Experiment on ultra-high cycle bending vibration fatigue of titanium alloy TC17

LI Quan-tong,LIU Qing-chuan,SHEN Jing-sheng, CHENG Li,GAO Chao,CHEN Wei(School of Engineering,Air Force Engineering University,Xi'an 710038,China)  
The development of an ultra-high cycle bending vibration fatigue system on the basis of the mechanism of the fatigue failure of aeroengine vanes was discussed,including the design of ultra-high cycle dissymmetrical bending fatigue specimens.Research about TC17 was accomplished by the Ultra-High Cycle bending fatigue system(20 kHz).The fractograph of specimens was analyzed.The result indicates that the crack initiation is independent of interior inclusion and defect,and there are two kinds of mechanism of fatigue crack initiation:arising on surface or subsurface void.In addition,behaviors of interior crack initiation and propagation were not found the image of crack propagation is different from "fish-eye".
【CateGory Index】: TG146.23;TG115.5
Download(CAJ format) Download(PDF format)
CAJViewer7.0 supports all the CNKI file formats; AdobeReader only supports the PDF format.
【Citations】
Chinese Journal Full-text Database 5 Hits
1 ZHAO Guang-ju1,ZHONG Shu-hui2,DENG Jian-hua2(1.Fundamental Courses Teaching Department of the College of Science,Guizhou University,Guiyang 550003,China;2.College of Civil Engineering and Architecture,Guizhou University,Guiyang 550003,China);Study on the Fatigue Fracture in TA6V Titanium Alloy[J];Journal of Guizhou University of Technology(Natural Science Edition);2007-06
2 LI Yongde YANG Zhenguo LI Shouxin LIU Yangbo CHEN Shuming Shenyang National Laboratory for Materials Science,Institute of Metal Research,Chinese Academy of Sciences,Shenyang 110016;CORRELATIONS BETWEEN VERY HIGH CYCLE FATIGUE PROPERTIES AND INCLUSIONS OF GCr15 BEARING STEEL[J];Acta Metallurgica Sinica;2008-08
3 HONG Youshi,ZHAO Aiguo,QIAN Gui'an State Key Laboratory of Nonlinear Mechanics,Institute of Mechanics,Chinese Academy of Sciences,Beijing 100190;ESSENTIAL CHARACTERISTICS AND INFLUENTIAL FACTORS FOR VERY-HIGH-CYCLE FATIGUE BEHAVIOR OF METALLIC MATERIALS[J];Acta Metallurgica Sinica;2009-07
4 ZHOU ChengEn HONG YouShi(State Key Laboratory of Nonlinear Mechanics(LNM), Institute of Mechanics, Chinese Academy of Sciences, Beijing 100080, China);EXPERIMENTAL INVESTIGATION ON VERY-HIGH-CYCLE FATIGUE OF GCr15 STEEL[J];Journal of Mechanical Strength;2004-S1
5 TANG Weiwei WANG Hong (School of Mechanics and Engineering,Southwest Jiaotong University,Chengdu 610031,China);METHOD OF ULTRASONIC BENDING FATIGUE AND APPLICATIONS[J];Mechanics in Engineering;2008-06
【Co-citations】
Chinese Journal Full-text Database 10 Hits
1 Zheng Duan · Xian-Feng Ma · Hui-Ji Shi AML,Department of Engineering Mechanics,School of Aerospace,Tsinghua University,100084 Beijing,China Ryosuke Murai · Eiichi Yanagisawa Mitsubishi Heavy Industries,Ltd.,Tokyo,Japan;Gigacycle fatigue behaviors of two SNCM439 steels with different tensile strengthes[J];力学学报(英文版);2011-05
2 Meng Bo Dai JingJun Mu Qing(Department of Mechanical Engineering,Beijing Institute of Petro-chemical Technology,Beijing 102617,China);Quantitative Analysis of the Effect of Initial Defects on Bearing Fatigue Performance[J];Journal of Beijing Institute of Petro-Chemical Technology;2010-02
3 SHAO Hong-hong,JIANG Xiao-yan,ZHANG Dao-jun(School of Material Science and Engineering,Jiangsu University,Zhenjiang 212013,Jiangsu,China);Ultrasonic Fatigue Lives of 40CrNiMoA Steel with Different Microstructures[J];Journal of Materials Engineering;2008-05
4 Shen Jingsheng1,Li Quantong1,Wu Xiaofeng2,Gao Chao1,Liu Qingchuan1 (1.The Engineering Institute,Air Force Engineering University,Xi'an 710038,Shanxi,China;2.93029 Troops 97 Squadron);Study on the Ultra High Cycle Bending Vibration Fatigue Test of Titanium Alloys[J];Iron Steel Vanadium Titanium;2011-03
5 TONG Xu-dong;LI Quan-tong;SHI Yong-fang;GAO Xing-wei;Aeronautics and Astronautics Engineering College,Air Force Engineering University;Xidian University;;Ultra-high Cycles Fatigue Properties of Titanium Alloy with Different Slight Damages on Surface[J];Materials for Mechanical Engineering;2013-09
6 SUN Peng-peng;LI Shi-kai;SUN Er-ju;WAN Zi-yong;GUO Ning;LEI Xiao-wei;Luoyang Ship Material Research Institute;;Effect of Forging Times on Fracture Toughness and High Cycle Fatigue of TB6 Alloy[J];Development and Application of Materials;2013-05
7 GAO Chao1,CHENG Li1,PENG Hua2,SHEN Jing-sheng1, QIU Chen-lin1,LIU Yan-jie1 (1.The Engineering Institute,Air Force Engineering University,Xi'an 710038,China; 2.School of Communication Engineering, Chong Qing University,Chongqing 400044,China);Investigation of ultra-high cycle fatigue behavior of TC17 alloy at a frequency of 20kHz[J];Journal of Aerospace Power;2012-04
8 REN Wei-xia,LEI Chun-wei,GAO Yi-xin(Henan Diesel Engine Industry Co.,Ltd.,Luoyang Henan 471039,China);Optimization of material and process technology for piston pin of high speed and power diesel engine[J];Heat Treatment of Metals;2012-01
9 HU YanHui1 ZHANG Zheng1 ZHONG QunPeng1 HAN BangCheng2(1.School of Materials Science and Engineering,Beijing University Aeronautics and Astronautics,Beijing 100083,China)(2.School of Instrument Science and Opto-electronics Engineering,Beijing University Aeronautics and Astronautics,Beijing 100083,China);RECENT DEVELOPMENT OF RESEARCH ON VERY HIGH CYCLE FATIGUE OF METAL MATERIALS[J];Journal of Mechanical Strength;2009-06
10 ZHAO Feng-xiao1,LI Hui2,XU Xiao-chang1,LI Liang1,XU Hao-hao1(1.School of Materials Science and Engineering,Central South University,Changsha 410083,Hunan,China;2.Technology Center,Lianyuan Steel Corporation,Loudi 417000,Hunan,China);Influence of Inclusion Size on Fatigue Life of High Strength Steel for Automobile Wheel[J];Mining and Metallurgical Engineering;2013-01
China Proceedings of conference Full-text Database 1 Hits
1 ZHOU Meng-jiao,WANG Hong (School of Mechanics and Eng.,Southwest Jiaotong Univ.,Chengdu 610031,China);Study on the Gigacycle Fatigue Behaviors of 40Cr Steel Under Variable Amplitude Loading[A];[C];2010
【Secondary Citations】
Chinese Journal Full-text Database 9 Hits
1 Ye Wujun Zang Wei Ding Chuanfu Zao Zenye (Institute of Aeronautical Materials , Beijing );Study on Spectrum Load Fatigue Behaviors, Fracture Mechanism and Fractography of Two Ultra - High Strengh Steels[J];Journal of Materials Engineering;1992-02
2 Zhang Wenyu(Luoyang Ship Material Research Institute, Luoyang 471039);Study on the Low Cycle Fatigue Fracture in TA5 Titanium Alloy Plates[J];RARE METAL MATERIALS AND ENGINEERING;1998-03
3 Ni Jingang (4th Dept.Beijing University of Aeronautics and Astronautics,Beijing 100083);APPLICATION OF ULTRASONIC FATIGUE TESTING TECHNIQUE[J];JOURNAL OF AEROSPACE POWER;1995-03
4 Yan Yunqi 1 , Wang Wensheng 1,2 , Zhang Zhenqi 2 , Hong Quan 2 , Luo Guozhen 2 , Zhou Lian 2 (1 Material School of Xi'an Jiaotong University, Xi'an 710049, 2 Northwest Institute for Nonferrous Metal Research, Xi'an 71;Investigation on TiAl Alloy with High Performance[J];TRANSACTIONS OF METAL HEAT TREATMENT;2000-03
5 WANG Qingyuan (Department of Civil Engineering and Mechanics, Sichuan University, Chengdu 610065, China);GIGACYCLE FATIGUE OF ULTRA-HIGH STRENGTH STEELS[J];Journal of Mechanical Strength;2002-01
6 YAN Guiling WANG Hong GAO Qing (Department of Applied Mechanics and Engineering, Southwest Jiaotong University, Chengdu 610031, China);ULTRASONIC FATIGUE TESTING AND ITS APPLICATIONS[J];Mechanics and Engineering;2004-06
7 WANG Qing yuan (Dept.of Civil Eng. & Mechanics, Sichuan Univ., Chengdu 610065,China);Accelerated Fatigue Testing by Ultrasonic loading[J];Journal of Sichuan University (Engineering Science Edition);2002-03
8 YAN Yun qi 1,2 , WANG Wen sheng 1,2 , ZHANG Zhen qi 2, LUO Guo zhen 2, HONG Quan 2, ZHOU Lian 1,2 (1.Material School,Xi'an Jiaotong University; 2.Titanium Research Center,Northwest Institute for Nonferrous Metal Research);Forging of TiAl Based Alloys Containing High Nb[J];HOT WORKING TECHNOLOGY;2000-01
9 WANG Hong,GAO Qing (Dept. of Appl. Mechanics and Eng., Southwest Jiaotong University, Chengdu 610031, China);Analytical Solution of the Resonance Length for Ultrasonic Torsional Fatigue Samples[J];Journal of Southwest Jiaotong University;2001-06
©2006 Tsinghua Tongfang Knowledge Network Technology Co., Ltd.(Beijing)(TTKN) All rights reserved