Corrosion Resistance of Electrolessly-Deposited Nano-Sized Ni-Mo-P Alloy Coatings

Zheng Zhi-jun Lu Zhong-ming Gao Yan(School of Mechanical and Automotive Engineering,South China University of Technology,Guangzhou 510640,Guangdong,China)  
In this paper,first,two kinds of Ni-Mo-P alloy coatings respectively with nanocrystalline and mixed-crystalline(a mixture of amorphous and microcrystalline) structures were prepared by an electroless process.Next,single-and double-phase nanocrystalline Ni-Mo-P alloy coatings were obtained via different crystallization processes of the mix-structure counterpart.Then,the corrosion behaviors of the obtained coatings in 5% sulfuric acid solution were investigated according to the anodic polarization curves of the coatings.The results were finally compared with those of Ni-P coatings.It is shown that the as-plated nanocrystalline Ni-Mo-P coatings possess much higher corrosion resistance than the as-plated nanocrystalline Ni-P coatings,that the single-and double-phase nanocrystalline Ni-Mo-P coatings after the annealing are of better corrosion resistance than the as-plated mix-structure and nanocrystalline counterparts,and that,after the annealing,the corrosion resistance of the double-phase nanocrystalline Ni-Mo-P(Ni+Ni3P) coatings is similar to that of the single-phase counterparts.
【Fund】: 广东省自然科学基金资助项目(020912)
【CateGory Index】: TG174.4
Download(CAJ format) Download(PDF format)
CAJViewer7.0 supports all the CNKI file formats; AdobeReader only supports the PDF format.
【Citations】
Chinese Journal Full-text Database 2 Hits
1 LU Zhong-ming, GAO Yan, ZHENG Zhi-jun (College of Mechanical Engineering, South China University of Technology, Guangzhou 510640 China);The Effect of pH Value and MoO_4~(2-) Concentration on the Plating Rate and Structure of Electroless Ni-Mo-P alloys[J];China Surface Engineering;2005-02
2 LI Tiefan (State Key Laboratory for Corrosion and Protection,Institute of Metal Research, The Chinese Academy of Sciences,Shenyang,110016);THE ROLE OF METALLIC GRAIN BOUNDARY IN HIGH TEMPERATURE OXIDATION[J];Journal of Chinese Society For Corrosion and Protection;2002-03
【Co-citations】
Chinese Journal Full-text Database 10 Hits
1 HAN Minfang, LI Botao, PENG Suping, YANG Cuibai, LIU JingChina University of Mining & Technology, Beijing 100083, China;Solid State Reactive Mechanism of La_(1-x)Sr_xMnO_3[J];Journal of University of Science and Technology Beijing;2002-06
2 WANG Zhi-cheng~(1,2),ZHAO Zeng-qi~2,FEN Yan~3,WU Shuang-xia~2,JIANG Li-peing~2 (1.Materials Science and Engineering School, UST Inner Mongolia, Baotou 014010,China;2.Baotou Research Instiute of Rare Earth,Baotou 014010,China;3.Seamless steel Tubing Mill,Baotou Iron and Steel(Group)Co.,Baotou 014010,China);Effect of terbium on structure and magnetostriction strain of Ni-Mn-Ga[J];Journal of Baotou University of Iron and Steel Technology;2005-02
3 ZHANG Jiangao (Department of Physics,South China Normal University, Guangzhou,510631,China) B, N. Sjertsenko S, D, Antibov G, E, Goliunov (Department of Physics ,Moscow State University,Russia);Structural and Magnetic Property of Chemical Deposited Ni(P) and Ni(B) Nanofilm[J];Materials Review;2002-09
4 HAN Min-fang,PENG Su-ping,YANG Cui-bai,LIU Ze,WANG Jun-wei (School of Chemical and Environmental Engineering,China University of Mining & Technology, Beijing 100083,China,);Research of ZrO_2 nano powders sintering properties[J];Material Science and Technology;2004-01
5 LI Xin-geng~(1, 2), FU Min~2, HE Jia-wen~1s, Xi'an Jiaotong University, Xi'an 710049, China, E-mail:lxgeng@126.com;2. Shandong Electric Power Research Institute of China, Jinan 250002, China);Deformation of surface layer by shot blasting on oxidation resistance of TP304H steel at elevated temperature in water vapor[J];Material Science and Technology;2004-03
6 DING Xin-geng,YANG Hui(1.Research Center of Nanometer Science and Technology,State Key Laboratory of Silicon,Zhejiang University, Hangzhou 310027,China;2.School of Life Sciences,Zhejiang University City College,Hangzhou 310015,China);Microstructure of antibacterial film and the interface reaction to the stainless steel[J];Materials Science and Technology;2006-04
7 ZHANG Jian-gao1, B.N. Sjertsenko2 1. Department of Physics, South China Normal University, Guangzhou 510631, China; 2. Department of Physics, Moscow State University, Russia;Microstructure and Magnetic Properties of Ni_(100-x)B_x Nanofilms[J];Journal of Magnetic Materials and Devices;2006-04
8 ZHANG Xiangyi; ZHANG Xiongguan (Yan Shan University) (Gui Zhou University);THE RELATION BETWEEN THE INITIAL PERMEABILITY AND STRUCTURE PARAMETERS IN Fe_(73.5)Cu_1Mo_3Si_(13.5)B_9 ANNEALED ALLOY[J];CHINESE JOURNAL OF MATERIAL RESEARCH;1994-06
9 Chemistry and Physics Central Lab,Nanjing Normal University,Jiangsu 210024Li Gang Jin Anding Ye Chonggao Cai Zhili;Crystal Size and Phase Components of Electrolytic Manganese Dioxide Used in Battery[J];Battery Bimonthly;1992-05
10 ZHENG Zhi-Jun, GAO Yan (Faculty of Mechanical Engineering, South China University of Technology, Guangzhou 510640);Effects of W Content on the Structure and Properties of Electroless Ni-W-P Alloy Coatings[J];Electroplating & Pollution Control;2005-03
【Co-references】
Chinese Journal Full-text Database 10 Hits
1 Wei-Long Liu1), Shu-Hue Hsieh1), Shen-Jenn Hwang2), Ting-Kan Tsai1), and Wen-Jauh Chen3) 1) Department of Materials Science and Engineering, Formosa University, Huwei, China Taipei 2) Department of Mechanical Design Engineering, Formosa University, Huwei, China Taipei 3) Department of Materials Engineering, Pingtung University of Science and Technology, Pingtung, China Taipei;Tribological properties of electroless Ni-P-SiC composite coatings in rolling/sliding contact under boundary lubrication[J];北京科技大学学报(英文版);2007-02
2 Xue-tao Yuan1), Dong-bai Sun1,2), Hong-ying Yu1,2), and Yu Wang1) 1) School of Materials Science and Technology, University of Science and Technology Beijing, Beijing 100083, China 2) Beijing Engineering-Research Center for Surface Nano-Technology, Beijing 100083, China;Effect of nano-SiC particles on the corrosion resistance of NiP-SiC composite coatings[J];矿物冶金与材料学报(英文版);2009-04
3 Huang Xinmin Wu Yucheng Xie Yueqing Song Wanying;Electroless Composite Plating of Ni-P with TiO_2 nano-partides[J];China Surface Engineerign;2001-03
4 LU Zhong-ming, GAO Yan, ZHENG Zhi-jun (College of Mechanical Engineering, South China University of Technology, Guangzhou 510640 China);The Effect of pH Value and MoO_4~(2-) Concentration on the Plating Rate and Structure of Electroless Ni-Mo-P alloys[J];China Surface Engineering;2005-02
5 LIU Chuan-hui1, ZHONG Liang1, LEI Ya-min2 (1.The manufacturing science and engineering school , Southwest University of Science and Technology, Mianyang 621010, China; 2.Research Institute of Synthetic Crystals, Bejing 100018 China);Influence of Re Element on High Temperature Self-lubricating Composite Coating[J];China Surface Engineering;2008-05
6 Su Guangyao Gao Deshu Lin Chengzhang;Study of Electroless Nickel-Iron Alloy Plating[J];Surface Technology;1996-03
7 ;Technology and Coating Properties of Electroless Plating (Ni-P)-MoS2 Composite Coating[J];Surface Technology;1996-04
8 ;Stduy on the Technology and Properties of Electroless Ni-P-Al_2O_3[J];Surface Technology;1999-06
9 XU Rui-dong,GUO Zhong-cheng,WANG Jun-li,XUE Fang-qin (Faculty of Materials and Metallurgical Engineering,Kunming University of Science and Technology,Kunming 650093,China);Process and Property of Electroless Ni-Cu-P Alloy Deposits[J];Surface Technology;2004-01
10 BI Shao-dan (Chemical Engineering Branch,Shenyang Institute of Technology,Shenyang 110045, China);Study on the Control Factors of Electroless Ni-Co-P Alloy Plating[J];Surface Technology;2004-04
【Secondary Citations】
Chinese Journal Full-text Database 10 Hits
1 ZHANG Yi,LIU Chang hai,WANG Ya li (1.Chemical Engineering Department,Daqing Petroleum Institute; 2.Scientrific Research Department of Daqing Petroleum Institute,Daqing 163318,China);Study on the Deposition Mechanism of Ni-P/Ni-Mo-P Alloy[J];Surface Technology;2003-02
2 ZHENG Zhi-jun,GAO Yan(College of Mechanical Engineering,South China University of Technology,Guangzhou 510640,China).;Electroless Ni-W-P Nanocrystalline Plating Technology[J];Materials Protection;2004-03
3 Tan Fengling Jiang Bingyuan (Material Science and Engineering Department of Luoyang Institute of Technology, Luoyang 471039,China);The Effect of the Processing Parameters on the Properties of Electroless Plating Ni-Mo-P Alloy[J];Development and Application of Materials;2001-06
4 Zhang Yi, Lin Yujuan, Fang Yongkui(Daqing Petroleum Institute, Anda 151400, P. R. China);Performance Comparison of the Chemical Deposition Amorphous Ni-Mo-P and Ni-P Alloy[J];Journal of Northeast Forestry University;2002-04
5 平凉 744000);Electroless Nickel Alloy and Its Application in Electronics Industry[J];;1999-05
6 YanHong(Kunming Research Institute of Metallurgy,Kun-ming,Yunnan,China);The relation between the structure of chemical sedi-mentation Ni-Mo-P alloy and its corrosion resistance.[J];CHEMICAL ENGINEERING & MACHNERY;1994-02
7 Zhang Gang and Lu Zhu(Department of Environment Engineering ECUST,Shonghai 200237);Effect of Heat Treatment on Corrosion Performance of Electroless Ni-Mo-P Deposit Alloy and Studies of Its Anti-Corrosive Mechanism[J];JOURNAL OF EAST CHINA UNIVERSITY OF SCIENCE AND TECHNOLOGY;1994-03
8 LOU Hanyi(Corrosion Science Laboratory, Institute of Corrosion and Protection of Metals, Chinese Academy of Sciences, Shenyang) TANG Youjun, SUN Xiaofeng,GUAN Hengrong(Institute of Metals Research, Chinese Academy of Sciences,Shenyang);OXIDATION BEHAVIOUR OF SPUTTERED MICRO-GRAINED SUPERALLOY K17F AT HIGH TEMPERATURES[J];ACTA METALLRUGICA SINICA;1994-15
9 YE Changjiang; LI Tiefan; ZHOU Longjiang (Corrosion Science Lab.,Institute of Corrosion and Protection of Metals, Chinese Academy of Sciences, Shenyang 110015);EFFECT OF GRAIN SIZE ON OXIDATION BEHAVIOUR OF Ni_3Al-Zr BASE ALLOY AT ELEVATED TEMPERATURE[J];ACTA METALLRUGICA SINICA;1995-15
10 GENG Shujiang, WANG Fuhui, ZHU Shenglong( State Key Laboratory for Corrosion and Protection, Institute of Metal Research, The Chinese Academy of Sciences, Shenyang 110016);CYCLIC OXIDATION BEHAVIOR OF A SPUTTERED NANOCRYSTALLINE COATING OF IN738 SUPERALLOY[J];Journal of Chinese Society For Corrosion and Protection;2001-06
©2006 Tsinghua Tongfang Knowledge Network Technology Co., Ltd.(Beijing)(TTKN) All rights reserved