YANG Dapeng1) FANG Huixin2) ZHAO Yao3)(Mechanical Engineering Department,Zhengzhou Technical College,Zhengzhou 450121,China)1)(Basic Teaching Department,Zhengzhou Technical College,Zhengzhou 450121,China)2)(Shipping and Ocean Engineering College,Huazhong University of Science & Technology,Wuhan 430074,China)3)  
In this article,the new manifestation of Paris formula has been mainly studied when fatigue loads with diverse stress ratio and frequency acting on component with cracks.Linear crack and curve crack propagation rate under fatigue loads with diverse stress ratio and frequency has been calculated quantificationally and accurately by modifying Paris formula.Scope of application of modifying Paris formula has been summarized where the effects of applied fatigue stresses,stress intensity factor transformation amplitudes at the fatigue crack tip are taken into considerations,accuracy and practicability of modifying Paris formula having been tested.
【Fund】: 河南省教育厅科学技术研究重点项目资助(批准号:2012B130007)
【CateGory Index】: O346.1
Download(CAJ format) Download(PDF format)
CAJViewer7.0 supports all the CNKI file formats; AdobeReader only supports the PDF format.
【Citations】
Chinese Journal Full-text Database 4 Hits
1 TANG Li_qiang 1,LI Rui_wen 2,LI Qi 1,MI Hai_rong 1 (1.Dept.of Civil Eng.,Harbin Engineering University ,Harbin 150001,China;2.Ying Lai Control of Civil Structure,Co.,Ltd. Shenzhen 518000,China);Fatigue Crack Growth Rate of Rotor Steel under the Condition of Subcritical Temperature[J];JOURNAL OF HARBIN ENGINEERING UNIVERSITY;2000-04
2 Liang Qianchao1) Peng Biao1) Ni Weimu2) Yao Jian2) Li Wusheng2)(Naval Univ. of Engineering, Wuhan 430033)1) (Naval Ensure Base, Wuhan 430000)2);On Reliability of Iimmerging Bolt-breaking in Diesel Pump[J];Journal of Wuhan University of Technology;2005-04
3 LIXin(Basic Department,Shenyang Pharmaceutical University,Shenyang 110015,China);Effects of Sclerosis on Crack Plastic Zone[J];Journal of Liaoning Normal University(Natural Science Edition);2006-02
4 Ding Zhiping~(*,2)) Chen Jiping~* Wang Tengfei~* Zhao Ping~+ *(School of Mechanical Engineering,Hunan University of Technology,Zhuzhou 412007,China) +(China Aviation Power Plant Research Institute,Zhuzhou 412002,China);STUDY ON LOW CYCLE FATIGUE OF SINGLE CRYSTAL NI-BASED SUPERALLOY UNDER MULTIAXIAL NON-PROPORTIONAL LOADING[J];Chinese Journal of Theoretical and Applied Mechanics;2012-02
【Co-citations】
Chinese Journal Full-text Database 10 Hits
1 Dong Zhaoxu Fang Daining Soh Ai Kah1(Department of Engineering Mechanics,Tsinghua University,Beijing 100084,China)2(Department of Mechanical Engineering,The University of Hong Kong,Hong Kong,China);ON THE EFFECT OF NANO-PARTICLE CLUSTERING ON TOUGHENING OF NANO-COMPOSITE CERAMICS[J];力学学报(英文版);2002-02
2 Dai Yao Liu Haixian (Surface Engineering Research Institute,CMES, Beijing,100072) Cui Jianguo He Jiawen (College of Materials Science and Engineering, Xi'an Jiaotong University);A STUDY ON THE DIRECTION OF FATIGUE CRACK GROWTH IN LAMINATED COMPOSITES USING THE MAXIMUM NORMAL STRESS RATIO CRITERION[J];Acta Armamentarii;2000-S1
3 YANG Da-peng,ZHAO Yao(Traffic Science & Engineering College,Huazhong University of Science & Technology,Wuhan 430074,China);A Second Order Perturbation Solution of a Slightly Curved Crack and Its Application to Prediction of Fatigue Crack Growth in Weldments[J];Journal of Ship Mechanics;2008-06
4 YANG Da-peng 1,ZHANG Xue-yan1,ZHAO Yao2,BAI Ling 1,ZHAO Hui1(1.Machine Department,Zhengzhou Technical College,Zhengzhou 450121,China;2.School of Naval Architecture and Ocean Engineering,Huazhong University of Science and Technology,Wuhan 430074,China);Crack Path Prediction of Brittle Fracture in Weldment under Dynamic Loads[J];Journal of Ship Mechanics;2012-03
5 Tang Huiming(China University of Geosciences, Wuhan);PROGRESS IN STUDY OF FRACTURE MECHANISM OF JOINTING[J];Geological Science and Technology Information;1991-02
6 WANG Can,CHEN Haoran(State Key Laboratory of Structural Analysis for Industrial Equipment, Dalian University of Technology,Dalian 116023,China);Experimental investigation and numerical simulation of interfacial crack kinking in foam core composite sandwich beams[J];Acta Materiae Compositae Sinica;2012-01
7 Yu Hengwen (University of Science & Technology of China,Hefei 230026,P.R.China) Song Jinliang (Tianjin University,Tianjin 300072,P.R.China) Feng Deyi Jian Chun (Tianjin Seismological Bureau,Tianjin 300070,P.R.China);EXPERIMENTAL STUDIES ON DYNAMIC PROPAGATION OF CRACKS UNDER BIAXIAL COMPRESSION[J];固体力学学报(英文版);1994-03
8 Zhao Yishu (Huazhong University of Science and Technology);A STRAIN ENERGY CRITERION FOR MIXED MODE CRACK PROPAGATION[J];Acta Mechanica Solida Sinica;1987-01
9 Rong Long · Chung-Yuen Hui Department of Biological and Environmental Engineering, Cornell University, Ithaca, 14853 New York, USA Field of Theoretical and Applied Mechanics, Cornell University, Ithaca, 14850 New York, USA;Crack buckling in soft gels under compression[J];力学学报(英文版);2012-04
10 YAN Yi-min1,HU Zheng-fei1,LIN Fu-sheng2,ZHAO Shuang-qun2(1 School of Materials Science and Engineering,Tongji University,Shanghai 200092,China; 2 Shanghai Power Equipment Research Institute,Shanghai 200240,China);Fatigue Behavior of 30Cr1Mo1V Rotor Steel at Elevated Temperature After Long-term Service[J];Journal of Materials Engineering;2012-11
China Proceedings of conference Full-text Database 3 Hits
1 Xu Yongjun~①Yu Junbo~②LI Min~①Liu Chuntu~①Zhang Chuanxu~②(①Institute of Mechanics,Chinese Academy of Sciences,Beijing,China) (②The 9th Oil Production Plant of Daqing Oilfield,Daqing,China);Interface Fracture Mechanics Analysis on Stratified Ccomposite Structures[A];[C];2008
2 Zhou Weiyuan;Liu Yuangao;Zhao Jidong;Yang Qiang Dept. of Hydr. Engng, Tsinghua Univ, Beijing 100084 China;A DISCONTINUOUS BIFURCATION MODEL FOR THE STABILITY OF JOINTED ROCKS[A];[C];2002
3 Zhengui Zhang,Jining Qin,Yifei Chen,Zhiwei Zhang,Weijie Lu*,Di Zhang State key Laboratory of Metal Matrix Composites,Shanghai Jiao Tong University, Dongchuan Road 800#,Shanghai 200240,People's Republic of China;Volume fraction effect of reinforcements on high temperature mechanical properties of in situ synthesized titanium matrix composites reinforced with TiB and La_2O_3[A];[C];2009
【Secondary Citations】
Chinese Journal Full-text Database 10 Hits
1 Yue Zhufeng, Lu Zhengzhou (Northwestern Polytechnical University, Xi'an 710072);A Model of Multiaxial Low Cycle Fatigue Life Time of a Nickel Base Single Crystal[J];RARE METAL MATERIALS AND ENGINEERING;2000-01
2 QIAN Caifu~(**) LI Huifang CUI Wenyong (Beijing University of Chemical Technology,Beijing 100029);Mode Ⅰ crack tip plastic zone,dislocation-free zone and their effects on crack propagation[J];Chinese Journal of Materials Research;2007-06
3 WANG Qing, LI Zhen, WANG Guozhen, CHEN Jianhong(College of Materials Science and Engineering, Gansu Univ. of Tech., Lanzhou730050, China);Study of fracture behavior at crack tip within C-Mn steel[J];Journal of Gansu University of Technology;2002-04
4 Chen Jiping1 Ding Zhiping1 Yin Zeyong2 Liu Yilun3 (1 School of Mechanical Engineering,Hunan University of Technology,Zhuzhou,412008) (2 China Aviation Power Plant Research Institute,Zhuzhou,412002) (3 School of Mechanical and Electrical Engineering,Center South University,Changsha,410083);STUDY ON LOW-CYCLE FATIGUE EXPERIMENTS AND LIFE PREDICTION OF SINGLE CRYSTAL NICKEL-BASED SUPERALLOYS UNDER ASYMMETRICAL CYCLIC LOAD[J];Acta Mechanica Solida Sinica;2007-02
5 ZHAO Ai guo 1, WANG Ke ran 2, ZHANG Wei fang 1, FAN Li wei 2, TAO Chun hu 1 (1. Beijing Institute of Aeronautical Materials, Beijing 100095, China; 2. Shenyang Aircraft Plants, Shenyang 110034, China);The Spread Mechanism of Cracks in the Forging Made of 300M Steel[J];Materials For Mechanical Engineering;2003-04
6 TANG Li_qiang 1,LI Rui_wen 2,LI Qi 1,MI Hai_rong 1 (1.Dept.of Civil Eng.,Harbin Engineering University ,Harbin 150001,China;2.Ying Lai Control of Civil Structure,Co.,Ltd. Shenzhen 518000,China);Fatigue Crack Growth Rate of Rotor Steel under the Condition of Subcritical Temperature[J];JOURNAL OF HARBIN ENGINEERING UNIVERSITY;2000-04
7 ZHANG Li, WANG Gang, CHENG Jin (Dept. of Astronautic Engineering and Mechanics, Harbin Institute of Technology,Harbin 150001, China,E-mail:19661994@sina.com);Investigation of fatigue damage parameters under multi-axial non-proportional loading[J];Journal of Harbin Institute of Technology;2004-05
8 SHANG De-guang~1,SUN Guo-qin~1,CAI Neng~1,WANG Jian-guo~2,WANG Lian-qing~2,WANG Hong-ying~2(1.College of Mechanical Engineering and Applied Electronics Technology,Beijing University of Technology,Beijing 100022,China; 2.State Key Laboratory for Advanced Metals and Materials,University of Science and Technology,Beijing 100083,China);Multiaxial Fatigue Behavior of GH4169 Superalloy under Non-Proportional Loadings at High Temperature[J];Journal of Aeronautical Materials;2006-06
9 YU Zhiwei, XU XiaoleiInstitute of Metal Materials and Technology, Dalian Maritime University, Dalian 116024LIU LuState Key Laboratory for Fatigue and Fracture of Materials, Institute of Metal Research, The Chinese Academy of Sciences, Shenyang 110016Corre;CONFIGURATION OF YIELD ZONE FOR STRAIGHT VOLTERRA DISLOCATION CORE[J];Acta Metallrugica Sinica;2002-03
10 QIAN Caifu, JIANG Zhongjun, CHEN Ping, DUAN Chenghong, GUI Wenyong Department of Process Equipment and Control Engineering, Beijing University of Chemical Technology, Beijing 100029;MICRO-SIMULATION OF CRACK TIP PLASTIC ZONE AND DISLOCATION-FREE ZONE[J];Acta Metallrugica Sinica;2004-02
©2006 Tsinghua Tongfang Knowledge Network Technology Co., Ltd.(Beijing)(TTKN) All rights reserved