《Acta Materiae Compositae Sinica》 2018-06
Add to Favorite Get Latest Update

Flexural behavior of hybrid joints of glass fiber reinforced composite sandwich panel-steel plate

LI Yongsheng;WU Jian;WANG Weibo;National Key Laboratory of Science and Technology on Ship Vibration & Noise,China Ship Scientific Research Center(CSSRC);  
Glass fiber reinforced resin composite(GRP)sandwich panels with PVC foam or Balsa wood as core material are widely used in ship construction and ocean engineering.Flexural behaviors of hybrid joints of sandwich panel-steel plate which subjected to static and fatigue loads respectively,were investigated with both numerical and experimental methods.Different parameter sets of hybrid joint specimens were designed and fabricated.Static and fatigue four-point bending experiments were implemented to study the bending strength,stiffness and failure modes of joints.ABAQUS and MSC.Fatigue softwares were also adopted to simulate their failure characteristics.The influences of filler material,geometric length of filler and the inserted length of steel plate on the bending performance of the joint were respectively assessed.The results show that failure occurs near the filler area of joints under bending load,and failure mode mainly depends on different filler parameters.Extending the steel end to filler area can obviously improve bending performance of joint,as well as adopting Balsa wood as filler material.All specimens are failed before 106 cycles in the larger fatigue load case,while in the lower fatigue load case,all the specimens are nearly intact after 106 cycles and their residual strengths are quite close to their static ultimate strength.It is indicated that fatigue cycles with smaller loading amplitudes have little influence on their loading capacities.
【Fund】: 深水半潜式支持平台研发专项(工信部联装2016[546])
【CateGory Index】: TB332
Download(CAJ format) Download(PDF format)
CAJViewer7.0 supports all the CNKI file formats; AdobeReader only supports the PDF format.
©2006 Tsinghua Tongfang Knowledge Network Technology Co., Ltd.(Beijing)(TTKN) All rights reserved