Manifestations in Corrosion Prophase of Ultra-high Strength Steel 30CrMnSiNi2 A in Sodium Chloride Solutions

LIU Jianhua;WEN Chen;YU Mei;LI Songmei;WANG Ruiyang;Materials Science & Engineering School, Beihang University;  
The corrosion behaviors of ultra-high strength steel 30CrMnSiNi2A in sodium chloride solution were studied by weight loss and electrochemical methods. The morphology of corrosion products was observed using scanning electron microscopy(SEM) and the composition was analyzed using an energy dispersive spectroscopy(EDS) and X-Ray diffraction(XRD). The experimental results showed that the corrosion came from pitting corrosion and the rust layer was composed of outer rust layer γ-FeOOH and inner rust layer Fe2O3 with a little β-FeOOH. The correlation between corrosion rate and test time accorded with exponential rule. The corrosion current measured by polarization methods was higher than that calculated by weight loss method after a long-time immersion, the main reason was that β-FeOOH and γ-Fe2O3 transformed by γ-FeOOH led to overestimating corrosion rate. The processes of corrosion prophase were obtained from XRD and EIS results. The corrosion product, Fe(OH)2 formed at the initial stage stayed at a non-steady state and then consequently transferred to γ-FeOOH, γ-Fe2O3 or β-FeOOH.
【Fund】: Funded by the National Natural Science Foundation of China(No.51171011)
【CateGory Index】: TG172
Download(CAJ format) Download(PDF format)
CAJViewer7.0 supports all the CNKI file formats; AdobeReader only supports the PDF format.
©2006 Tsinghua Tongfang Knowledge Network Technology Co., Ltd.(Beijing)(TTKN) All rights reserved