《Materials for Mechanical Engineering》 2018-09
Add to Favorite Get Latest Update

Effect of Deposition Speed on Microstructure and Properties of Double-Wire and Plasma Arc Additive Manufactured Carbon Steel Stacking Layer

LIU Siyu;FENG Yuehai;ZHAN Bin;LUO Zhenjiao;FANG Lele;School of Materials and Science Engineering,Nanjing University of Science and Technology;  
Multi-layer stacking layer samples were prepared by double-wire and plasma arc additive manufacturing process on Q235 steel plate at different deposition speeds with H08 Mn2 Si low alloy carbon steel welding wire as wire.The effects of deposition speed on the macro size,microstructure and mechanical properties of stacking layer were investigated.The results show that with the deposition speed increasing,the surface formation quality of stacking layer became better,the interlayer lines became clearer,and the macro size decreased.At a relatively high deposition speed,the ferrite grains in the stacking layer were relatively small,the content of pearlite was relatively high,and the microstructure was relatively uniform.With the increase of deposition speed,the tensile strength of stacking layer in both vertical direction and horizontal direction increased,the elongation decreased slightly,and the average microhardness inside increased.The tensile fracture was fiber-like and had a lot of dimples,indicating that the ductile fracture occurred.
【Fund】: 总装备部研究项目(7131532);; 国防创新特区项目(17-H863)
【CateGory Index】: TG456.2;TG142.1
Download(CAJ format) Download(PDF format)
CAJViewer7.0 supports all the CNKI file formats; AdobeReader only supports the PDF format.
©2006 Tsinghua Tongfang Knowledge Network Technology Co., Ltd.(Beijing)(TTKN) All rights reserved