《Thermal Spray Technology》 2019-02
Add to Favorite Get Latest Update

Preparation of Nickel-Chromium Based Powder and Microstructure of Its Atmospheric Plasma Spraying Coating

Wei Hu;Zhenyu Zhang;Bunv Liang;Chunxia Hu;Chenggong Gong;Baiming Chen;Fengjuan Si;Lanzhou Institute of Technology;Lanzhou University of Technology;  
The high-energy ball-milled nickel-based alloy with silver and fluoride eutectic composite powders were used as raw materials to prepare thermal spray materials with particle size of 20~110μm by spray drying and sintering technology. Nickel-based composite coating was prepared by plasma spraying technology. The physical properties of the feed particles and the microstructure of the coating were analyzed. The results show that the powder after granulation has good sphericity and the fluidity. As the temperature increases during the granulation and sintering process, the fluidity and bulk density increased. After heat treatment at 800℃, the morphology of powder are round and smooth, with the average particle size of bulk density of 1.37 g/cm~3, and fluidity of 12.18 s/50 g, respectively, which is suitable for thermal spray feeding. As-coating with typical layered structure and the thickness of it is about 320μm. The porosity of the coating is about 3.6%. The phase contained is NiCr, Ni_3Al,NiAl, Ag, BaF_2 and CaF_2, etc. No new phase is formed during the spraying process.
【Fund】: 2018年度甘肃省高等学校科研项目(2018A-126);; 2017年度兰州工业学院青年科技创新项目(17K-001);; 兰州市人才创新创业项目(2017-RC-50);; 兰州工业学院“开物”科研团队支持计划(2018KW-11)
【CateGory Index】: V261;TG174.4
Download(CAJ format) Download(PDF format)
CAJViewer7.0 supports all the CNKI file formats; AdobeReader only supports the PDF format.
【Citations】
Chinese Journal Full-text Database 10 Hits
1 WANG Hai-bin 1,2,SONG Xiao-yan 1,2,LIU Xue-mei 1,2,FU Jun 1,2,WEI Chong-bin 1,2,GAO Yang 1,2(1.College of Materials Science and Engineering,Beijing University of Technology,Beijing 100124,China; 2.Key Laboratory of Advanced Functional Materials,Ministry of Education, Beijing University of Technology,Beijing 100124,China);Spray granulation of WC-Co composite powders and influencing factors of apparent density[J];中国有色金属学报;2012-11
2 Chen Jie1,2 Zhou Huidi1 An Yulong1,2 Zhao Xiaoqin1 Liu Guang1,2 Hou Guoliang1,2(1.State Key Laboratory of Solid Lubrication,Lanzhou Institute of Chemical Physics,Chinese Academy of Sciences, Lanzhou Gansu 730000,China;2.Graduate School,Chinese Academy of Science,Beijing 100049,China);Micro-sliding Friction and Wear Properties of PS304 Coating against Si_3N_4[J];润滑与密封;2011-09
3 YAN Jian-hui1,ZHANG Hou-an2,XU Hong-mei1,WU Hai-jiang1,TANG Si-wen1 (1.Advanced Materials Synthesis and Application Technology Institute, Hunan University of Science and Technology,Xiangtan 411201,China; 2.Department of Mechanical Engineering,Xiamen University of Technology,Xiamen 361024,China);Preparation of MoSi_2 powder used for plasma-spraying and its melting characteristics in plasma arc[J];中国有色金属学报;2011-04
4 YAN Jian-Hui1,TANG Si-Wen1,ZHANG Hou-An2(1.Advanced Materials Synthesis and Application Technology Laboratory,Hunan University of Science and Technology,Xiangtan 411201,China;2.Department of Mechanical Engineering,Xiamen University of Technology,Xiamen 361024,China);Preparation of Spraying Powders and Microstructure of Molybdenum Disilicide Coating[J];无机材料学报;2011-02
5 ZHANG You-cha1,2,JIA Cheng-chang1,HE Li-min2,LI Wei-guang2,MI Qing-tian2(1.School of Materials Science and Engineering,University of Science and Technology Beijing,Beijing 100083,China;2.Beijing Institute of Aeronautical Materials,Beijing 100095,China);FABRICATION OF NiCr-Cr_2O_3-BaF_2/CaF_2 COMPOSITE POWDER BY HIGH ENERGY BALL MILLING AND PROPERTIES OF IT'S DETONATION SPRAYED COATING[J];粉末冶金工业;2010-02
6 CHEN Zu-jun1,2,REN Shu-fang1,2,WANG Jing-bo1,JIA Jun-hong1,LU Jin-jun1(1.State Key Laboratory of Solid lubrication,Lanzhou Institute of Chemical Physics,Chinese Academy of Sciences,Lanzhou 730000,China2.Graduate School,Chinese Academy of Sciences,Beijing 100039,China);Tribological Properties of Ti_3SiC_2/PM304 Tribo-pair at Elevated Temperature[J];摩擦学学报;2010-02
7 Guo Yongfeng,Ding Chunhua,Zhang Hongtao,Yang Zhimao,Ding Bingjun(State Key Laboratory for Mechanical Behavior of Material,Xi'an Jiaotong University,Xi'an 710049,China);The Preparation of PS304 Nonacomposite Powders by High Energy Milling[J];稀有金属材料与工程;2006-12
8 DING Chunhua, WANG Yaping, ZHOU Jing'en State Key Laboratory for Mechanical Behavior of Materials, Xi'an Jiaotong University, Xi'an 710049 School of Science, Xi'an Jiaotong University, Xi'an 710049;A NiCr-BASED HIGH TEMPERATURE SELF LUBRICATING COATING PM304 PREPARED BY POWDER METALLURGY[J];金属学报;2006-11
9 Wang Linzhong Lin Shaoning Hou Yu Zhou Quan Chen Chunzheng(Institute of Cryogenic Engineering,Xi’an Jiaotong University,Xi’an 710049,China);Several Effects on the Flow Characteristics of PS304 Feedstock Powder Blend[J];润滑与密封;2005-05
10 Xue Qunji Lu Jinjun (Laboratory of Solid Lubrication Lanzhou Institute of Chemical Physics the Chinese Academy of Sciences Lanzhou 730000 China);Research Status and Developing Trend of Solid Lubrication at High Temperatures[J];摩擦学学报;1999-01
【Co-citations】
Chinese Journal Full-text Database 10 Hits
1 SHAN Yu;LIU Feng;WANG Jian-yi;WANG Wen-zhen;JIA Jun-hong;State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences;School of Materials Science and Engineering, Xian Shiyou University;Graduate University of Chinese Academy of Sciences;;High Temperature Tribological Properties of NiCrWAl_2O_3-SrCO_3-Ag Cement Composites[J];摩擦学学报;2015-06
2 LIU Er-yong;JIA Jun-hong;GAO Yi-min;ZENG Zhi-xiang;WU Xue-dong;Key Laboratory of Marine Materials and Related Technologies,Ningbo Institute of Materials Technology and Engineering,Chinese Academy of Sciences;Zhejiang Key Laboratory of Marine Materials and Protective Technologies,Ningbo Institute of Materials Technology and Engineering,Chinese Academy of Sciences;State Key Laboratory of Mechanical Behavior of Materials,Xi’an Jiaotong University;State Key Laboratory of Solid Lubrication,Lanzhou Institute of Chemical Physics,Chinese Academy of Sciences;;Progress of Continuous Lubricating Materials over a Wide Temperature Range[J];中国表面工程;2015-04
3 GE Xuelian;NIU Yaran;LI Hong;ZHENG Xuebin;School of Material Science and Engineering,Shanghai University;Key Laboratory of Inorganic Coating Materials,Shanghai Institute of Ceramics,Chinese Academy of Sciences;;Study on Fabrication and Properties of ZrC-SiC Composite Coating Prepared by Vacuum Plasma Spray[J];热加工工艺;2015-04
4 GAO Ming-chuan;TONG Xiang-yang;WANG Hong-sheng;Wuhan Research Institute of Materials Protection;;RESEARCH PROGRESS OF Mo-BASED COATINGS FABRICATED BY THERMAL SPRAY TECHNOLOGY[J];中国钼业;2014-06
5 GUO Sheng-da;YANG Jian-gao;CHEN Hao;ZHU Er-tao;Lü Jian;Project Research Institute, Jiangxi University of Science and Technology;Engineering Research Center of Tungsten Resources High-efficiency Development and Application Technology of the Ministry of Education;Advanced Corporation for Materials & Equipment;;The effect factors on morphology of nanophase WC-Co composite powder[J];粉末冶金材料科学与工程;2014-06
6 ZHU Er-tao;YANG Jian-gao;TAN Xing-long;DENG Jun-wang;DAI Yu;GUO Sheng-da;School of Materials and Chemical Engineering,Jiangxi University of Science and Technology;Advanced Corporation for Materials & Equipment;Project Research Institute,Jiangxi University of Science and Technology;;Preparation of WC-Co Thermal Spraying Powder by Spray Granulation-H_2 Reduction Process[J];金属功能材料;2014-06
7 GUO Jun-de;HE Shi-quan;MA Wen-lin;MENG Jun-hu;WANG Jing-bo;LU Long;Institute of Petrochemical Technology,Lanzhou University of technology;State Key Laboratory of Solid Lubrication,Lanzhou Institute of Chemical Physics,Chinese Academy of Sciences;Lanzhou Industrial Institute;;Tribological Characteristics of Fe-Mo-Ni-Cu-Graphite High Temperature Self-Lubricating Composites[J];摩擦学学报;2014-06
8 Zhu Langtao;Yang Jun;Zhang Qingying;Wang Jing;Han Zhihai;Yang Jianfeng;School of Metallurgical Engineering,Xi'an University of Architecture & Technology;China National Heavy Machinery Research Institute Co. ,Ltd.;School of Materials Science and Engineering,Lanzhou University of Technology;State Key Laboratory for Mechanical Behavior of Materials,Xi'an Jiaotong University;;Preparation and Influence Factors of ZrO_2-MoSi_2 Agglomerated Composite Powder used for Plasma-Spraying[J];稀有金属;2014-06
9 WANG Jun-hai;LIU Yang;DUAN De-li;LI Shu;Division of Special Materials and Devices,Institute of Metal Research,Chinese Academy of Sciences;;Exploration on Hybrid Lubricating Behavior of Znic Perrhenate in a Wide Temperature Range[J];中国表面工程;2014-05
10 CHEN Jian-min;LU Xiao-wei;LI Hong-xuan;ZHOU Hui-di;State Key Laboratory of Solid Lubrication,Lanzhou Institute of Chemical Physics,Chinese Academy of Sciences;Graduate School of Chinese Academy of Sciences;;Progress of Solid Self-lubricating Coating over a Wide Range of Temperature[J];摩擦学学报;2014-05
【Secondary Citations】
Chinese Journal Full-text Database 10 Hits
1 AN Yu-long1,2,CHEN Jian-min1,ZHOU Hui-di1,WEI Jia-jun3 (1.State Key Laboratory of Solid Lubrication,Lanzhou Institute of Chemical Physics,Chinese Academy of Sciences,Lanzhou 730000 2.Graduate School of Chinese Academy of Science,Beijing 100049 3.Gansu Zixin Mining Industry and Coal Chemistry Industry Company Ltd.,Lanzhou 730000);Characterization of the Microstructure of Atmosphere Plasma-sprayed Mullite Powders and Coatings[J];中国表面工程;2010-05
2 SONG Xiao-yan(College of Materials Science and Engineering,Beijing University of Technology,Beijing 100124,China);Low-cost & Short-term Preparation and Applications of Ultrafine and Nano-scaled WC-Co Composite Powders[J];中国钨业;2010-03
3 MA Guozheng,XU Binshi,WANG Haidou,SI Hongjuan (National Key Laboratory for Remanufacturing,Academy of Armored Forces Engineering,Beijing 100072);State of Research on Space Solid Lubrication Materials[J];材料导报;2010-01
4 ZHANG Shou-quan1,2),ZHU Jing-lei1),WANG Hai-tao1),HUANG Ji-hua1),ZHANG Hua1),ZHAO Xing-ke1)1)School of Materials Science and Engineering,University of Science and Technology Beijing,Beijing 100083,China 2)Xiamen Golden Egret Special Alloy Co.Ltd.,Xiamen 361006,China;TiC-reinforced Fe-base metal ceramic composite coatings fabricated by reactive plasma spraying[J];北京科技大学学报;2009-03
5 WU Heng,LI He-Jun,WANG Yong-Jie,FU Qian-Gang,HE Zi-Bo,WEI Jian-Feng(C/C Composites Technology Research Center,Northwestern Polytechnical University,Xi'an 710072,China);Effect of Deposition Temperature on Microstructures and Properties of MoSi_2 Coatings Prepared by Low Pressure Chemical Vapor Deposition[J];无机材料学报;2009-02
6 YAN Jianhui1,2, ZHANG Houan2, LI Yimin1, TANG Siwen2 (1. State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083, China; 2. Advanced Materials Synthesis and Application Technology Laboratory, Hunan University of Science and Technology, Xiangtan, Hunan 411201, China).;Phases evolution of molybnenum silicide coating in plasma spraying and heat treatment process[J];焊接学报;2008-08
7 HOU Pu-yun,HE Ding-yong,JIANG Jian-min,ZHAO Qiu-ying (College of Materials Science and Engineering,Beijing University of Technology,Beijing 100022);The Influence of Milling Parameters on the Properties of Al_2O_3-dispersion-strengthened NiCr Powders and Sprayed Coatings[J];中国表面工程;2007-06
8 ZHANG Xianglin,ZHANG Xiaofeng,WANG Aihua(State Key Laboratory of Material Processing and Die and Mould Technology,Huazhong University of Science and Technology,Wuhan 430074);Research and Development of High Temperature Solid Lubrication Coatings[J];材料导报;2007-06
9 Zhao Hui Zhang Yunquan Ding Zhangxiong (School of Energy & Power Engineering,WUT,Wuhan 430063);Resistance of HVOF Nanostructured WC-12Co Coatings to Cavitation Erosion[J];武汉理工大学学报(交通科学与工程版);2007-03
10 Cui Dawei,Li Ke,Qu Xuanhui,Jia Chengchang (School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China);Research on preparation of nitrogen-contained stainless steels by high-energy ball milling and sintering[J];粉末冶金技术;2007-01
©2006 Tsinghua Tongfang Knowledge Network Technology Co., Ltd.(Beijing)(TTKN) All rights reserved