《Materials for Mechanical Engineering》 2015-09
Add to Favorite Get Latest Update

Fracture Causes of an Aero Engine Air Pipe

LI Yong-bin;XIONG Yong;CHEN Chang-da;Special Testing Center,Guizhou Liyang Aero Power Co.Ltd;  
After 264 hworking,an air pipe made of 1Cr18Ni9 Ti in an aero engine cracked around brazing root zone.Through observating the macro/micro morphology of the fracture,analyzing the chemical composition of the air pipe,calculating the strength of the air pipe,the characteristics and causes of fracture were confirmed,and the improvement measure was given.The results show that the characterisitcs of the fracture of the air pipe was fatigue fracture and the fatigue extension stress was relatively small.The large assembly stress during assembly process was the main cause of the fatigue crack initiation.Improving assembly quality can effectively prevent the fracture of air tube.
【CateGory Index】: V263.6
Download(CAJ format) Download(PDF format)
CAJViewer7.0 supports all the CNKI file formats; AdobeReader only supports the PDF format.
【Citations】
Chinese Journal Full-text Database 5 Hits
1 YANG Li(Shanghai Research Institute of Materials,Shanghai 200437,China);Fracture Causes for Railway Turnout Switch Connecting Rod[J];Materials for Mechanical Engineering;2012-06
2 XIONG Yong1,LI Yong-bin1,CHEN Chang-da1,WU Ping2,LI Wei1(1.Special Testing Center;2.Department of Quality Management, Guizhou Liyang Aero Power Co.,Ltd.,Pingba 561102,China);Cracking Failure Analysis of Compressor Rectifier Guide Vane[J];Materials for Mechanical Engineering;2013-07
3 DU Jing-feng;LIANG Jun;SUN Biao;Shenhua Guohu Electric Power Research Insitate(Beijing)Co.,Ltd.;;Reasons for Leakage of Low Temperature Superheater Pipe SA210C in Subcritical Units for A Thermal Power Plant[J];Materials for Mechanical Engineering;2013-10
4 XIONG Yong1,LE Shu-jun2,CHEN Chang-da1,ZHENG Zhi-mei1(1.Special Testing Center,Guizhou Liyang Aero Power Co.,Ltd.,Pingba 561102,China; 2.Guizhou Pingba Liyang School,Pingba 561102,China);Analysis on Cracks in 1Cr18Ni9Ti Tubing[J];Physical Testing and Chemical Analysis(Part A:Physical Testing);2013-03
5 FU Guo-ru, CHEN Rong, LV Feng-jun, LI Song-hang (Beijing Aeronautical Technology Research Center, Beijing 100076, China);Fracture Failure Analysis of a Fuel Pipe in an Aero-engines[J];Failure Analysis and Prevention;2007-01
【Co-citations】
Chinese Journal Full-text Database 10 Hits
1 XING Ze-kuan~(1),TANG En-jun~(1),DUAN Rui~(1),YAN Minghua~(1),XU Tao~(2)(1.Institute of Aeroengine Overhaul,Airforce of People's Liberation Army,Chengdu 611937;2.Lanzhou Institute of Chemical Physics,Chinese Academy of Sciences,Lanzhou 730000,China);Research on Structure and Properties of Micro-Arc Anodic Oxidation Film on TC4 Titanium Alloy[J];Materials Protection;2005-12
2 CAI Jian-ming, ZHANG Wang-feng, LI Zhen-xi, MA Ji-min, CAO Chun-xiao (Beijing Institute of Aeronautical Materials, Beijing 100095, China);Characteristic and Control of Bright and Dark Striations in TC11 Titanium Alloy Blades[J];Journal of Materials Engineering;2005-01
3 ZHANG Dan,CHEN Wen-hua,WANG Cheng-guo,DONG Feng-bo(Nanjing University of Aeronautics and Astronautics,Nanjing 210016,China);Analysis on the properties and fractures of welding joints of TA12 alloy electron beam[J];Electric Welding Machine;2011-10
4 LIU Jiang,ZHANG Xiao-yun,LIU Ming-hui,YANG Yong-jin(Beijing Institute of Aeronautical Materials,Beijing 100095,China);Effect of Acid Cleaning and Passivity Technology on the Hydrogen Content and Corrosion Resistance of TC4 Titanium Alloy[J];Plating & Finishing;2012-06
5 CHEN Huai-zhuang,DENG Zong-bai(College Aerospace Engineering,Nanjing University of Aeronautics & Astronaucics,Nanjing 210016,China);The Design and Calculation of Duct for Dual Vectoring Nozzle[J];Aircraft Design;2008-01
6 CHEN Huai-zhuang,DENG Zong-bai(College Aerospace Engineering,Nanjing University of Aeronautics & Astronaucics,Nanjing 210016,China);The Design and Calculation of Duct for Dual Vectoring Nozzle[J];Aircraft Design;2008-03
7 WANG Bin1,LIU Yong1,LIU Yan-bin1,TANG Hui-ping2,QIU Jing-wen1,WANG Yu-lin1(1.State Key Laboratory of Powder Metallurgy,Central South University,Changsha 410083,China; 2.Northwesten Research Institute for Nonferrous Metals,Xi'an 710016,China);Effects of LaH_2 and LaB_6 addition on microstructure and mechanical property of powder metallurgy Ti alloy[J];Materials Science and Engineering of Powder Metallurgy;2011-01
8 SUN Zhi-hua,LIU You-hou,ZHANG Xiao-yun,TANG Zhi-hui,LIU Ming-hui(Beijing Institute of Aeronautical Materials,Beijing 100095,China);A REVIEW OF ELECTROPLATING TECHNOLOGY ON TITANIUM AND TITANIUM ALLOYS[J];Corrosion & Protection;2005-11
9 Ru Qiang1,Hu Xianqi2,Sheng Gang2(1.School of Physics and Telecommunication Engineering,South China Normal University,Guangzhou 510006;2.Shenzhen Goldenhouse Vacuum Technology Co.,Ltd.,Shenzhen 518103,China);Application Progress of Titanium Alloy Surface Protection Technology[J];Guangdong Chemical Industry;2010-04
10 Jiusheng Ren1 Jinwen Zhou1 Xuegang Yuan2(1 Department of Mechanics,Shanghai Institute of Applied Mathematics and Mechanics,Shanghai University,Shanghai,200444)(2 College of Science,Dalian Nationalities University,Dalian,116600);DYNAMICAL ANALYSIS OF HIGH PRESSURE RUBBER HOSES[J];Chinese Journal of Solid Mechanics;2010-S1
China Proceedings of conference Full-text Database 7 Hits
1 Qi Lichun,Huang Lijun,Liu Delin,Liu Changkui,Huang Xu (Beijing Institute of Aeronautical Materials,Beijing,100095,china);Analysis of Ti-1023 Titanium Alloy forging fold[A];[C];2011
2 JIANGTao LI Yun-ju ZHAO Xu (Failure Analysis Center,Beijing Institute of Aeronautical Materials,Beijing 100095,China);Crack Analysis of Stainless Steel Pipes[A];[C];2007
3 HU Mei-juan, LIU Jin-he (School of Materials Science and Engineering, Northwestern Polytechnical University Xi'an. 710072. China);Finite element numerical simulation of 3D temperature and stress field in electron beam welding of titanium alloy[A];[C];2006
4 DANG Wei~1,XUE Xiang-yi~1,LI Jin-shan~1,HU Rui~1,ZHU Zhi-shou~2,ZHANG Feng-shou~3,ZHOU Lian~1 (1.State Key Laboratory of Solidification Processing,Northwestern Polytechnical University,Xi'an 710072,China; 2.Beijing Institute of Aeronautical Materials,Aviation Industry Corporation of China,Beijing 100095,China; 3.Western Superconducting Technologies Co.,Ltd.,Xi'an 710021,China);Influence of lamellar microstructure feature on fracture toughness of TC21 alloy[A];[C];2010
5 HE Yu-huai,LIU Chang-kui,ZHANG Bing (Beijing Institute of Aeronautical Materials,Beijing 100095,China);Fracture analysis of rotor blade of titanium alloy TC11[A];[C];2010
6 LIU Chang-kui,LI Ying,HE Yu-huai,TAO Chun-hu (Beijing Institute of Aeronautical Materials,Beijing 100095,China);Effect of laser cutting in nitrogen atmosphere on microstructure of TC11 titanium alloy and properties of welding joints[A];[C];2010
7 ZHANG Qing-yun,LU Ye-hang,LI Zhong-cheng,LI Wei-qiang (Beijing Aeronautical Manufacturing Technology Research Institute,Beijing 100024,China);a contamination layer of TC4 titanium alloy fasteners[A];[C];2010
【Secondary Citations】
Chinese Journal Full-text Database 8 Hits
1 Yan Yongjing Yin Defong Hong Weizhong (Shanghai Reasearch Institute of Materials);Failure analysis for П-11 steel superheater tubes[J];Materials For Mechanical Engineering;1985-01
2 FU Guo ru 1,2 , ZHANG Zheng 1 (1. School of Materials Science and Engineering, Beijing University of Aeronautics and Astronautics, Beijing 100083, China; 2. Beijing Aeronautical Technology Research Center, Beijing 100076, China);FAILURE ANALYSIS TECHNOLOGY[J];Physical Testing and Chemical Analysis Part A Physical Testing;2005-04
3 FU Guo-ru~1, YU Zhe-ming~2, WANG Hong-wei~1 (1. Beijing Aeronautical Technology Research Center, Beijing 100076, China; 2. Factory No.5713 of PIA , Hubei 470000, China);Main Failure Attributes and Rule of Compressor-blades in Aero-engines[J];Failure Analysis and Prevention;2006-01
4 LIU Chang-kui~1 LIU Hua~2 (1 Institute of Aeronautial Materials,Beijing 100095,China 2 Sichuan Engineering Technical College,Deyang 618000,China);Welded Joints Properties and Fracture Behavior of TA15 Titanium Alloy[J];Failure Analysis and Prevention;2006-02
5 LIU Chang-kui, LIU Xin-ling(Failure Analysis Center of Aviation Industries of China, Beijing Institute of Aeronautical Materials, Beijing 100095, China);Fatigue Crack Propagation Behavior in FZ and HAZ of TA15 Titanium Alloy Welds[J];Failure Analysis and Prevention;2007-01
6 FU Guo-ru, CHEN Rong, LV Feng-jun, LI Song-hang (Beijing Aeronautical Technology Research Center, Beijing 100076, China);Fracture Failure Analysis of a Fuel Pipe in an Aero-engines[J];Failure Analysis and Prevention;2007-01
7 ZANG Jin-xin1,BAI Ming-yuan1,JIANG Tao1,CHEN Zhi-chuan2(1.Beijing Institute of Aeronautical Materials,Beijing 100095,China;2.Cheng Du Aircraft Industrial Group Co,LTD.,Chengdu 610091,China);Failure Analysis of Compressor Blades[J];Failure Analysis and Prevention;2008-02
8 HU Xiao-hui(China Airborne Missile Academy,Luoyang 471009,China);Failure Analysis of a 1Cr18Ni9 Steel Clamp Strip[J];Failure Analysis and Prevention;2008-03
©2006 Tsinghua Tongfang Knowledge Network Technology Co., Ltd.(Beijing)(TTKN) All rights reserved