Solvothermal Sysnthesis of Sb-Doped SnO_2 Nanospheres and Their Properties

ZHU Bing-Jie1,2 ZHOU Feng2 ZHANG Qing-Hong2 CHEN Li-Yun2 LI Yao-Gang,1,2 WANG Hong-Zhi,2,3(1State Key Laboratory for Modification of Chemical Fibers and Polymer Materials,Donghua University,Shanghai 201620,China)(2College of Materials Science and Engineering,Donghua University,Shanghai 201620,China)(3Engineering Research Center of Advanced Class Manufacturing(MOE),Donghua University,Shanghai 201620,China)  
Sb-doped SnO2(ATO) nanosphere was synthesized by the solvothermal route,starting with SnCl4·5H2O and SbCl3.The obtained samples were characterized by X-ray diffraction pattern,transmission electron microscopy,UV-visible transmission spectrophotometer and low-impedance surface impedance instrument.The results indicated that the 80~120 nm monodispersed ATO nanosphere was tetragonal structure,which was composed of numerous 5~10 nm ATO nanocrystallines.The Sb3+ doping content had a significant impact on optical property and electrical conductivity.With the increase of Sb3+ doping content,the transmittance in visible region and the conductivity were increased first,and then decreased.The preferable nSb/nSn molar ratio was 9:100.
【Fund】: 国家自然科学基金(No.50772022 50772122);; 教育部科技创新工程重大项目培养基金项目(No.708039);; 上海市重点学科建设项目(No.B603);; 高等学校学科创新引智计划项目(No.111-2-04)资助
【CateGory Index】: TB383.1
Download(CAJ format) Download(PDF format)
CAJViewer7.0 supports all the CNKI file formats; AdobeReader only supports the PDF format.
©2006 Tsinghua Tongfang Knowledge Network Technology Co., Ltd.(Beijing)(TTKN) All rights reserved