Deterioration Mechanism of Cables and Mechanics Model of Wires

XU Jun,CHEN Weizhen,LIU Xue(Department of Bridge Engineering,Tongji University,Shanghai 200092,China)  
Inspections of the fracture of corrosion wires from old bridge cables show that corrosion leads to three types of failure modes,which are general corrosion with pitting,corrosion fatigue and stress corrosion.Through experimental research,the degradation of the mechanical properties of corrosion wires is drawn.Furthermore,wires are modeled as a cylinder with monolateral crack.Based on this model,the damage evolution of corrosion wires is simulated.
【CateGory Index】: U443.38
Download(CAJ format) Download(PDF format)
CAJViewer7.0 supports all the CNKI file formats; AdobeReader only supports the PDF format.
【References】
Chinese Journal Full-text Database 3 Hits
1 ZUO Hai-hong,TIAN Fei-long (Department of Bridge Engi.,Tongji Univ.,Shanghai 200092,China);FRACTURE FAILURE MODES ANALYSIS OF BRIDGE CABLES[J];Low Temperature Architecture Technology;2012-05
2 MA Xiao-li1,WANG Li-bin1,2,3,DING Sheng1(1.Department of Civil Engineering,Nanjing Forestry University,Nanjing 210037,China; 2.Key Laboratory of Concrete and Prestressed Concrete Structures of Ministry of Education,Southeast University,Nanjing 210096,China; 3.ATLSS Laboratory,Department of Civil Engineering,Lehigh University,Bethlehem,PA 18015,U.S.);TIME-DEPENDENT FAILURE PROBABILITY ANALYSIS OF CORRODED PARALLEL WIRE CABLE[J];Engineering Mechanics;2012-04
3 Liu Muyu Chen Qifeng Wu Zhiqiang(Hubei Key Laboratory of Roadway Bridge & Structure Engineering,Wuhan University of Technology,Wuhan 430070,China);Time-dependent reliability analysis of strand cables of cable-stayed bridges considering fretting-fatigue factor[J];China Civil Engineering Journal;2012-07
【Citations】
Chinese Journal Full-text Database 1 Hits
1 WANG Rong(Xi'an Petroleum Institute, Xi'an 710061);A FRACTURE MODEL FOR CORROSION FATIGUE CRACK PROPAGATION PROCESS[J];Journal of Chinese Society For Corrosion and Protection;1998-02
【Co-citations】
Chinese Journal Full-text Database 7 Hits
1 Hu Jun Ou Jinping(School of Civil Engineering,Dalian University of Technology,Dalian 116024,China);THE CORROSION FATIGUE LIFE ANALYSIS ON HANGERS OF LONG SPAN SUSPENSION BRIDGE UNDER WIND LOAD[J];Steel Construction;2011-05
2 WANG Rong (Xi'an Petroleum University, Xi'an 710065, China);Crack Propagation Characteristics of X70 Pipeline Steel under Fluctuation Loading[J];Materials For Mechanical Engineering;2004-06
3 FAN Lin,LI Xiao-gang,DU Cui-wei,LIU Zhi-yong(Corrosion and Protection Center,University of Science and Technology Beijing,Beijing 100083,China);Current Research on the Corrosion Fatigue Crack Propagation Rate of Pipeline Steels[J];Corrosion & Protection;2012-11
4 LUO She-ji1,2,ZHAO Kang1,WANG Rong2(1.School of Materials Science and Engineering,Xi′an University of Technology,Xi′an 710048,China; 2.School of Materials Science and Engineering,Xi′an Shiyou University,Xi′an 710065,China);Fatigue Cracks Propagation Behavior of S135 Drill Pipe Steel at Different Stress Ratios[J];Materials for Mechanical Engineering;2013-07
5 Li Mingxing(Xi'an Petroleum Institute, Xi'an), Wang Rong, Li Pengliang, et al.;Investigation on the crack propagation characteristics of X70 pipeline steel in the synthetic soil solution.[J];China Petroleum Machinery;2002-07
6 Chen Yanhua Shi Zhifei,Prof.Meng Fansheng(School of Civil & Architecture Engineering, Northern Jiaotong University)(Daqing Refining chemical Company);Corrosion Fatigue at the Interface of Reinforcing Bar and Concrete[J];China Safety Science Journal;2003-03
7 LI Mingxing 1,2 ,WANG Rong 1,LI Pengliang 3,LU Minxu 4 (1.Xi'an Petroleum Institute,Xi'an 710065; 2.Oil and Gas Technology Research Institute,Changqing Oilfield Company,Xi'an 710021; 3.School of Materials Science and Engineering,Xi'an Jiaotong University,Xi'an 710049; 4.School of Materials Science and Engineering,University of Science and Technology Beijing,Beijing 100083);CRACK PROPAGATION QUANTITATIVE MODELS OF X70 PIPELINE STEEL IN THE SYNTHETIC SOIL SOLUTION[J];Journal of Chinese Society For Corrosion and Protection;2004-03
【Co-references】
Chinese Journal Full-text Database 10 Hits
1 XU Hong1,2,HUANG Ping-ming2,HAN Wan-shui2(1 China Railway No.1 Engineering Group Co.,Ltd,Xi'an 710054,China;2 Key Laboratory for Bridge and Tunnel of Shaanxi Province,Chang'an University,Xi'an 710064,China);Analysis and evaluation for the strength safety of the parallel sling wires[J];Journal of Safety and Environment;2008-05
2 MU Xian-liang~1,2,3,TIAN Yue-e~1,2,3,WEN Bang-wei~1,2,3,ZHOU Yi~1,2,3(1.No.59 Institute of Ordnance aindustry China,Chongqing 400039,China;2.The Natural Environmental Test and Research Center of Science,Technology and Industry for National Defense,Chongqing 400039,China;3.Chongqing environmental corrosion and protection engineering research center,Chongqing 400039,China);The Primary Investigation on the Corrosion Status of the Inclined Cable of Shimen Bridge on Chongqing Jialing River[J];Surface Technology;2006-06
3 Yuan Jinsong (East China Shipbuilding Institute, Zhenjiang 212003,China);Approximate Calculation of Crack Propagation Rate of Metal Corrosion Fatigue[J];DEVELOPMENT AND APPLICATION OF MATERIALS;2000-02
4 WANG Wei-sheng1,ZHAO Rong-gao2,LI Feng-hui1(1.Chongqing Jiaotong University,Chongqing 400074,China;2.Lugang Group Co.Ltd,Zhejiang Wenzhou 325014,China);Determination of Cable Forces in Completion State with ANSYS[J];Journal of Chongqing Jiaotong University(Natural Science);2007-05
5 SUN Ming-jun LIU Yu-jin(Wanfang Science and Technology College,Henan Polytechnic University,Jiaozuo 454003);Contract Characteristic of Fretting Fatigue Based on ANSYS Finite Element[J];Journal of Chongqing University of Science and Technology(Natural Sciences Edition);2009-05
6 XU Hong,HUANG Ping-ming(Key Laboratory for Bridge and Tunnel of Shaanxi Province,Chang'an University,Xi'an 710064,China);Analysis of daniel effect for parallel wire cable[J];Journal of Railway Science and Engineering;2008-02
7 YU Jianxin, HE Bin,YANGgang(School of Civil Engineering, Tianjin University, Tianjin 300072,China);Reliability analysis method for wind-excited vibration of large-stayed bridges[J];Earthquake Engineering and Engineering Vibration;2003-01
8 LI Xue-ming1*,ZHOU Jie-min1,LIU Qiang1,KONG Ling-feng1,ZHOU Jian-ting2(1.College of Chemistry and Chemical Engineering,Chongqing University,Chongqing 400030,China,2.School of Civil and Architecture,Chongqing jiaotong University,Chongqing 400047,China);Effect of Tension on Corrosion Behavior of Galvanized Steel Wire for Cable-Stayed Bridge[J];Electrochemistry;2007-03
9 Li Aiqun 1 Miao Changqing 1 Li Zhaoxia 1 Han Xiaolin 1 Wu Shengdong 2 Ji Lin 2 Yang Yudong 2 ( 1College of Civil Engineering, Southeast University, Nanjing 210096, China) ( 2Construction Commanding Department, Jiangsu Provincial Yangtze River Highway Bridge, Zhenjiang 212002, China);Health monitoring system for the Runyang Yangtse River Bridge[J];Journal of Southeast University (Natural Science Edition);2003-05
10 Miao Changqing~1 Li Aiqun~1 Han Xiaolin~1 Li Zhaoxia~1 Ji Lin~2 Yang Yudong~2(~1College of Civil Engineering,Southeast University,Nanjing 210096,China)(~2Jiangsu Construction Headquarters of the Yangtse River Bridge,Zhenjiang 212002,China);Monitor strategy for the structural health monitoring system of Runyang Bridge[J];Journal of Southeast University (Natural Science Edition);2005-05
【Secondary References】
Chinese Journal Full-text Database 1 Hits
1 Chen Xiaoyu,Shen Ruili,Tang Maolin(School of Civil Engineering,Southwest Jiaotong University,Chengdu 610031,Sichuan,China);Current Situation and Development for Detection and Bearing Capacity Evaluation of Main Cable of Suspension Bridge[J];Journal of Chongqing Jiaotong University(Natural Science);2013-S1
【Secondary Citations】
Chinese Journal Full-text Database 1 Hits
1 Lu Minxu; Liu Xiaokun; Wang Jianjun; Zheng Xiulin(Northwestern Polytechnical University);A MODEL OF HYDROGEN EVOLUTION AND TRANSPORT AT CRACK TIP FOR DESCRIBING THE EFFECT OF WAVEFORM ON CORROSION FATIGUE AND THE EXPERIMENTAL VERIFICATION THEREOF[J];JOURNAL OF CHINESE SOCIETY FOR CORROSION AND PROTECTION;1994-04
©2006 Tsinghua Tongfang Knowledge Network Technology Co., Ltd.(Beijing)(TTKN) All rights reserved