《Materials for Mechanical Engineering》 2012-01
Add to Favorite Get Latest Update

High Temperature Compression Performance of Hot Die Steel 4Cr2Mo2W2V

SHI Nan-nan,WU Xiao-chun,CHEN Ying-wei(School of Materials Science and Engineering,Shanghai University,Shanghai 200072,China)  
Using Gleeble-3500 thermal simulation testing machine,high temperature compression tests were performed on hot die steel 4Cr2Mo2W2V.Then properties of the steel were compared with those of the 3Cr2W8V steel and H13 steel.Combining with TEM,EDS and internal friction equipment,the steel structure,shape and size of carbides as well as elastic modulus were analyzed.The results show that compared with H13 steel and 3Cr2W8V steel,4Cr2Mo2W2V steel had higher elastic modulus and high temperature compression performance at 700 ℃.The steel had fine martenite laths,carbides were mainly composed of small globular MC after quenching and tempering.Mn and Cr were primary dissolving in matrix,that increased the solution strengthenning effect which improved the high temperature compression performance.
【Fund】: 国家“十一五”科技支撑计划资助项目(2007BAE51B04);; 上海市重点学科建设资助项目(S30107)
【CateGory Index】: TG142.4
Download(CAJ format) Download(PDF format)
CAJViewer7.0 supports all the CNKI file formats; AdobeReader only supports the PDF format.
Chinese Journal Full-text Database 2 Hits
1 ;The Study of the Chemical Composition and Improvement and Development for the H13 Hot Work Die & Mold Steel[J];Die & Mould Manufacture;2006-04
2 Qin Cha~1 Yu Xuguang~1 Wu Lizhi~2 Lang Yingcui~2 Xu Changling~1 Wang Hong~2 1 School of Materials Science and Engineering,Shijiazhuang Railway Institute,Shijiazhuang 050043; 2 Hebei Metallurgy Science and Technology Co Ltd,Shijiazhuang 050031;Effect of Carbides Pile-up on Properties of Tungsten Molybdenum High Speed Steel Series[J];Special Steel;2008-03
Chinese Journal Full-text Database 10 Hits
1 XU Jin-yong1,2,TANG Wan-xing1,XU Min1,DU Li1,Gao Yuan2,XU Zhong2(1.Guilin University of Electronic Technology,Guilin 541004,China;2.Taiyuan University of Technology,Taiyuan 030024,China);Study on plasma surface metallurgy Mo-Cr alloy layer of mild steel[J];Ordnance Material Science and Engineering;2006-02
2 LIU Xiaohong1,2,WANG Maoqiu2,DONG Han2,HUA Wenjie3,XU Cunying1(1.Faculty of Materials and Metallurgical Engineering,Kunming University of Science and Technology,Kunming 650093,China;2.National Engineering Research Center of Advanced Steel Technology,Central Iron and Steel Research Institute,Beijing 10008,China;3.Special Steel Branch,Baosteel Limited Company,Shanghai 200940,China);Fatigue properties of high strength martensitic steels for transmission shaft[J];Ordnance Material Science and Engineering;2009-05
3 WANG Shuhua1,X Jiawen1,AN Xiujuan2(1.Department of Material Science and Engineering,Science and Technology University of Heilongjiang,Harbin 150027,China;2.Military Products Institute of Harbin Jiancheng Group,Harbin 150000,China);Tensile properties of 1Cr18Ni9Ti steel at moderate temperature[J];Ordnance Material Science and Engineering;2010-04
4 LUO Yang,WANG Lei,LI Zhen,SU Na,TIAN Wenhuai(Department of Materials Physics and Chemistry,School of Materials Science and Engineering,University of Science and Technology Beijing,Beijing 100083,China);Influence of two additives on the plasticity of electroformed nickel in nickel sulfamate electrolyte[J];Ordnance Material Science and Engineering;2010-06
5 ZHU Hou-guo,ZHAO Kun(FCW Department of Harbin Welding Institute,Harbin 150080);Research on Thermal Fatigue Resistance Overlay Welding Materials for Repairing the Casting Pipe Model[J];China Surface Engineering;2009-06
6 Hugjiltu,ZHANG Bang-wen(Rare Earth School,Inner Mongolia University of Science and Technology,Baotou 014010,China);Machanical properties of anisotropic silicon rubber filled iron particles[J];Journal of Inner Mongolia University of Science and Technology;2011-03
7 Hou Xuming(Material Engineering Department,Baotou Vocational & Technical College, Baotou Inner Mongolia, 014030);The Influence of Notch on the Fatigue Property of Metal Parts and its Examples[J];Journal of Baotou Vocational & Technical College;2006-01
8 Hou Xuming(Material Engineering Department,Baotou Vocational & Technical College,Baotou Inner Mongolia,014030);Cause Analysis on the Lower Contact Fatigue Strength of Nitrided Part[J];Journal of Baotou Vocational & Technical College;2009-04
9 CHEN Qingjun WEI Dandan ZHOU Xianliang HUA Xiaozhen ZHANG Jianyun AI Yunlong (School of Materials Science and Engineering,Nanchang Hangkong University,Nanchang 330063);Study of Crystallization Behavior and Mechanical Properties of Fe_(43)Cr_(16)Mo_(16)C_(18)B_5Y_2 Bulk Amorphous Alloy[J];Materials Review;2008-12
10 WANG Shao-yun1,2,LI Guo-lu1,WANG Hai-dou2,LIU Jin-hai1, XU Bin-shi2,PIAO Zhong-yu2(1 School of Materials Science and Engineering,Hebei University of Technology, Tianjin 300130,China;2 National Key Laboratory for Remanufacturing, Academy of Armored Forces Engineering,Beijing 100072,China);Influence of Microdefect on Rolling Contact Fatigue Performance of Thermal Spraying Coating[J];Journal of Materials Engineering;2012-02
China Proceedings of conference Full-text Database 8 Hits
1 WANG Shao-yun~1,LI Guo-lu~1,WANG Hai-dou~2,LIU Jin-hai~1,XU Bin-shi~2,PIAO Zhong-yu~2 (1.School of Materials Soience and Engineering,Hebei University of Technology,Tianjin 300130,China; 2.National Key Lab for Remanufacturing,Academy of Armored Forces Engineering,Beijing 100072,China);Accelerated fatigue life testing of NiCr-Cr_3C_2 coating at different loads under rolling contact condition[A];[C];2011
2 WANG Qingfang WU Xiaochun Wu Tianrong (School of Material Science and Engineering,Shanghai University,Shanghai 200072,China);A STUDY OF LOW TEMPERATURE PLASMA ASSISTED BORIDING[A];[C];2008
3 Guo Wen-tao1, LI Jun-wen1, JIA Zheng1,2 (1.College of Material and Chemical Engineering, Liaoning University of Technology, Jinzhou 121001, China; 2. College of Materials and Metallurgy,Northeastern University,Shenyang 110004,China);Effect of ultrasonic power on solidification structure and mechanical properties of ZA27 bearing alloy[A];[C];2009
4 CHEN Wan-hua,ZHOU Zhang-jian (School of Materials Science and Engineering,University of Science and Technology Beijing,Beijing 100083,China);Research on preparation and tensile properties of 9Cr-ODS steel[A];[C];2011
5 WANG Hui,XU Kun,LU Shou-dong (Baosteel Group Changzhou Roll Manufacture Company,Jiangsu,Changzhou 213019,China);Effect of eutectoid carbide on Akv Properties of 4Cr5MoSiV1 Mandrel Used Steel[A];[C];2012
6 ZHANG Bao-yi,WANG Xian-zhong,WANG Zhi-gang (School of Material Science & Engineering,Shandong Jianzhu University,Ji'nan 250101,China);The analysis of the failure of chain plate in silent chain[A];[C];2012
7 WANG Ning~1,LUO Jian-hua~1,CHANG Hong-wei~2 (1 Steelmaking General Plant of AnSteel Co.,Ltd.Anshan Liaoning 114001 2 Product Production Deparment of AnSteel Co.,Ltd.Anshan Liaoning 114001);Development and Research of A4Cr5MoSiV1 high Alloy Mandril[A];[C];2012
8 Zhi Jinhua~1,Li Xun~1,Zhang Haicun~1,Lu Zhengxin~2,Zhang Min~2,Chu Qiaoling~2 (1.Xi'an Shaangu Power Co.Ltd.,Xi'an 710075,China;2.Xi'an University of Technology,Xi'an 710048, China);Analysis on fatigue performance of 0Cr13Ni5Mo Welded Joints[A];[C];2013
©2006 Tsinghua Tongfang Knowledge Network Technology Co., Ltd.(Beijing)(TTKN) All rights reserved