-yin1,PAN Hua2,LEI Ming2 (1.Shanghai Key Laboratory of Materials Laser Processing and Modification,Shanghai Jiaotong University,Shanghai 200240,China;2.Baosteel Technology Center,Shanghai 201900,China);Properties of resistance spot welding joint of DP590GA hot galvanized dual-phase steel[J];Electric Welding Machine;2009-10
6 JIANG Hai-tao,TANG Di,MI Zhen-li (National Engineering Research Center of Advanced Rolling Technology,University of Science and Technology Beijing,Beijing 100083,China);Latest Progress in Development and Application of Advanced High Strength Steels for Automobiles[J];Journal of Iron and Steel Research;2007-08
7 HUANG Quan-wei,SONG Ren-bo,ZHOU Le-yu,FANG Yuan,LIU Ya-zheng(School of Materials Science and Engineering,University of Science and Technology Beijing,100083,China);Microstructure and Property of 700 MPa Grade Hot Rolled Dual Phase Steel[J];Journal of Iron and Steel Research;2009-08
8 DOU Ting-ting1,KANG Yong-lin1,YU Hao1,KUANG Shuang1,LIU Ren-dong2,YAN Ling2(1.School of Materials Science and Engineering,University of Science and Technology Beijing,Beijing 100083,China;2.Technology Center of Anshan Iron & Steel Group Corporation,Anshan Liaoning 114001,China);Microstructural evolution of cold rolled dual-phase steel during initial stages of continuous annealing[J];Heat Treatment of Metals;2008-03
9 ZHAO Zheng-zhi1,XU Gang1,JIN Guang-can1,ZHANG Zeng-liang1,ZHAO Ai-min1,CHENG Zhi-song2(1.Metallurgical Engineering Research Institute,University of Science and Technology Beijing,Beijing 100083,China;2.National Engineering Research Center for Advanced Rolling Technology,University of Science and Technology Beijing,Beijing 100083,China);Development of high strength cold rolling C-Mn-Si dual phase steels[J];Heat Treatment of Metals;2009-01
10 Yang Haigeng,Yu Jinan (Jiangxi Xinyu Iron and Steel Co., Ltd.Jiangxi Xinyu338001);Research of Rolling Process on Hot-Rolled Dual Phash Strip[J];Metal World;2009-01
©2006 Tsinghua Tongfang Knowledge Network Technology Co., Ltd.(Beijing)(TTKN) All rights reserved