Study on melt spinning process and properties of trilobal profiled polylactic acid fiber

Yan Yurong,Zhao Yaoming , Zhan Huaiyu, Mo Junying (Department of Polymer Materials Science and Engineering, College of Material Science and Engineering, South China University of Technology, Guangzhou 510640;State Key Laboratory of Pulp and Paper Engineering, South China University of Technology, Guangzhou 510640)  
Trilobal profiled polylactic acid (PLA) fiber with a profiled degree of 52% was prepared from PLA with intrinsic viscosity 1.51 dL/g using trilobal profiled spinneret via melt spinning process. The thermal and mechanical properties of the trilobal profiled PLA fiber were studied. The results showed that the breaking strength and initial modulus were increased with the increase of draw ratio and reached to 2. 39 cN/dtex and 17. 27 cN/dtex at 4-time drawing, respectively. The crystalline structure was formed with different crystal layerthickness during the slow cool crystallization process of PLA. A certain degree of free fibrillar structure was observed on the fiber surface due to the sheath structure of the fiber subjected to the greater drawing and orientation.
【CateGory Index】: TQ342.29
Download(CAJ format) Download(PDF format)
CAJViewer7.0 supports all the CNKI file formats; AdobeReader only supports the PDF format.
【References】
Chinese Journal Full-text Database 3 Hits
1 Chen Chunming (Department of Chemistry,Hanshan Normal University,Chaozhou 521041);Catalytic synthesis of poly(lactic acid) with ionic liquid/stannous chloride as catalyst[J];China Synthetic Fiber Industry;2009-06
2 XIE De-cheng(Shanghai Textile Research Institute, Shanghai 200082, China);Investigation on Production Process of PLA Staple Fiber[J];Synthetic Fiber in China;2008-06
3 Sun Jia1,2(1.Donghua College,Shanghai 200051,China;2.Taiyuan University of Technology,Taiyuan 030000,China);Analysis on Spinning Temperature and Draw Ratio Effected on Fiber Properties of Polylactic Acid Fiber[J];Shandong Textile Science & Technology;2012-05
【Co-citations】
Chinese Journal Full-text Database 3 Hits
1 YANG Lixin1,2,ZHAO Shuzhen1,CHEN Xuesi1,JING Xiabin1(1 State Key Lab of Polymer Physics and Chemistry,Changchun Institute of Applied Chemistry,Chinese Academy of Sciences,Changchun 130022)(2 Graduate School of Chinese Academy of Sciences,Beijing 100039)WANG Jun,LI Yunong,LI Chunhao(Jiamusi Synthetic Industry Co.Lt.,Jiamusi 154004);PRELIMINARY STUDY ON MELT-SPINNING,ADHESION AND ADSORPTION PROPERTIES OF POLY(LACTIC ACID)[J];Acta Polymerica Sinica;2007-10
2 YAO Junyan1,YANG Qingfang1,ZHOU Yingxue2,XUE Dan1(1 School of Science,Northwestern Polytechnical University,Xi'an 710072;2 School of Textiles and Materials,Xi'an University of Engineering Science and Technology,Xi'an 710048);Advances of poly(lactic acid)fibers with high performance[J];Chemical Industry and Engineering Progress;2006-03
3 Liang LI, Yancheng Textile Vocational Technology College, Yancheng, Jiangsu;Low Temperature Plasma Modification of PLA Fibres[J];Textile Dyeing and Finishing Journal;2010-10
【Co-references】
Chinese Journal Full-text Database 10 Hits
1 Yang Weicai(China Petroleum and Chemical Industry Association,Beijing 100723,China);STATUS AND DEVELOPMENT TREND OF PLASTICS INDUSTRY OF CHINA[J];Engineering Plastics Application;2007-05
2 FEI Xiaochen YAN Yongnian XIONG Zhuo (Department of Mechanical Engineering,Tsinghua University ,Beijing 100084,China);Fabrication of Scaffolds Used in Bone Tissue Engineering[J];Materials Review;2002-09
3 REN Jie, DONG Bo(Institute of Nano and Bio-polymeric Materials, College of Polymer Materials Science and Engineering, Tongji University,Shanghai 200092);The Developments of Studies on Fiber Spinning of PLA[J];Materials Review;2006-02
4 ZENG Zheng1,DONG Fang-hua1,CHEN Xiao2,ZHOU Hong2,ZHOU Jian-zhong1 (1. College of Hydroelectricity & Digital Engineering, HUST, Wuhan 430074, China; 2. The Quartermaster Research Institute of the General Logistics Department of CPLA, Beijing 100088,China);Three Dimensions Reconstruction of CT Image by MATLAB[J];Computerized Tomography Theory and Applications;2004-02
5 Zou Liming;New Hygiene Fibre[J];Technical Textiles;2000-10
6 HU Sha-li~1 , TANG Zhi-de~1, ZHAO Yi-fan~2 ( 1. College of Electrical Engineering, Chongqing University ,Chongqing 400030,China; 2. Software Department ,Nanjing Great Wall Information System Co. Ltd., Nanjing 210004,China);Research and Development a Visualization System for Medical CT Images[J];Journal of Chongqing University(Natural Science Edition);2004-09
7 SHEN Xiong-jun~(1,2),RUAN Jian-ming~1,ZHOU Zhong-cheng~1,ZHANG Haipo~1(1.State Key Laboratory of Powder Metallurgy,Central South University, Changsha 410083,China; 2.Department of Chemical and Environmental Engineering, Changsha University of Science and Technology,Changsha 410076,China);Fabrication of porous polymer scaffolds using Na_2CO_3/NaHCO_3 particulates as pore-forming material[J];Materials Science and Engineering of Powder Metallurgy;2006-05
8 Hu Zuming et al;Drying and Thermal Degradation of Poly(lactic acid)[J];Journal of Textile Research;2001-02
9 HU Yu-qun,XU Xiu-juan,ZHOU Wen-long(College of Materials & Textiles,Zhejiang Sci-Tech University,Hangzhou,Zhejiang 310018,China);Identification method of polylactide and poly-ethylene terephthalate fibers[J];Journal of Textile Research;2006-05
10 YANG Qingbin~(1,2),WANG Rui~1,LIU Yixin~2,XUN Shan~2(1.School of Textiles,Tianjin Polytechnic University,Tianjin 300160,China;2.College of Textile and Apparel,Qingdao University,Qingdao,Shandong 266071,China);Impact of heat treatment on mechanical properties of PLA fibers[J];Journal of Textile Research;2008-04
【Secondary References】
Chinese Journal Full-text Database 7 Hits
1 LIU Shuqiang1,2,DAI Jinming2,JIA Husheng1,3,LIU Xuguang3,XU Bingshe1,3(1.College of Materials Science and Engineering,Taiyuan University of Technology,Taiyuan,Shanxi 030024,China; 2.College of Textile & Arts,Taiyuan University of Technology,Jinzhong,Shanxi 030600,China; 3.Key Lab of Interface Science and Engineering in Advanced Materials(Taiyuan University of Technology), Ministry of Education,Taiyuan,Shanxi 030024,China);Drying process of polylactic acid chip for spinning filaments[J];Journal of Textile Research;2012-07
2 LIU Shuqiang1,2,ZHANG Ruiping2,JIA Husheng1,3,DAI Jinming2,LIU Xuguang3,XU Bingshe1,3(1.College of Materials Science and Engineering,Taiyuan University of Technology,Taiyuan,Shanxi 030024,China; 2.College of Textile & Arts,Taiyuan University of Technology,Jinzhong,Shanxi 030600,China; 3.Key Laboratory of Interface Science and Engineering in Advanced Materials(Taiyuan University of Technology), Ministry of Education,Taiyuan,Shanxi 030024,China);Melt spinning process of biodegradable PLA filaments[J];Journal of Textile Research;2012-11
3 GU Jin,XUE Min-min,ZOU Rong-hua (Shanghai Synthetic Fiber Research Insitute,Shanghai 200082,China);Research on Spinning Process of PLA Staple Fiber Production[J];Synthetic Fiber in China;2009-12
4 WU Gai-hong1,LIU Shu-qiang1,2(1.College of Textile & Arts,Taiyuan University of Technology,Jinzhong 030600,Shanxi,China; 2.College of Materials Science and Engineering,Taiyuan University of Technology,Taiyuan 030024,Shanxi,China);Effect of Spinning Temperature on Properties of Degradable PLA Filament[J];Synthetic Fiber in China;2012-01
5 ZHU Xiao-dan,WANG Jie(Dalian Synthetic Fiber Research & Design Institute Co.Ltd.,Dalian 116023 China);The development and application of PLA and its fiber[J];Polyester Industry;2011-02
6 LIU Li,LI Hong-xia (College of Textile and Garment,Tianjin Polytechnic University,Tianjin 300160,China);The Structure,Properties and Usages of the PLA Fiber[J];Tianjin Textile Science & Technology;2009-01
7 JIANG Quan-guang,LI Ya-bin(Textile Division,Tianjin Polytechnic University,Tianjin 300387,China);Study on guide wet performance of polylactide/cotton knits[J];Journal of Tianjin Polytechnic University;2013-03
©2006 Tsinghua Tongfang Knowledge Network Technology Co., Ltd.(Beijing)(TTKN) All rights reserved