Research on Near-Net-Shaping Ti6Al4V Alloy Parts under Two-Step Hot Isostatic Pressing

Huang Jun;Xue Pengju;Wei Qingson;Shi Yusheng;State Key Laboratory of Material Process and Die and Mould Technology,Huazhong University of Science and Technology;  
Monolithic superalloy parts shaped by hot isostatic pressing may exist low density region which will cause uneven overall performance.This paper proposed a two-step hot isostatic pressing method:at low temperature and pressure original parts were shaped without connected pores from alloy powder,then the low density regions were densed at an appropriate temperature and pressure after removing capsule and shape-control mold,which could guarantee uniform performance.Taking Ti6Al4 Vpowder material as an example,two-step HIP parameters were determined by combining finite element simulation and experimental tests,with which bladed disk parts were made.The SEM results show that:it is fine and homogeneous stripα+βphase in the parts and there is no prior particle boundary or connected pores,which contribute to the good performance of parts.The fracture morphology analysis shows that:the powder particles are metallurgically bonded firmly and no longer the crack source given appropriate processing parameters.Tensile strength of two-step HIP parts is slightly better than that of conventional HIP and as same as the forging's.
【Fund】: 国家自然科学基金资助项目(51375188);; 国家科技重大专项(2009ZX04005-041-03)
【CateGory Index】: TF124
Download(CAJ format) Download(PDF format)
CAJViewer7.0 supports all the CNKI file formats; AdobeReader only supports the PDF format.
【Citations】
Chinese Journal Full-text Database 5 Hits
1 Zhang Xiaowei,Liu Hongxi,Jiang Yehua,Wang Chuanqi,Zeng Weihua(Kunming University of Science and Technology,Kunming 650093,China);Research Progress of Functional Composite Coatings on Ti6Al4V Alloy Surface Prepared by Laser Cladding Technique[J];Rare Metal Materials and Engineering;2012-01
2 ZHANG Yi-wen(High Temperature Materials Research,CISRI,Beijing 100081,China);DEVELOPMENT IN HIP TECHNOLOGY[J];Powder Metallurgy Industry;2009-04
3 Wang Xuebin (Liaoning Technical University, Fuxin 123000, China);An Assessment of the Peak Temperature in the Adiabatic Shear Band of Ti-6Al-4V Based on the Measured Shear Stress and Local Strain[J];Rare Metal Materials and Engineering;2013-02
4 Liu Guocheng Shi Yusheng Wei Qingsong Xue Pengju(State Key Laboratory of Material Processing and Die and Mould Technology, Huazhong University of Science and Technology,Wuhan 430074,China);Numerical simulation of the densification of 316L powder during hot isostatic pressing[J];Journal of Huazhong University of Science and Technology(Natural Science Edition);2011-10
5 Lu Heng;Wei Qingsong;Xue Pengju;Wang Jiwei;Shi Yusheng;State Key Laboratory of Materials Processing and Die&Mould Technology,Huazhong University of Science and Technology;;Numerical Simulation and Verification of Near-net-shaping Inconel625 Powder Disk under Hot Isostatic Pressing[J];China Mechanical Engineering;2013-19
【Co-citations】
Chinese Journal Full-text Database 10 Hits
1 YUAN Wuhua JI Zhe ZHANG Zhaochun YANG Shouzhi (College of Material Science and Engineering,Hunan University,Changsha 410082);Progress in the Preparation of Titanium Matrix Composite[J];Materials Review;2005-04
2 HUANG Zhanghong,QU Henglei,DENG Chao,YANG Jianchao(Western Titanium Technologies Co.,LTD,Xi'an 710201);Development and Application of Aerial Titanium and Its Alloys[J];Materials Review;2011-01
3 Cheng De-bin(Representative Office of Navy in 407 Factory,Luoyang 471039,China);Difference between Titanium Alloys Used for Shipbuilding and Aerial Industry[J];Development and Application of Materials;2012-03
4 Zeng Weidong1,Shu Ying1,,Zhou Yigang1 2(1.Northwestern Polytechnical University,Xi’an 710072,China)(2.Northwest Institute for Nonferrous Metal Research,Xi’an,710016,China);Artificial Neural Network Model for the Prediction of Mechanical Properties of Ti-10V-2Fe-3Al Titanium Alloy[J];Rare Metal Materials and Engineering;2004-10
5 Qi Yunlian1,2, Zeng Weidong1, Zhao Yongqiang2, Xi Zhengping2, Wang Ruining1, Du Yu1, Hong Quan1, Guo Ping1 (1. Northwestern Polytechnical University, Xi’an 710072, China) (2. Northwest Institute for Nonferrous Metal Research, Xi’an 710016, China);Hot Plastic Deformation and the Processing Map of Ti-Al-Zr-Sn-Mo-Si-Y Alloy[J];Rare Metal Materials and Engineering;2007-11
6 Yu Teng1,Wang Lei1,Zhao Yongqing2,Liu Yang1(1.Key Laboratory for Anisotropy and Texture of Materials,Ministry of Education,Northeastern University,Shenyang 110004,China)(2.Northwest Institute for Nonferrous Metal Research,Xi'an 710016,China);Low Cycle Fatigue Behavior of Ti600 Titanium Alloy with Two Types of Microstructure[J];Rare Metal Materials and Engineering;2011-03
7 Chen Huiqin1,Cao Chunxiao2 1 Taiyuan University of Science and Technology,Taiyuan 030024,China;2 Beijing Institute of Aeronautical Materials,AVIC,Beijing 100095,China;Static Globularization of TC11 Alloy during Hot Working Process[J];Rare Metal Materials and Engineering;2011-06
8 ZHOU Hongwei~(1,2) HE Yizhu~(2**) ZHANG Wenxue~2 JIANG Jianqing~1 1.School of Material Science and Engineering,Southeast University,Nanjing 211189 2.School of Material Science and Engineering,Anhui University of Technology,Maanshan 243002;Oxidation Behavior of Ti600 Titanium Alloy[J];Chinese Journal of Materials Research;2011-03
9 CHU Mao-you,HUI Song-xiao,ZHANG Zhu,SHEN Jian-yun~* (General Research Institute for Nonferrous Metals,Beijing 100088,China);Precipitation mechanism of silicide in BT25y titanium alloy in solution treatment and thermal exposure[J];Journal of Chinese Electron Microscopy Society;2004-02
10 Ru Qiang1,Hu Xianqi2,Sheng Gang2(1.School of Physics and Telecommunication Engineering,South China Normal University,Guangzhou 510006;2.Shenzhen Goldenhouse Vacuum Technology Co.,Ltd.,Shenzhen 518103,China);Application Progress of Titanium Alloy Surface Protection Technology[J];Guangdong Chemical Industry;2010-04
China Proceedings of conference Full-text Database 4 Hits
1 LU Weijie~1 XIAO Lu~1 CHEN Yifei~1 QIN Jining~1 ZHANG Di~1 WANG Minmin~2 ZHU Feng~2 JI Bo~2 1(State Key Laboratory of Metal Matrix Composites,Shanghai Jiao Tong University,Dongchuan Road 800#,Shanghai 200240) 2(Special Steel Branch,Baoshan Iron & Steel Co.,LTD,Shuichan Road 1269#,Shanghai 200940);High Temperature Creep Behavior of in-situ synthesized Titanium Matrix Composites[A];[C];2009
2 ZHU Jing-chuan~1 WANG Yang~1 YOU Feng-hai~2 LIU Yong~1 LAI Zhong-hong~1 (1.School of Materials Science and Engineering,Harbin Institute of Technology,Harbin 150001,China; 2.Beijing Hangxing Machine Manufacturing Company,Beijing 100013,China);Microstructure and mechanical properties of thermal deformed TA15 titanium alloy[A];[C];2007
3 GUO Ping~(1,2),HONG Quan~1,ZHAO Yong-qing~(1,2),QI Yun-lian~1,XIN She-wei~1,LIU wei~1 (1.Titanium Alloy Research Center,Northwest Institute for Nonferrous Metal Research,Xi'an 710016,China; 2.School of Materials Science and Engineering,Northwestern Polytechnical University,Xi'an 710072,China);Mechanical properties of Ti600 high temperature titanium alloy[A];[C];2010
4 ZHAO Er-tuan,KONG Fan-tao,XIAO Shu-long,CHEN Yan-fei,CHEN Yu-yong (National Key Laboratory of Science and Technology on Precision Heat Processing of Metals, Harbin Institute of Technology,Harbin 150001,China);Investment casting mold filling capacity of high temperature titanium alloy IMI834[A];[C];2010
【Secondary Citations】
Chinese Journal Full-text Database 10 Hits
1 DONG Jianxin, HE Dong, ZHANG Maicang, ZENG YanpingMaterials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China;Dynamic Simulations of Element Mutual Diffusion during Hot Isostatic Pressing Diffusion Bonding[J];Journal of University of Science and Technology Beijing;2003-01
2 Zeng Quanpu Wang Zhangmo Mao Xiaonan Wu Bende Lu Feng (Northwest Institute for Nonferrous Metal Research);Investigation of Partical Reinforced Ti Based Composites[J];Rare Metal Materials and Engineering;1991-06
3 Yu Jiadou (Northwest Institute for Nonferrous Metal Research, Baoji 721014);Surface Modification Investigation of Ti Alloys by High Energy Beams[J];Rare Metal Materials and Engineering;1992-06
4 Sun Ronglu1,2, Niu Wei1, Wang Chengyang2 (1. Tianjin Polytechnic University, Tianjin 300160, China) (2. Tianjin University, Tianjin 300072, China);Microstructure and Wear Resistance of TiN-NiCrBSi Laser Clad Layer on Titanium Alloy Surface[J];Rare Metal Materials and Engineering;2007-01
5 Xu Yawei, Wang Huaming (Laboratory of Laser Materials Processing and Manufacturing, Beijing University of Aeronautics and Astronautics, Beijing 100083, China);Corrosion Behavior of Laser Melting-Deposited γ/Mo_2Ni_3Si Metal Silicide Alloy[J];Rare Metal Materials and Engineering;2007-04
6 Xue Yi, Wang Huaming (Laboratory of Laser Materials Processing and Manufacturing, Beijing University of Aeronautics and Astronautics, Beijing 100083, China);Microstructure and Wear Resistance of Laser Melted TiCo/Ti_5Si_3 Dual-Phase Intermetallic Alloy[J];Rare Metal Materials and Engineering;2007-12
7 Yuan Yuan, Wang Huaming (Beijing University of Aeronautics and Astronautics, Beijing 100083, China);Microstructure and Tribological Property of Laser Melt Deposited α/Fe_9Cr_9Si_2 Metal Silicide Alloys[J];Rare Metal Materials and Engineering;2008-09
8 Wang Xuebin (Liaoning Technical University, Fuxin 123000, China);New Method for Calculating Local Shear Strain in Adiabatic Shear Band of Titanium Alloy[J];Rare Metal Materials and Engineering;2009-06
9 Huang Yu1,2, Chen Jing1, Zhang Fengying1, Lin Xin1, Huang Weidong1 (1. State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi’an 710072, China) (2. Northwest Institute for Nonferrous Metal Research, Xi’an 710016, China);Influence of Heat Treatment on Microstructure of Laser Solid Forming Ti-6.5Al-3.5Mo-1.5Zr-0.25Si Alloys[J];Rare Metal Materials and Engineering;2009-12
10 Wang Xuebin (Liaoning Technical University,Fuxin 123000,China);Study on Evolution of Adiabatic Shear Band Width of Titanium Alloy[J];Rare Metal Materials and Engineering;2010-04
©2006 Tsinghua Tongfang Knowledge Network Technology Co., Ltd.(Beijing)(TTKN) All rights reserved