Comparative Analysis of Salt Spray Corrosion of 10CrMoAl Hot Rolled Sheet in Different Periods

ZHANG Dao-da;ZHOU Hui-yun;MENG Yang;YAO Deng-can;XIAO Yan-qin;Jiangxi Mechanical Science Institute;Nanchang Radio and TV University;Shandong Huijia Magnetoelectricity Technology Co.Ltd;  
The work aims to reveal cause and mechanism of corrosion resistance of 10 CrMoAl steel.Seawater corrosion of 10 CrMoAl steel was simulated by performing salt spray test(72 h,168 h and 240 h).Corrosion rate,SEM,energy spectrum,XRD and electrochemical properties of the sample subject to test were analyzed and studied.After 72 h,168 h and 240 h salt spray corrosion,the corrosion rate of the sample was 2.352 mm/a,1.915 mm/a and 2.218 mm/a,respectively.After 72 h salt spray corrosion test,Cr and Mo were mainly enriched near the substrate; after 168 h salt spray corrosion test,Cr mainly congregated seriously on the rust layer close to outer surface; after the 240 h salt spray corrosion test,Cr and Mo congregated obviously on the substrate near the rust layer again,and "white light layer" appeared simultaneously.As corrosion time prolongs,variation trends of FeCr_2O_4 and γ-Fe_2 O_3 content in the rust layer were consistent,that is,first rose continuously and then tended to be stabile.As corrosion time prolongs,corrosion rate first decreases and then increases,later decreases,and finally stabilizes.Enrichment law of Cr and Mo: first enrich at the junction of rust layer and substrate→corrosion resistant layer takes shape→corrosion layer peels off→Cr and Mo again enrich at the junction,this cycle goes round and round.This enrichment law has certain effect on corrosion prevention.In addition,FeCr_2O_4 exhibits significant corrosion resistance function when FeCr_2O_4 content is higher in rust layer.
【CateGory Index】: TG172
Download(CAJ format) Download(PDF format)
CAJViewer7.0 supports all the CNKI file formats; AdobeReader only supports the PDF format.
©2006 Tsinghua Tongfang Knowledge Network Technology Co., Ltd.(Beijing)(TTKN) All rights reserved