Inhibition Behavior of Dodecylamine Inhibitor in Oilfield Produced Water Containing Saturated CO_2 and SRB

LIU Hong-wei;ZHANG Fan;WU Ya-nan;TAO Yin-Guang;ZHANG Lu;LIU Hong-fang;Hubei Key Laboratory of Materials Chemistry and Service Failure,School of Chemistry and Chemical Engineering,Huazhong University of Science and Technology;  
The short-term corrosion inhibition performance of dodecylamine for 20# carbon steel in the presence of saturation CO2 and sulfate-reducing bacteria(SRB)was investigated by electrochemical impedance spectroscopy(EIS),potentiodynamic polarization,weight loss method and three-dimensional stereogram.The results showed that the corrosion inhibitor exhibited high inhibition efficiency,reaching 95.8%in the absence of SRB.After inoculating10% SRB and cultivating for 11 days at stationary temperature,when the concentration of corrosion inhibitor was less than 20mg/L,the corrosion inhibition performance was worse;when the concentration of corrosion inhibitor reached100 mg/L,the inhibition efficiency could reach 85.2% depending on weight loss method.The SRB content measurements indicated that the corrosion inhibitor had toxicity for SRB and could inhibit the growth of SRB.The corrosion morphology of specimens indicated that the specimen produced uniform corrosion accompanied by pitting corrosion in the presence of SRB and CO2;when adding 100mg/L corrosion inhibitor,the corrosion of specimen was lighter,and accompanied by a little pitting corrosion.
【Fund】: 国家自然科学基金(51171067);; 深圳市基础研发基金(JC201005310696A)
【CateGory Index】: TG174.42
Download(CAJ format) Download(PDF format)
CAJViewer7.0 supports all the CNKI file formats; AdobeReader only supports the PDF format.
【Citations】
Chinese Journal Full-text Database 5 Hits
1 YIN Cheng-xian~1,2,LAN Xin-zhe~1,FENG Yao-rong~2,BAI Zhen-quan~21.The Precious Metal Engineering Institute of Xi'an University of Arch and Tech,Xi′an 710055;2.The Key Laboratory for Mechanical and Environmental Behavior of Tubular,CNPC,Xi′an 710065;INHIBITION EFFECT OF THIOUREA ON CORROSION OF N80 STEEL IN SOLUTIONS WITH HIGH CO_2 AND Cl~-CONTENT[J];Corrosion Science and Protection Technology;2006-05
2 LU Zhao-Ling QIU Yu-Bing GUO Xing-Peng (Key Laboratory of Materials Chemistry and Service Failure of Hubei Province, Department of Chemistry and Chemical Technology, Huazhong University of Science and Technology, Wuhan 430074, P. R. China);Effect of pH Value on the Adsorption Behavior and Inhibition Mechanism of Dodecylamine on Carbon Steel[J];Acta Physico-Chimica Sinica;2008-02
3 LIU Wei* ZHAO Yan-Liang LU Min-Xu (School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, P. R. China);Corrosion Electrochemical Characteristics of X60 Pipeline Steel in SRB and CO_2 Coexistence Environment[J];Acta Physico-Chimica Sinica;2008-03
4 LIU Hong Fang, XU Li Ming, ZHENG Jia Shen (Chemistry Dept, Huazhong Univ of Science and Technology, Wuhan, Hubei 430074, China);STEEL COROSION UNDER SRB BIOFILM:A REVIEW[J];OILFIELD CHEMISTRY;2000-01
5 ZHANG Qian,CHEN Zhenyu,GUO Xingpeng(Department of Chemistry,Huazhong University of Science and Technology,Wuhan 430074);INVESTIGATION OF THE ADSORPTION BEHAVIOR OF DODECYLAMINE ON CARBON STEEL[J];Journal of Chinese Society for Corrosion and Protection;2007-05
【Co-citations】
Chinese Journal Full-text Database 10 Hits
1 LIU Jing, HOU Bao-li,ZHENG Jia shen et al(Chemistry Department, Huazhong Uni versity of Science and Technology, Wuhan. P.R. China 430074).;Advances on Corrosion Caused by Sulfate-Reducing Bacteria[J];Materiais Protection;2001-08
2 Feng Bing1,2;Chen Guoxu2;Liu Shuanghong1;Chen Junjun3;Wang Kun1(1.Beijing No.7220 mailbox,Beijing 100072;2.Logistical Engineering University,Chongqing 401331;3.Foreign Language Department,Xi'an Shiyou University,Xi'an 710065);Competitive Adsorption of Anticorrosion and Antiwear Additives[J];中国炼油与石油化工(英文版);2012-01
3 LIANG Cheng-hao1,HUANG Nai-bao1,WANG Hua2(1.Transportation & Logistics Engineering College,Dalian Maritime University,Dalian 116026,China;2.School of Chemical Engineering,Dalian University of Technology,Dalian 116012,China);Corrosion behavior of 09Cr2AlMoRE steel in seawater with sulfate-reducing bacteria[J];Journal of Dalian Maritime University;2010-01
4 ZHAO Xue-e,JIANG Jun-cheng,WANG Ruo-jun Institute of Safety Engineering,Nanjing University of Technology,Nanjing 210009;CORROSION FAILURE ANALYSIS OF OIL TANKS BY MEANS OF FAULT TREE ANALYSIS[J];Corrosion Science and Protection Technology;2006-03
5 TAI Chuang1,ZHENG Li-qun1,YANG Yong-kuan1,LI Chun-shu2,LI Tao2,WANG Jiang-yuan2,ZHANG Pei-jun21.Research Center of Materials & Environment of IMR,Shenyang 110016;2.Tianjin Petro-chemical Machinary Research Institute,Tianjin 300271;An Electrical-field Induction Based Method of Leakage Detecting for Storage Tanks[J];Corrosion Science and Protection Technology;2010-03
6 FAN Mei-mei,LIU Hong-fang School of Chemistry and Chemical Engineering,Huazhong University of Science and Technology, Wuhan 43007;Effect of Carbon Dioxide on Microbiologically Influenced Corrosion Characteristic of X60 Steel[J];Corrosion Science and Protection Technology;2012-02
7 WANG Guo-rui,LIU Zheng,LIU Er-xi,LIU Bao-yu(1.Guilin University of Technology,Guilin 541004,China;2.Puguang Branch of Zhong Yuan Oilfield,Dazhou 636150,China);Research and Development Status of the Environmental Corrosion Inhibitors[J];Corrosion & Protection;2009-10
8 LI Xiao-wei,GAO Yan-min,LI Yan-xi (Jiangsu University of Science and Technology,Zhenjiang 212003,China);Adsorption Behaviour of Thioglycolic Acid on Pre-corroded A3 Steel[J];Corrosion & Protection;2010-01
9 LIU Xiao-bo(Institute of Geology,Yushulin Oil Field Development Co.,Ltd.,Heilongjiang Daqing 163453,China);Advances in Research of Inhibiter for CO_2 Corrosion in Oil and Gas Wells[J];Guangzhou Chemical Industry;2011-06
10 LIU Zheng,LIU Jie,CHEN Shi-liang,WANG Guo-rui(College of Chemical and Biological Engineering,Guilin University of Technology,Guilin 541004,China);Adsorption Thermodynamics and Adsorption Kinetics of Substituted Pyridine Formyl Hydrazone Schiff Base Inhibitors on Q235 Carbon Steel Surface in Hydrochloric Acid[J];Materials Protection;2012-06
China Proceedings of conference Full-text Database 2 Hits
1 YUAN Qing;Niu Zengqian;BI Yanxia;LIU Yin;Engineering technology Research Institute BHDC;;Research Progress of the imidazoline inhibitor in the prevention of CO_2 corrosion[A];[C];2014
2 ;Forecast and Control of "Red Water" in Distribution System During the Source Water Switch[A];[C];2014
【Secondary Citations】
Chinese Journal Full-text Database 10 Hits
1 Liu Hongfang ; Xu Zhimou; Yang Haopeng et al;Sensitiveuess of Metals to Microbiologically induced corrosion[J];MATERIAIS PROTECTION;1999-11
2 ZHAO Jing-mao, LIU He-xia, DI Wei,ZUO Yu~*(College of Materials Science and Engineering, Beijing University of Chemical Technology, Beijing 100029, China);The Inhibition Synergistic Effect Between Imidazoline Derivative and Thiourea[J];Electrochemistry;2004-04
3 LIN Jing~(*1,2),YAN Yong-gui~2,CHEN Guang-zhang~(2),LIU Guang-zhou~2,LI Qing-fen~(1)(1.Mechanics & Electronics Engineering School,Harbin Engineering University,Harbin 154001,Heilongjiang,China,2.State Key Laboratory for Marine Corrosion and Protection,Qingdao 266071,Shandong,China);Effects of SRB Biofilm and Corrosion Product Films on Corrosion Behavior of Carbon Steel[J];Electrochemistry;2006-01
4 LI Guangchao 1,LU Changqing 2,YANG Wenzhong 2,YU Bin 2 (1 XU Zhou Chemical Industrial College of Jiangsu Province,Xuzhou 221006) (2 NAN Jing University of Chemical Technology,chemistry department,Nanjing 210009);PROGRESS ON RESEARCH OF THIOUREA AND DERIVATIVES AS CORROSION INHIBITORS[J];Corrsion Science and Technology Protection;2001-03
5 LIN Jian 1,ZHU Guowen 1,SUN Cheng 2, HAN Enhou 2,GAO Liqun 2,ZHANG Shuquan 2 (1 The Sales Storage and Transportation Sub-Company of Daqing Oilfield Limited Company,Daqing 163453; 2 State Key Laboratory for Corrosion and Protection, Institute o;A REVIEW OF MICROBIOLOGICALLY INFLUENCED CORROSION OF METALS[J];Corrsion Science and Technology Protection;2001-05
6 LI Xiangbo 1,2 ,WANG Wei 1,2 ,WANG Jia 1,3 ,LIU Wuyi 4(1.Institute of Oceanology,The Chinese Academy of Sciences,Qingdao 266071; 2 Graduate School of the Chinese Academy of Sciences,Beijing 100039; 3 State Key Laboratory for Corrosion and;EFFECT OF BIOFILMS ON METAL CORROSION IN SEA WATER[J];Corrsion Science and Technology Protection;2002-04
7 ZHANG Jun ping 1,ZHANG Qiu yu 1,YAN Hong xia 1,ZHAO Wen 1,ZHANG Yu fang 2,LU Min xu 2 1 Department of Chemical Engineering,Northwestern Polytechnical University,Xi'an 710072,China; 2 Tubular Goods Research Center of China National Petroleum Corporation,Xi'an 710065,China;HIGH EFFICIENT INHIBITORS FOR STEEL IN VAPOR-LIQUID PHASES[J];Corrosion Science and Technology Protection;2003-04
8 L Xiang-hong1,FAN Zhi-hai2,ZHAO Guo-xian2,YANG Yan-qing1,CHEN Chang-feng3,LU Min-xu3 1.Material Science and Engineering Department,Northwestern Polytechnical University,Xi'An 710072; 2.Tubular Goods Research Center of CNPC,Xi'an 710065; 3.University of Science and Technology Beijing,Beijing 100083;EFFECTS OF CATIONS ON CO_2 INDUCED CORROSION PROCESS OF P110 STEEL IN HIGH TEMPRATURE AND HIGH PRESSURE WATERS[J];Corrosion Science and Protection Technology;2005-02
9 Lu Zhanpeng(Shanghai Research Institute of Materials, Shanghai 200437) Zheng Jiashen Liu Jianghong Peng Fangming(Huazhong University of Science and Technology, Wuhan 430074);INHIBITIVE EFFECT OF THIOUREA DERIVATIVES ON CORROSION OF CARBON STEEL IN CO_2-SATURATED BRINE[J];Corrosion & Protection;1999-01
10 GU Ren′ao,DENG Zhengfa and SUN Ru Department of Chemistry and Chemical Engineering,Suzhou University,215006 Suzhou;SERS AND ELECTROCHEMISTRY STUDIES ON THE INHIBITION OF THIOUREA AND PHENYL THIOUREA ON IRON[J];SPECTROSCOPY AND SPECTRAL ANALYSIS;1997-06
©2006 Tsinghua Tongfang Knowledge Network Technology Co., Ltd.(Beijing)(TTKN) All rights reserved