Preparation of Cementitious Materials from Blast Furnace Slag

LU Hong-xia,YU Lin,REN Xiang-qian,XU Hong-liang,ZHANG Rui (School of Materials Science and Engineering,Zhengzhou University,Zhengzhou 450001,China)  
Cementitious materials were prepared by using a large amount of blast furnace slag and a small amount of metakaolin as raw materials,as well as the mixture of NaOH and Na 2SiO 3 as alkali activator.Effects of average particle size of raw material,content of activator,curing time and temperature on the properties of cementitious materials were studied.When the content of the activator was 12%,the compressive strength was 17.66 MPa for the sample prepared from raw material granularity of 10 μm and cured at room temperature.However,it reached 27.91 MPa when the amount of activator increased to 16%.The results also showed that the compressive strength increased with the extending of the curing time.The curing temperature at 80 ℃ was more suitable for the improvement of the early strength than other temperatures but the temperature shouldnot be too high.
【Fund】: 中国博士后科研基金资助项目(20060400790);; 2008河南省高校青年骨干教师资助项目
【CateGory Index】: TQ177
Download(CAJ format) Download(PDF format)
CAJViewer7.0 supports all the CNKI file formats; AdobeReader only supports the PDF format.
【References】
Chinese Journal Full-text Database 2 Hits
1 HAO Hongshun1,XU Lihua1,ZHANG Zuoshun1,YANG Zengchao1,ZHANG Xiaomeng2,XIE Zhipeng3(1 Advanced Material &Technology Institute,University of Science and Technology Beijing,Beijing 100083;2 State KeyLaboratory of Multi-phase Complex System,Institute of Process Engineering,Chinese Academy of Sciences,Beijing 100190;3 State Key Lab of New Ceramics &Fine Processing,Tsinghua University,Beijing 100084);Development of Green Inorganic Material from Blast Furnace Slag[J];Materials Review;2010-21
2 MENG Bing-chen,ZHANG Chao-hui,JU Jian-tao(School of Metallurgical Engineering,Xi'an University of Architecture and Technology,Xi'an,Shaanxi 710055,China);New Approach and Present Situation of Recycling Utilization of Blast Furnace Slag[J];Hydrometallurgy of China;2011-01
【Citations】
Chinese Journal Full-text Database 6 Hits
1 Sun Peng Che Yuman Guo Tianyong Li Liancheng Sun Bo(Technology Center of Angang Steel Co.,Ltd.);Present Situation and Forecast of Blast Furnace Slag Comprehensive Utilization[J];Angang Technology;2008-03
2 Zhang Shuqing,Shen Yanhua;Study on the Hydrahlic Activity of Granulated Furnace Slag[J];Fly Ash Comprehensive Utilization;2008-02
3 ZHU Zheng;The Treatment and Utilization of Blast Furnace Slag[J];Sci/tech Information Development & Economy;2005-06
4 CHEN Quan-yuan,LIU Huang-huang(School of Environmental Science and Engineering,Donghua University,Shanghai 200051,China);Comprehensive Utilization of Solid Wastes Discharged from Iron and Steel Industry[J];Mining and Metallurgical Engineering;2007-03
5 GAO Shujun1 , WU Qisheng2 , ZHANG Shaoming1(1.College of Materials Science and Engineering,Nanjing University of Technology,Nanjing 210009,China; 2.Yan Cheng Institute of Technology,Yancheng 224003,China);Study on mechano-chemical activity of the slag treated by high-energy ball milling[J];Journal of Nanjing University;2002-06
6 YAO Zhen-ya,ZHENG Juan-rong,LIU Li-na (College of Civil Engineering,Zhengzhou University,Zhengzhou 450001,China);Test Investigation on the Chemical Shrinkage or Expansion of Alkali-activated Cementing Materials[J];Journal of Zhengzhou University(Engineering Science);2008-04
【Co-citations】
Chinese Journal Full-text Database 10 Hits
1 LU Xiao-shu,HE Feng-wei (Dept.of Biological and Chemical Engineering,Benxi College of Metallurgy,Benxi,Liaoning,117022 China);The Theoretical Basis of Alkali-activated slag Cement[J];Journal of Benxi College of Metallurgy;2001-04
2 XIN Ying;LU Xiao-shu(Dept.of Biological and Chemical Engineering,Liaoning Institute of Science andTechnology,Benxi,Liaoning,117022,China);Investigation and Application of Comprehensive Utilizing the Ground Granulated Blast Furnace Slag[J];Journal of Liaoning Institute of Science and Technology;2006-04
3 LIU Bo(Faculty of Civil Engineering,Changchun Instituteof Technology,Changchun 130012,China);Application of alkali-slag cementation materials in rapid determination of fired perforated bricks compressive strength[J];Journal of Changchun Institute of Technology(Natural Sciences Edition);2009-02
4 YI Zhihui JIANG Haiqing WANG Xiaojun YU Shigang (College of Material Science and Engineering,Nanjing University of Technology,Nanjing 210009);Analysis and Comparisons of ATR/YTIR,FTIR and NMR in the Activation of Fly Ash[J];Materials Review;2007-S3
5 ZHANG Chang-sen, FANG Li-mei (Dept. of Material Engineering, Yancheng Institute of Technology, Yancheng 224003, China, );Hardening mechanisms of alkali activated burned gangue cementitious material[J];Material Science and Technology;2004-06
6 ZHANG Shu-zheng, GONG Ke-cheng (Polymer structure & modification Res. Lab.,South China Univ.of Tech.,Guangzhou 510640,China);Geopolymer[J];Materials Science and Engineering;2003-03
7 GAO Fei Dept.of Mal.Sci.Eng.,Shenyang Arch. & Civ. Eng.Institute, Shenyang 110168, China;The Study and Development on Alkali-Activated Slag Cement[J];Dandong Textile College;2004-01
8 WANG Qiang,YAN Pei-yu~*(Key Laboratory of Structural Engineering and Vibration of Education Ministry,Tsinghua University,Beijing 100084,China);Morphological characteristics of hardened paste of complex binder containing high volume of slag[J];Journal of Chinese Electron Microscopy Society;2008-04
9 Jiang Fenghua1,2,Xu Delong1 (1.College of Materials Science and Engineering,Xi'an University of Architecture & Technology,Xi'an 710055,China;2.College of Materials Science and Engineering,Jinan University,Jinan 250022,China);Theory and practice of the slag cementious with low clinker[J];;2006-04
10 JIANG Feng-hua 1,2,XU De-long 1(1.College of Material Science and Engineering,Xi'an University of Architecture & Technology,Xi'an 710055,China; 2.College of Material Science and Engineering Jinan University,Jinan 250022,China);Analysis in Materials and Phases of Hydraulic Production of Slag Cement with High Volume Slag[J];Construction Conserves Energy;2007-08
China Proceedings of conference Full-text Database 5 Hits
1 Qinbo Lu Quanbing Yang (Research Lab of Materials Engineering, Tongji University, 200433, China);Influencing factors to activate the potential activity of slag[A];[C];2005
2 LI Yi-kai,LIU Fu-tian,ZHOU Zong-Hui,CHENG Xin (School of Materials Science and Engineering,University of Jinan,Jinan 250022,China);Study of Improving the Activity of Steel Slag Powder Using Compound Activator[A];[C];2008
3 ;钢渣-碱矿渣水泥强度影响因素的研究[A];[C];2005
4 Guang-yan Liu (Xiamen Academy of Building Research(Group) CO.,LTD 361004);Study on the Properties of Alkali-activated Slag and Fly-ash Concrete[A];[C];2008
5 Guangyan Chen,Chenlai Ding,Chenhui Zhou,Yaohui Zhang,Mengchen Ma (Maanshan Iron & Steel Co.,Ltd.Maanshan Anhui 243000);The development of steel slag quenching with wind technology and energy saving[A];[C];2010
【Co-references】
Chinese Journal Full-text Database 10 Hits
1 Yuan Ling Wang Zhenglan Li Yan(Department of Materials,Anhui Institute of Architecture,Hefei,230022);EFFECT OF GROUND GRANULATED BLAST FURNACE SLAG ON FREEZING-THAWING DURABILITY OF CONCRETE[J];Journal of Anhui Institute of Architecture;2002-02
2 YANG Zhong-gang, YU Jun (Transportation Department of Baotou Steel (Grup) Corporation, Baotou 014010, China; Deportment of Science and Technslogy of Baotou Steel (Group ) Corporation, Baotou 014010, China );The comprehensive utilization of blast furnace slag at Baotou Steel[J];Science & Technology of Baotou Steel(Group) Corporation;2000-02
3 LIUKeming, WANG Fuming, LI Wenchao, ME Lijun, GUO Yuyan Department of Physical Chemistry. UST Beijing, Beijing 100083, China;Synthesis of Ca-α-Sialon-SiC Powders from Blast Furnace Slag and Optimization of Its Synthesis Process[J];Journal of University of Science and Technology Beijing;2001-05
4 GAO shui-jing,ZHANG wen-li(Hebei University of Technology,Tangshan 063020);Feasibility of Tataniferous Blast—Furnance at Chengde Steel for Preparing Photocatalytic Materials[J];Shandong Ceramics;2009-02
5 LIU Mao,XUE Xiangxin,YANG He,DUAN Peining,CHA Feng,BU Erjun,ZHANG Yu (School of Materials and Metallurgy, Northeastern University,Shenyang 110004);An Experimental Study on Degradation of Ortho-nitrophenol with Titania-bearing Blast Furnace Slag[J];Materials Review;2006-01
6 ZHANG Wei~1 LU Hongxia~(1,2) YANG Huizhi~1 YANG Delin~1 HU Xing~1 (1 Key Laboratory of Materials Physics of Ministry of Education of China,Zhengzhou University,Zhengzhou 450052; 2 Postdoctoral Research Station of Zhengzhou University,Postdoctoral Working Station of Angang Group,Anyang 455004);Research Progress in Preparation of Glass-ceramics from Metallurgical Slag[J];Materials Review;2007-S3
7 Cen Yongquan(Shanghai Technical College of Metallurgy);DEVELOPMBNT OF DISPOSAL AND APPLlCATION OFIRON AND STEEL SLAG[J];IRON AND STEEL;1994-05
8 ZhouZhiming ZhangBinghuai ZhuZizong (ChongqingUniversity);A TEST OF TITANIA SEPARATION FROM HIGH TITANIA BEARING BLAST FURNACE SLAG[J];IRON STEEL VANADIUM TITANIUM;1999-04
9 YANG He , XUE Xiangxin , ZUO Liang , YANG Zhongdong (1. School of Materials and Metallurgy , Northeastern University, Shenyang 110004; 2. Department of Materials Science and Engineering, Shenyang Architecture and Civil Engineering University, Shenyang 110015, China);PHOTOCATALYTIC DEGRADATION OF BRILLIANT RED X - 3B WITH BLASTFURNACE-SLAG CONTAINING TITANIA AND RARE EARTH OXIDES[J];Journal of The Chinese Ceramic Society;2003-09
10 ZHANG Xufang1,NI Wen1,WANG Wei1,WU Junyu2(1 State Key Laboratory of the Ministry of Education for High-Efficient Mining and Safety of Metal Mines,University of Science and Technology Beijing,Beijing 100083;2 Beijing DongfangjianyuInstitute of Concrete Science and Technology,Beijing 100190);Preparation of Cementitious Material with Slag and Fly-ash[J];Materials Review;2009-12
【Secondary Citations】
Chinese Journal Full-text Database 10 Hits
1 Zhang Chunlei (Angang Technology Center);Development State of Steel Slag Reutilization Technology at Home and Abroad and Discussion on Developing Steel Slag Product in Angang[J];Angang Technology;2003-04
2 Wang Maohua Wang Baoping Hui Zhigang(Maanshan Iron and Steel Co.);Treating Methods for BF Slag[J];Angang Technology;2006-02
3 Yuan Ling Wang Zhenglan Li Yan(Department of Materials,Anhui Institute of Architecture,Hefei,230022);EFFECT OF GROUND GRANULATED BLAST FURNACE SLAG ON FREEZING-THAWING DURABILITY OF CONCRETE[J];Journal of Anhui Institute of Architecture;2002-02
4 CAO Zhi dong,XIE Liang de (Baosteel Steelmaking Department,Shanghai China,200941);Facility for Liquid Slag Treatment by Rotary Cylinder and Its Production Results At Baosteel[J];Bao Steel Technology;2001-03
5 LIUKeming, WANG Fuming, LI Wenchao, ME Lijun, GUO Yuyan Department of Physical Chemistry. UST Beijing, Beijing 100083, China;Synthesis of Ca-α-Sialon-SiC Powders from Blast Furnace Slag and Optimization of Its Synthesis Process[J];Journal of University of Science and Technology Beijing;2001-05
6 XU Shu?hui, LIN Hong?fei, PENG Guo?xun, JIANG Wen?jian, HE Chao (Northwest Institute of Light Industry, Shanxi Xianyang 712081, China);Research and Development of Slag Glass-Ceramic Products[J];GLASS & ENAMEL;2000-02
7 DENG Zai?de, ZENG Hui?dan, YING Ting?zhao (Department of Materials, South China University of Technology,Guangdong Guangzhou 510641,China);Wollastonite System Sintered Glass-Ceramics and Its Application Progress[J];Glass & Enamel;2001-01
8 Zheng Lisheng,Wang Shilong,Li Hui;el slag[J];MATERIAIS PROTECTION;1999-05
9 WU Qi sheng 1, ZHANG Shao\|ming 2,ZHOU Yong\|ming 2,FANG Ying 2 (1.Yancheng Institute of Technology,Jiangsu\ Yancheng\ 224002; 2.Nanjing University of Chemical Technology,Jiangsu nanjing \ 210009,China);The Research and Development of Mechanochemistry in Inorganic Materials Preparation[J];Materials Science and Engineering;2001-01
10 MA Hong-wen, YANG Jing, REN Yu-feng, LING Fa-ke (National Laboratory of Mineral Materials, China University of Geosciences, Beijing 100083, China);MINERAL POLYMER: CURRENT DEVELOPMENTS AND PROSPECTS[J];Earth Science Frontiers;2002-04
©2006 Tsinghua Tongfang Knowledge Network Technology Co., Ltd.(Beijing)(TTKN) All rights reserved