Effect of annealing time on microstructure and phase transformation of SMAW welded joint for T91 steel

LI Zizhou;FENG Keyun;LIU Peng;Huadian Electric Power Research Institute Co.,Ltd;School of Materials Science and Engineering,Shandong Jianzhu University;  
Optical microscope,micro-hardness tester,scanning electron microscope(SEM),energy dispersive spectrometer(EDS) and X-ray diffractometer(XRD) were applied to analyze the microstructure and phase transformation of Shielded Metal Arc Welding(SMAW) joint for T91 heat resistant steel under 760 ℃+different holding time of annealing treatment. The test results show that the hardness of welded joints decreases obviously,and the hardness distribution decreases from base metal to heat affected zone by different holding time of annealing treatment. In the same time,the microstructure in the weld zone transforms from lath martensite to acicular martensite or plate martensite with different holding time of annealing treatment. Fine dispersed precipitated phases are mainly distributed in grain boundaries and martensitic boundaries and interior after annealing treatment of holding 6 h. The properties of materials are relatively excellent by second phase strengthening.
【CateGory Index】: TG407
Download(CAJ format) Download(PDF format)
CAJViewer7.0 supports all the CNKI file formats; AdobeReader only supports the PDF format.
©2006 Tsinghua Tongfang Knowledge Network Technology Co., Ltd.(Beijing)(TTKN) All rights reserved