CAUSE ANALYSIS ON THE FRACTURE OF HEAT EXCHANGE TUBE IN METHANOL SYNTHESIS REACTOR

Liang Bin;Rui Leshun;Cui Qiang;Nanjing Boiler and Pressure Vessel Inspection Institute;Nanjing Jinchuang Non-Ferrous Metal Technology Limited Company;  
This paper analyzes and studies the fracture reasons of 0 Cr18 Ni9 stainless steel heat exchange tube in methanol synthesis reactor by adopting such methods as chemical component analysis,mechanical performance test,microstructure analysis and SEM observation of fracture and energy spectrum analysis.The results show that the boiler feed water containing Cl-in the shell side of the reactor formed corrosive environment.Under the action of working stress and temperature,cracks initiated in the pitting corrosion region on the outer surface of tube and extended to the inner wall until penetrating.The fracture was characterized by cleavage fracture,which was intergranular and transgranular brittle fracture.The fracture reason of the heat exchange tube was chloride-induced stress corrosion cracking.
【Fund】: 国家重点研发计划《非铁磁性材料脉冲涡流与微磁检测关键技术研究及仪器研制》(编号:2017YFF0209701)项目资助
【CateGory Index】: TQ223.121
Download(CAJ format) Download(PDF format)
CAJViewer7.0 supports all the CNKI file formats; AdobeReader only supports the PDF format.
©2006 Tsinghua Tongfang Knowledge Network Technology Co., Ltd.(Beijing)(TTKN) All rights reserved