《Materials for Mechanical Engineering》 2015-04
Add to Favorite Get Latest Update

Effects of Normalizing Temperature on Microstructure and Properties of Surfacing Layer on NM360 Wear-Resistant Steel

DENG Han-zhong;MENG Xiang-feng;College of Materials Science and Engineering,Liaoning Technical University;Mechanical Engineering Department,Liaoning Engineering Vocational College;  
NM360 wear resistant steel plates were repaired by surfacing with D507 MoNb welding rod,fellowed by normalizing at different temperatures.The microstructure,hardness,impact toughness and wear resistance of the surfacing layers after treatment were studied.The results show that the microstructure of surfacing layer before normalizing was martensite and carbide.The microstructure of surfacing layer after normalizing at different temperatures was ferrite,pearlite and carbide,and became coarser with the increase of normalizing temperature.Widmanstatten structure was observed in the microstructure at normalizing temperature of 1 050 ℃.And the hardness,impact toughness and wear resistance of surfacing layers decreased with the increase of normalizing temperature.The surfacing layer after normalizing at 900 ℃ had the best comprehensive performance.
【CateGory Index】: TG455;TG156.4
Download(CAJ format) Download(PDF format)
CAJViewer7.0 supports all the CNKI file formats; AdobeReader only supports the PDF format.
【Citations】
Chinese Journal Full-text Database 10 Hits
1 DENG Han-zhong1,SUN Yuan-zhang1,LIU Shao-ping1,ZHANG Wei-qiang1,KANG Shao-guang2,CAO Wen-zhi2(1.Liaoning University of Engineering and Technology,Fuxin 123000,China;2.China Coal Zhangjiakou Coal Mining Machinery Co Ltd,Zhangjiakou 075000,China);Microstructure and Mechanical Properties of K360 Wear Resistant Steel Hardfacing Alloy Layer[J];Materials for Mechanical Engineering;2008-03
2 LI Wen-bin,FEI Jing,CAO Zhong-xiao,SU Hong-ying,LI Yang(Technology Center of Angang Steel Co.,Ltd.,Anshan 114009,China);Production Status and Development Direction of Wear Resistant Steel with Low Alloy and High Strength in China[J];Materials for Mechanical Engineering;2012-02
3 DENG Han-zhong;MENG Xiang-feng;College of Materials Science and Engineering,Liaoning University of Engineering and Technology;Mechanical Engineering Department,Liaoning Engineering Vocational College;;Effect of Annealing Temperature on Microstructure and Properties of Wear-Resistant Steel NM360 Hardfacing Layer[J];Materials for Mechanical Engineering;2015-03
4 YAN Xiao feng, ZHANG Hong tao, WANG Rui zhen, PANG Gan yun (Central Iron & Steel Research Institute, Beijing 100081, China);Austenite Grain Coarsening and NbC Dissolution-Precipitation Behavior in Niobium Bearing Steel 16Mn[J];JOURNAL OF IRON AND STEEL RESEARCH;2000-02
5 ZHAO Ying-li1,2,SHI Jie2,CAO Wen-quan2,HUI Wei-jun2,XIE Gang1(1.School of Material and Metallurgy Engineering,Kunming University of Science and Technology,Kunming 650093,China;2.Institute for Structural Materials,Central Iron and Steel Research Institute,Beijing 100081,China);Effect of heating temperature on austenite grain growth of a medium-carbon Nb steel[J];Transactions of Materials and Heat Treatment;2010-04
6 WU Yu-ping~(1,2),LIN Ping-hua~2,WANG Ze-hua~2,XIE Guo-zhi~2 (1.Department of Materials Science and Technology,Southeast University,Nanjing Jiangsu 210096,China; 2.Department of Materials Science and Technology,Hehai University,Nanjing Jiangsu 210098,China);Application of Plasma Cladding Technology on Mine Machines[J];Heat Treatment of Metals;2004-09
7 HU Shi-chao1,ZENG Ben1,GU Yu-wei1,ZHU Song-he1,ZENG Wei-ming1,WU Jing1,ZHANG Heng-hua1,ZHU Ai-ling2,LIN Guo-qiang2(1.School of Materials Science and Engineering,Shanghai University,Shanghai 200072,China;2.Nanjing Iron & Steel Co.,Ltd.,Product Development Center,Nanjing Jiangsu 210035,China);Normalization process of E36 grade ship plate steel[J];Heat Treatment of Metals;2010-01
8 ZHANG Chao-jun,ZHANG Zhi-min,WANG Hong-yang(Yongcheng Coal Industry Group,Yongcheng 476600,China);Shave Central Section Slot Treatment Able to Endure Transporting Machine Paper[J];Coal Mine Machinery;2007-06
9 SUN Yuan-zhang1,DENG Han-zhong1,LIU Shao-ping1,ZHANG Wei-qiang1,KANG Shao-guang2,CAO Wen-zhi2(1.Department of Materials Science and Engineering,Liaoning University of Engineering and Technology,Fuxin 123000,China;2.China Coal Zhangjiakou Coal Mining Machinery Corporation Limited,Zhangjiakou 075000,China);Microstructures and anti-crack properties of K360 alloy overlaying[J];Journal of China Coal Society;2008-09
10 DENG Han-zhong1,WANG Da-yong2(1.College of Materials Science and Engineering,Liaoning University of Engineering and Technology,Fuxin 123000,China;2.College of Mechanical Engineering,Liaoning University of Engineering and Technology,Fuxin 123000,China);Impact of postweld heat treatment on microstructures and mechanical properties of K360 steel hardfacing layer[J];Journal of China Coal Society;2011-06
【Co-citations】
Chinese Journal Full-text Database 10 Hits
1 Hong Jinge(AISC Technology Centre);Analysis of the Fracture Cause in the Drawing Process of 65MnTi Wire Rod[J];;1997-07
2 Wang Yong Zhang Pengyuan (Angang Technology Center);Study on Optimum Heat Treatment System for Hardened and Tempered Steel[J];Angang Technology;2003-06
3 Yuan Genfu, Yan Xingshu (Department of Basic Subjects, Anhui Institute of Architecture, Hefei, 230022);STUDY ON THE NEW TECHNOLOGY OF FAST HEAT GUENCHING OF FILE[J];JOURNAL OF ANHUI INSTITUTE OF ARCHITECTURE;1998-03
4 LIU Jiang-long,PI Jin-hong(Material Science and Engineering Institute,Chongqing University,Chongqing 400044,China );Development of high-strength and low-cost constructional steels[J];Ordnance Material Science and Engineering;2003-03
5 DU Chenyang(Heat Treatment Works,Qiqihaer North Machinery Limited Company,Qiqihaer 161000,China);Crack analysis of 25CrMnSi thick steel plate after cutting[J];Ordnance Material Science and Engineering;2011-05
6 Chang Shouren(Ha bin Songian Machinery Factioy, Harbin 150046);Yu Min;INTERMEDIATE FREQUENCY TEMPERATURE CONTROLLED QUENCHING PROCESS OF CARTRIGE CASE[J];ORDNANCE MATERIAL SCIENCE AND ENGINEERING;1994-06
7 Ma Bigang;Zhang Jianhua;APPLICATION OF INDUCTION QUENCHING IN PRE-FORMED FRAGMENT STEEL[J];ORDNANCE MATERIAL SCIENCE AND ENGINEERING;1996-02
8 WANG Quan, LI Zhi-li, HAN Feng-ying (Technical Center of Baotou Steel (Group) Corporation, Baotou 014010, China);Study on slit of heavy rail waist[J];Science & Technology of Baotou Steel(Group) Corporation;2003-04
9 ZHANG Fu-qiang(Mechanical Equipment Manufacture Co.Ltd.of Baotou Steel(Group) Corp.,Baotou 014010,Nei Monggol,China);Design of Heat Treatment for High-chromium Cast Iron Grinding Bowl[J];Science & Technology of Baotou Steel(Group) Corporation;2009-01
10 Wang Zhihui Wnag Yueqin( Department of Metallic Materials Science and Engineering );The Affect of Martensite Laryer at Weld Bond On the Fracture Toughness of 9%Ni Steel Joints Welded by Austenitic Electrodes OK69.45[J];Journal of Beijing Polytechnic University;1992-03
China Proceedings of conference Full-text Database 10 Hits
1 HUANG Lei,PANG Zhao-fu,LI Wen-zhu(Ansteel Technology Center,Anshan 114009,Liaoning,China);Fracture Analysis of Four-Roll Crusher Main Shaft[A];[C];2011
2 YA NG Fan~1,XU Jin-feng~1,ZHU A i-jun~2,GA 0 Jun~2 (1.School of Materials Science and Engineering,Xi'an University of Technology,Xi'an 710048,Shanxi, China;;2.Duowei Co.Ltd.,Dqfeng 224115,Jiangsu,China);Effect of Nb on the Microstructure and Hardness of Heat-Resistant Stainless Steel[A];[C];2011
3 LIU Wu-bin~(1,2),FENG Yun-li~1 (1.Metal Material Engineering Department,Hebei Polytechnic University,Tangshan Hebei 063009,China;2.Technologic Centre, Tangshan Iron and Steel Co.,Ltd.,Tangshan Hebei 063016,China);Application of Trace Cr in Production of High-Carbon Steel Wire[A];[C];2009
4 Li Jinbo Hu Zhigang Lv Jianquan (Technology and R&D Department,Hebei Iron & Steel Group Handan Iron & Steel Group Co.,Ltd,Handan 056015,Hebei);Handan Steel heavy and medium plate mill Z ultrasonic test analyse and control[A];[C];2009
5 ;Analysis of drawing fracture of ER70S-6 wire rod[A];[C];2010
6 ;Research of SWRCH22A wire rod cold heading property improvement[A];[C];2010
7 Li Jinbo Hu Zhigang Lv Jianquan (Technology and R&D Department,Hebei Iron & Steel Group Handan Iron & Steel Group Co.,Ltd.,Handan,056015);Handan Steel Heavy and Medium Plate Mill Z Ultrasonic Test Analysis and Controling[A];[C];2009
8 ;Research on Controlled Cooling Technology of Hard Wire Production in the Fourth High-Speed Wire of Beitai Iron and Steel Group[A];[C];2010
9 CHI Shao-ning,ZHANG Shui-li,WU Qing,PEI Hong-lei,JIA Wu,LI Zesheng (JINAN DIESEL ENGINE CO.,LTD,Jinan 250306 Shandong.China);Failure Analysis of the L Type Marine Diesel Engine Piston[A];[C];2011
10 Ma Xiao-li~1 Pen Hui-fen~1 Wu Xiao-chun~2 (1.School of Material Science and Engineering,Hebei University of technology,Tianjin 300130,China;2.School of Material Science and Engineering,Shanghai University,Shanghai 200070,Chian);Effect of B on the CCT curve of the 3Cr2Mo steel[A];[C];2007
【Secondary Citations】
Chinese Journal Full-text Database 10 Hits
1 Huang Song Ma Yupu Cong Jingong Han Peng(Angang New Steel Co.,Ltd.);Study on Ship Steel Plate with High Strength of 40kg Level Produced by TMCP Technology[J];Angang Technology;2005-06
2 SHANG Deli,LV Chunfeng Technical Center,Angang Steel Co.Ltd.,Anshan 114009,China;Precipitation behavior of inclusions-induced formation nucleation of intragranular ferrite in micro-alloyed steel[J];Journal of University of Science and Technology Beijing;2008-08
3 DENG Hanzhong~1,ZHANG Weiqiang~2,SUN Yuanzhang~1,LIU Shaoping~1, KANG Shaoguang~2,CAO Wenzhi~2 (1 Dpartment of Materials Science and Engineering,Liaoning University of Engineering and Technology,Fuxin 123000; 2 School of Materials Sciene and Engineering,Shenyang Ligong University,Shenyang 110168; 3 Zhangjiakou Coal Mining Machinery Co.,Ltd,Zhangjiakou 075000);Effect of Hardness of Contact Friction Materials on Friction Behavior of K360 Wear Resistant Steel Surfacing Layer[J];Materials Review;2008-S2
4 NI Hong-qi1,2,LIU Xiang-hua2,WANG Guo-dong2(1.Mechanical College,Shenyang Institute of Chemical Technology,Shenyang 110142,China;2.State Key Lab of Rolling and Automation,Northeastern University,Shenyang 110004,China);Tensile test research of stamping property for super steel plate[J];Materials Science and Technology;2008-05
5 Wu Yuping Li Huqi Li Huidong Li Yingqing (Shandong Mining and Institute, Taian 271019);Multicomponent Cementation by Ordinary Pressure Plasma and Application to Cylinder Jacket[J];MATERIAL SCIENCE AND TECHNOLOGY;1998-03
6 PENG Sheng,ZHU Song-he,ZHANG Heng-hua,SHAO Guang-jie,XU Luo-ping(School of Materials Science and Engineering,Shanghai University,Shanghai 200072,China);Study on Austenite Grain Growth Behavior of High-Strength Shipbuilding Steel[J];Iron & Steel;2009-02
7 ZNEN Shian;ZHANG Yimin;MA Yunqing;HUANG Jinliang(Luoyang Technology Institute);MICROSTRUCTURE AND CORROSION-WEAR BEHAVIORS OF LASER REMELTED ALLOY COATINGS[J];IRON AND STEEL;1996-09
8 YANG Shang-lei~(1,2), L Xue-qin~1, ZOU Zeng-da~3, LOU Song-nian~1 (1. Shanghai Jiaotong University, Shanghai 200030, China; 2. Qingdao University of Science and Technology, Qingdao 266042, China; 3. Shandong University, Jinan 250061, China);Development of Abrasive Wearability Surfacing Electrode Based on TiC-VC[J];Materials For Mechanical Engineering;2004-06
9 CHENG Ju-qiang, LIU Zhi-xue, XU Zhen-hua, KANG Mo-kuang (Xi'an Institute of Technology, Xi'an 710032, China; Northwestern Polytechnical University, Xi'an 710072, China);Microstructure and Properties of 1 250 MPa Grade New Type Bainite Wear-resistant Steel Plate as Hot Rolled and Low Temperature Tempered[J];Materials for Mechanical Engineering;2005-10
10 GAO Cai-ru~1 MA Jin-long~1 WANG Jia-fu~1 LIU Xiang-hua~1 L(?) Chao-yang~2 (Northeastern University,Shenyang 110004,China);Effect of Welding Process on Weld Joint Impact Toughness of Ultrafine Grained Steel Plate[J];Materials for Mechanical Engineering;2006-04
©2006 Tsinghua Tongfang Knowledge Network Technology Co., Ltd.(Beijing)(TTKN) All rights reserved