Lightning strike damage test research for carbon fiber/epoxy resin matrix composite laminates when subjected to combined lightning current waveforms

XIAO Yao;YIN Junjie;LI Shulin;YAO Xueling;CHANG Fei;ZHANG Xianhang;Aeronautics and Astronautics Engineering College,Air force Engineering University;The State Key Laboratory of Electrical Insulation and Power Equipment,Xi'an Jiao Tong University;  
In order to evaluate the lighting strike damage degree and characteristics of the carbon fiber/epoxy resin matrix composite material under different aircraft lighting strike zones,three different lighting current combined waveforms(A+B,D+B+C and A+B+C+D)were used to simulate lighting strike experimental research on two kinds of composite specimens with different sizes(Type1 and Type2).Damage was assessed using visual inspection and ultrasonic testing to analyze and evaluate the lighting strike damage degree and characteristics of the composite material on the plane 1 A,2 Aand 1 Blighting zone.Meanwhile,the damage resistance characteristics of the carbon fiber/epoxy resin matrix composite specimens with copper wire mesh were compared to the benchmark values of unprotected specimens under different lighting strike zones.The results show that under different lighting strike zones,the damage modes of the carbon fiber/epoxy resin matrix composite materials caused by lighting current are basically the same,including fiber fracture,matrix ablation and delamination.For the same type of test specimens,most severe lighting damage is in the 1 Blighting zone followed by 2 Alighting zone,and 1 Alighting zone has the least degree of damage.Type1 test specimens with small length-width radio have the less damage degree than theones with large length-width radio under the same lighting strike zones.0.25 mm copper wire mesh can effectively protect the carbon fiber/epoxy resin matrix composite material.Type2 protected test specimens have 88.9%,53.9% and68.7% damage degree compared to the unprotected ones,which are located in 1 A,2 Aand 1 Blighting zones.
【Fund】: 国家自然科学基金(51477132)
【CateGory Index】: TB33
Download(CAJ format) Download(PDF format)
CAJViewer7.0 supports all the CNKI file formats; AdobeReader only supports the PDF format.
©2006 Tsinghua Tongfang Knowledge Network Technology Co., Ltd.(Beijing)(TTKN) All rights reserved