Corrosion Resistance and Applicability of Four Different Steels in Sulfur Recovery Unit

ZENG De-zhi;SHANG Jian-feng;LONG De-cai;LIU Yuan-zhi;CUI Wen-peng;ZHANG Heng-wei;State Key Laboratory of Oil & Gas Reservoir Geology and Exploitation,Southwest Petroleum University;Sinopec Zhongyuan Oilfield Branch;CNOOC-Fujian LNG Co.,Ltd;  
For the sulfur recovery unit in a high sulfur purification plant,liquid sulfur corrosion coupon testing was performed to study the corrosion resistance of 20 G,16MnR,304 Land 316Lsteels in sulfur recovery unit,and corresponding preventive measures were put forward.The results show that 304 Land 316Laustenitic stainless steels had good corrosion resistance in liquid sulfur,while 20 Gand 16MnR steels suffered serious H2SO3/H2SO4 dew point corrosion,H2O-H2 S corrosion and high-temperature sulfidation corrosion,and the corrosion mode was mainly uniform corrosion.The corrosion rate of 20 G steel and 16 MnR steel increased when the process temperature was very high or very low and when the water content and oxygen content increased.The corrosion products on 20 Gsteel and 16 Mn steel were mainly iron sulfide and oxide.In corrosive vapor,the corrosion products on 20 Gsteel and 16 MnR steel were mainly FeSO4 and FeSO3,in addition,a small amount of iron sulfide and oxide were found.Based on the results above,setting corrosion monitoring points and monitoring these points for a long time were suggested.What′s more,it is necessary to keep suitable repairing and maintenance for the easily corrosive positions.
【Fund】: 国家重大科技专项项目(2011ZX05017);; 高等学校博士学科点专项科研基金资助项目(20105121120002)
【CateGory Index】: TQ125.11;TG172
Download(CAJ format) Download(PDF format)
CAJViewer7.0 supports all the CNKI file formats; AdobeReader only supports the PDF format.
【Citations】
Chinese Journal Full-text Database 10 Hits
1 GAO Wa, LUO Jian - min, YANG Jian - jun ( Ningbo Branch of China Academy of Ordnance Science, Ningbo 315103, China; No. 3 Branch of China Metallurgy Geological Exploration and Engineering Bureau, Taiyuan 030002, China);Research progress and application of double phase stainless steel[J];Ordnance Material Science and Engineering;2005-03
2 LI Ming1, LI Xiao-gang 1,2,CHEN Hua1 1.Corrosion and Protection Center of University of Science and Technology Beijing,The Key Lab.of Corrosion, Erosion and Surface Technology of Beijing,Beijing 100083; 2.State Key Laboratory of Corrosion and Protection,Institute of Metal Research, Chinese Academy of Sciences,Shenyang 110016;A REVIEW ON CORROSION BEHAVIOR AND MECHANISM OF METALS IN WET H_2S[J];Corrosion Science and Protection Technology;2005-02
3 JIN Hua feng (Department of Chemistry, Ankang Normal College, Ankang 725000, China);ANALYSIS OF CORROSION OF CONDENSER-COOLER IN SULFUR RECOVERY UNIT AND COUNTERMEASURES[J];Corrosion & Protection;2001-04
4 RONG Dong-song,JIANG Yong,GONG Jian-ming,YU Zheng-gang(College of Mechanical and Power,Nanjing University of Technology,Nanjing 210009,China);Property of Resistance to Hydrogen Sulfide Stress Corrosion Cracking of Dissimilar Welded Joints between 0Cr18Ni9 Steel and 20G Steel[J];Materials for Mechanical Engineering;2011-05
5 LIN Cui1,2,CHEN San-juan2,XIAO Zhi-yang2(1.National Defence Key Discipline Laboratory of Light Alloy Processing Science and Technology; 2.School of Material Science and Engineering,Nanchang Hangkong University,Nanchang 330063,China);Effect of Humidity on Corrosion Behavior of Low Carbon Steel in Atmosphere Containing SO_2[J];Materials for Mechanical Engineering;2012-01
6 SHANG Jian-feng;LONG De-cai;TIAN Gang;LUO Bao-jun;LIU Yuan-zhi;XIAO Guo-qing;Sinopec Zhongyuan Oilfield Puguang Branch;The College of Chemistry and Chemical Engineering,Southwest Petroleum University;State Key Laboratory of Oil and Gas Reservoir Geology and Exploitation;;Corrosion Characteristics of 20~# Steel in Water Granulation Sulfur Solidification Process[J];Corrosion & Protection;2013-10
7 Cen Ling1,Li Yang2, Wen Chongrong2, et al(1.Chongqing Natural Gas Purification Plant General;2.Research of Institute of Natural Gas Technology, Southwest Oil & Gasfield Company, Chengdu, 610213).;Corrosion and Protective Measures of Sulfur Recovery & Tail Gas Treatment Plant[J];Chemical Engineering of Oil & Gas;2009-03
8 Pei Aixia,Zhang Lisheng,Yu Yanqiu,et al(Puguang Branch Gas Purification Plant of Zhongyuan Oilfield).;Application and research of high sulfur content gas desulfurization and decarbonization process on Puguang gas field[J];Chemical Engineering of Oil & Gas;2012-01
9 Cao Shengwei,Xia Li,Zhu Ajie,et al(Sinopec Zhongyuan Oilfield Puguang Branch,Dazhou 637156,Sichuan,China);Operation optimization of tail gas treatment unit in Puguang natural gas purification plant[J];Chemical Engineering of Oil & Gas;2012-03
10 Weng Duan,Zhang Jian;Essentials in Sulfur Corrosion Research[J];Petrochemical Corrosion and Protection;1997-01
【Co-citations】
Chinese Journal Full-text Database 10 Hits
1 MIAO Lede,ZHANG Yi and WU Junfei(Research Institute,Baoshan Iron and Steel Co.,Ltd.,Shanghai 201900,China);The Progress on Quantitative Analysis of the Precipitated Phase in Stainless Steel[J];Baosteel Technology;2009-05
2 LI Ming~ 1,2) , LI Xiaogang~ 1) , CHEN Gang~ 2) , LIU Zhiyong~ 1) 1) Materials Science and Engineering School, University of Science and Technology Beijing, Beijing 100083, China 2) China Special Equipment Inspection and Research Center, Beijing 100013, China;Influencing factors of hydrogen diffusion in hydrogen sulfide environment[J];Journal of University of Science and Technology Beijing;2007-01
3 LI Ming1, 2), LI Xiaogang1), CHEN Gang2), LIU Zhiyong1)1) Materials Science and Engineering School, University of Science and Technology Beijing, Beijing 100083, China 2) China Special Equipment Inspection and Research Center, Beijing 100013, China;Experimental investigation on sulfide stress corrosion cracking of 16Mn hydrogen-induced cracking resistance steel[J];Journal of University of Science and Technology Beijing;2007-03
4 YU Lan-ying,LUO Hong,ZENG Xian-guang(Key Laboratory of Material Corrosion and Protection of Sichuan Colleges and Universities,College of Materials and Chemistry Engineering,Sichuan Universty of Science and Engineering,Zigong 643000,Sichuan,China);Microstructure of the bonding interface in an explosively cladded 2205 duplex stainless steel-16MnR steel combination[J];Explosion and Shock Waves;2010-04
5 FAN Hong-fu, LIANG Tao , ZHAO Ke-hui(1. School of Petroleum Engineering, Daqing Petroleum Institute, Daqing 163318, China; 2. Natural Gas Company, Daqing Oilfield, Daqing 163714, China).;Application of Sacrificing Magnesium Anode in Corrosion Protection of Inner Wall of Triphase Separator Used in Natural Gas Field[J];Materials Protection;2006-12
6 ZHANG Peng-cheng1,TANG Di1,WU Hui-bin1,HUANG Guo-jian2,WANG Lu-bing1,XIE Guang-yu1(1.National Engineering Research Center for Advanced Rolling Technology,University of Science and Technology Beijing,Beijing 100083,China;2.Center of Technology,Anshan Iron and Steel Group Corporation,Anshan 114001,China);Sulfide Stress Corrosion Cracking of X80 Pipeline Steel[J];Materials Protection;2008-07
7 CAI Xiao-wen,GE Lei,YU Hao-bo,CHEN Chang-feng(Department of Materials Science and Engineering,China University of Petroleum,Beijing 102249,China);Localized Corrosion Characteristics of Nickel Based Alloy 825 in Sulfur Deposition Environments[J];Journal of Materials Science and Engineering;2010-02
8 Wu Xiyun;The Technical Study of 2205 Duplex Stainless Steel Solid Solution Treatment[J];Heavy Castings and Forgings;2009-04
9 ;The pitting research of 2205 duplex stainless steel in acetic acid environments[J];Chemical Engineering & Equipment;2009-08
10 ZHANG Yan,CAI Qing-wu,XIE Guang-yu National Engineering Research Center for Advanced Rolling Technology,University of Science and Technology Beijing,Beijing 100083;INFLUENCE OF MICROSTRUCTURE ON HIC-RESISTANCEIN H_2S CONTAINING SOLUTIONS OF HIGH STRENGTH PIPELINE STEEL X65~X70[J];Corrosion Science and Protection Technology;2007-06
China Proceedings of conference Full-text Database 2 Hits
1 Li Jingtao Mo Demin luo Yingming Di xi (Wu yang Iron and Steel Co.Ltd);Low Alloy High Strength Steel for H_2S and H_2O Environment Application Developed by Wugang[A];[C];2010
2 Zeng Dezhi~1 Yang Bin~2 Tian Gang~1 Zhu Dajiang~1 Lin Yuanhua~1 Shi Taihe~1 (1.State Key Laboratory of Oil and Gas Reservoir Geology and Exploitation(Southwest Petroleum University);2.Chongqing University of Science & Technology,Chongqing,401331, China.);Finite Element Simulation and Experimental Study of Carbon Steel Tubing lined Stainless Steel Tube[A];[C];2012
【Secondary Citations】
Chinese Journal Full-text Database 10 Hits
1 JIANG Jun-cheng, WANG San-ming, WANG Zhi-rong & JIANG Hui(Institute of Safety Engineering, Nanjing University of Chemical Technology, Nanjing 210009, China) and LU Peng-yu & ZHAO Fei (Refinery Factory in Jinling Petrochemical Company, Nanjing 210037,;THE MECHANISM AND CAUSES OF THE ACCIDENTAL SPONTANEOUS COMBUSTION OF PETROLEUM CONTAINING SULFUR IN A TANK[J];Journal of Safety and Environment;2001-02
2 Sun Wenshan;PROGRESS IN DUPLEX STAINLESS STEEL AND ITS APPLICATION IN INDUSTRY[J];Ordnance Material Science and Engineering;2001-04
3 Zuo Yu;Zhang Shuxia (Department of Applied Chemistry, Beijing Institute of Chemical Technology. Beijing, 100029);Stepwise Stress Corrosion Cracking of 1Cr18Ni9Ti Stainless Steel in Aqueous H_2S Solutions[J];;1994-04
4 SONG Limin, LI Wei, ZHANG Minghui, TAO Keyi(Institute of New Catalytic Materials Science, Department of Material Chemistry, College of Chemistry, Nankai University, Tianjin 300071, China);Preparation and Characterization of Ni_2P/SiO_2-Al_2O_3 and Its Catalytic Performance for Hydrodesulfurization of 4,6-Dimethyldibenzothiophene[J];Chinese Journal of Catalysis;2007-02
5 Tan Wen-Zhi et al;A STUDY OF THE LIMITING CONCENTRATION OF HYDROGEN SULFIDE FOR SULFIDE STRESS CORROSION CRACKING OF STEELS[J];Materials Protection;1987-05
6 WANG Hui-long, LIU Hong-fang, ZHENG Jia-shen (Department of Chemistry, Huazhong University of Science and Technology, Wuhan 430074, China);Study on Inhibiting Behavior of HGZ in H_2S and NaCl-Containing Hydrochloric Acid Solutions[J];Materiais Protection;2002-01
7 XIA Xiang-ming(Aromatics Plant,Yangzi Petrochemical Co.Ltd.,Nanjing 210048,China);Stress Corrosion-Induced Cracking of 20 Steel in H_2S Solution[J];Materials Protection;2007-07
8 Zhang Xueyuan,Du Yuanlong,Zheng Liqun ( 3);Brittleness Cracking Sensitivity of 16 Mn Steel in H\-2S Solution[J];MATERIAIS PROTECTION;1998-01
9 LIANG C  (Qingdao Marine Corrosion Institute, Central Iron & Steel Research Institute,Qingdao 266071,China);Atmospheric Corrosion of Steels in China[J];Electrochemistry;2001-02
10 WANG Yi-gang 1 ,DOU Li-rong 2 ,WEN Ying-chu 1 ,ZHANG Jing 1 ,LIU Hua-yi 1 (1.Research Institute of Exploration a nd Development,PetroChina Southwe st Oil and Gas Field Company,Chengdu610051,China;2.Research Institute of Petroleum Exploration and Development,CNPC,Beijing100083,China) ;Origin of H_2S in Triassic Feixianguan Formation gas pools,Northeastern Sichuan Basin,China[J];Geochimica;2002-06
©2006 Tsinghua Tongfang Knowledge Network Technology Co., Ltd.(Beijing)(TTKN) All rights reserved