A Study of Pulse Electrodeposition on Suppressing the Formation of Lithium Dendrite

GUO Wen-jun;LI Zi-qiong;KE Ruo-hao;NIU Dong-fang;XU Heng;ZHANG Xin-sheng;State Key Laboratory of Chemical Engineering, East China University of Science and Technology;Collaborative Innovation Center for Petrochemical New Materials;  
A pulse charge method was used to suppress the formation of lithium dendrite on the copper electrode in 0.5 mol·L~(-1) LiBr/propylene carbonate(PC) electrolyte. The surface variation of lithium deposition was investigated by scanning electron microscope and impedance measurement. The SEM test showed that the lithium dendrites were formed on the copper electrode during the traditional process of electrodeposition. However, the formed dendrite was suppressed by pulse charge method. The results of the impedance measurement confirmed that the pulse electrodeposition could suppress the dendrite under the optimized duty ratio(0.5). The long single pulse deposition time decreased the resistance of SEI film and led to the lithium dendrite growth.The current density had an effect on dendrite and the dendrite could be effectively suppressed with no less than 2 mA·cm~(-2) of current density.
【Fund】: 安徽省石油化工新材料协同创新中心资助
【CateGory Index】: TM912
Download(CAJ format) Download(PDF format)
CAJViewer7.0 supports all the CNKI file formats; AdobeReader only supports the PDF format.
©2006 Tsinghua Tongfang Knowledge Network Technology Co., Ltd.(Beijing)(TTKN) All rights reserved