《Physical Testing and Chemical Analysis(Part A:Physical Testing)》 2007-02
Add to Favorite Get Latest Update


DU Shi-hong,QIU Jie(China South locomotive & Rolling Stock Industry(Group) Chengdu locomotive & Rolling Factory,Chengdu 610051,China)  
The main generator revolution axis for the large power locomotive was broken in operation.The failure parts was tested by means of chemical composition analysis,mechanical property testing and metallographic examination.The results showed that the heating of revolution axis is not enough,austenitic homogenize is unsufficient.These caused fatigue strengtht of the generator revolution axis greatly depression,which are the main reason of the revolution axis fracture.
【CateGory Index】: U269
Download(CAJ format) Download(PDF format)
CAJViewer7.0 supports all the CNKI file formats; AdobeReader only supports the PDF format.
Chinese Journal Full-text Database 2 Hits
1 TONG Jian-guo1,2),GAO Xiao-dan1),QU Hai-tao1),ZOU Shi-wen1),LI Shu-xia1),REN Xue-ping1)1) School of Materials Science and Engineering,University of Science and Technology Beijing,Beijing 100083,China 2) Journal Publishing Center,University of Science and Technology Beijing,Beijing 100083,China;Diffusion behavior of Cr element at the bonding interface of a 25Cr5MoA/Q235 solid-liquid cladding shaft[J];Journal of University of Science and Technology Beijing;2009-04
2 GAO Xiao-dan,QU Hai-tao,TONG Jian-guo,REN Xue-ping(School of Materials Science and Engineering,University of Science and Technology Beijing,Beijing 100083,China);Research on Interface Characteristics of 25Cr5MoA/Q235 Solid-solid Clad Shaft[J];Journal of Netshape Forming Engineering;2009-01
Chinese Journal Full-text Database 9 Hits
1 CHEN Jing1),TONG Jianguo1,2),REN Xueping1)1) Materials Science and Engineering School,University of Science and Technology Beijing,Beijing 100083,China 2) Journal Publishing Center,University of Science and Technology Beijing,Beijing 100083,China;Bonding behavior of 25Cr5MoA/Q235 hot rolled clad plates[J];Journal of University of Science and Technology Beijing;2007-10
2 DONG Chengwen1), LI Yanfang2), REN Xueping1)1) School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China2) Capital Engineering and Research Incorporation Ltd., Beijing 100176, China;Joint interface characteristics of TA1/Q235 clad plates manufactured by accumulative roll-bonding[J];Journal of University of Science and Technology Beijing;2008-03
3 Liu Yinqi,Meng Xiangjun, Feng Yan,Li Qimin,Zheng Xiaojun(Luoyang Ship Material Research Institute, Luoyang 471039, China);An lnvestigation on the corrosion Behavior of TB-19 Alloy[J];Development and Application of Materials;2003-06
4 HUANG Guo-sheng, LIU Guang-zhou, DUAN Dong-xia, WANG Jun ory for Marine Corrosion and Protection, Qingdao 266071, China);EFFECT OF SRB ON CORROSION OF Cu-Ni ALLOY[J];Corrosion & Protection;2004-06
5 ZHANG Fu-ze1, YE Xu-bin2, SONG Jun2, GUO Hong-quan2(1.Beijing Aeronautical Technology Research Center, Beijing 100076) (2.Beijing Institute of Aeronautical Materials, Beijing 100095);Study on Crack Growth Behaviors of Three Kinds of Aeronautical Materials at 25℃ and -40℃[J];Acta Aeronautica Et Astronautica Sinica;2007-03
6 DAI Juan, XIA Zun-Feng, WANG Da-Peng (The Department of Machinery Engineering of ChangSha University,ChangSha Hunan 410003,China);Analysy on the Abatement of Axis Parts[J];Development & Innovation of Machinery & Electrical Products;2004-03
7 Zhao Zhangyan 1) Peng Zejun 2) (Department of Logistics Engineering,WUT,Wuhan 430063) 1) (School of Transportation, WUT,Wuhan 430063) 2);Fracture Analysis for Rotary Shaft of Reducer[J];Journal of Wuhan University of Technology;2002-06
8 DOU Man-feng,WANG Bei-she(Northwestern Polytechnical University,Xi'an 710072,China);Rotor Shaft Mechanical Design of Big Length to Diameter Ratio High Power Density Asynchronous Motor[J];Micromotors Servo Technique;2006-09
9 ZENG Yu, YIN Zhimin, ZHU Yuanzhi, and CUI Jianzhong College of Materials Science and Engineering, Central South University, Changsha 410083, China;College of Metallurgy and Material, Northeastern University, Shenyang 110015, China;Microstructure investigation of a new type super high strength aluminum alloy at different heat-treated conditions[J];稀有金属(英文版);2004-04
©2006 Tsinghua Tongfang Knowledge Network Technology Co., Ltd.(Beijing)(TTKN) All rights reserved