《Physical Testing and Chemical Analysis(Part A:Physical Testing)》 2017-02
Add to Favorite Get Latest Update

Color-change Method to Detect and Characterize the Fatigue Damage Process of 304 Stainless Steel

LIU Xin-yue;CHENG Cong-qian;LI Hui-fang;XU Jun;ZHAO Jie;School of Materials Science and Engineering,Dalian University of Technology;  
Color-change method was used to detect and characterize the surface damage of 304 stainless steel in the process of fatigue.And combined with scanning electron microscopy(SEM)observation,the color-change characteristic during different fatigue damage stages,as well as the effect of surface roughness and stress amplitude on color-change test results was studied.The results show that with the increase of sample deformation,the colorchange experienced three stages,i.e.,the area of color-change was large and homogeneous,the area of color-change was partial,and the area of color-change was similar to the shape of surface cracks.These three stages were corresponding to the damage of the surface passivation film and initiation of micro cracks on the surface,the main crack initiation,and the long main crack propagation respectively.The higher sample surface roughness and the greater stress amplitude of the fatigue test were,the higher color-change values were.
【Fund】: 国家自然科学基金资助项目(51571051 51101024 51101037 u1610256)
【CateGory Index】: TG142.71
Download(CAJ format) Download(PDF format)
CAJViewer7.0 supports all the CNKI file formats; AdobeReader only supports the PDF format.
【Citations】
Chinese Journal Full-text Database 10 Hits
1 BIAN Chun-hua;FANG Ke-wei;ZHANG Wei;MIAO Xue-liang;CNNC Nuclear Power Operations Management Co.,Ltd.;Suzhou Nuclear Power Research Institute;;Analysis on Fracture Reason of Pneumatic Actuator Bolt in Steam Trap Valve of High Pressure Heating System[J];理化检验(物理分册);2013-11
2 CHENG Cong-qian;CAO Tie-shan;SONG Guan-yu;ZHAO Jie;LEI Ming-kai;DENG De-wei;School of Materials Science and Engineering,Dalian University of Technology;;A New Method of Chromaticity Inspection for Evaluating Quality of Passive Film on Stainless Steel[J];原子能科学技术;2013-10
3 CHENG Cong-qian,FU Qin-qin,CAO Tie-shan,ZHAO Jie(School of Materials Science and Engineering,Dalian University of Technology,Dalian 116085,Liaoning,China);Effect of Passive Film Quality on Corrosion Resistance of Austenitic Stainless Steel and Chromaticity Inspection[J];材料工程;2013-08
4 XIONG Yong1,LE Shu-jun2,CHEN Chang-da1,ZHENG Zhi-mei1(1.Special Testing Center,Guizhou Liyang Aero Power Co.,Ltd.,Pingba 561102,China; 2.Guizhou Pingba Liyang School,Pingba 561102,China);Analysis on Cracks in 1Cr18Ni9Ti Tubing[J];理化检验(物理分册);2013-03
5 WANG Liang,HUANG Xin-yue,GUO Guang-ping (Beijing Institute of Aeronautical Materials,Beijing 100095,China);Fatigue Crack Growth Behavior of Superalloy Detected by High Temperature Direct Current Potential Drop Method[J];理化检验(物理分册);2011-08
6 WANG Liang,DING Chuan-fu(Institute of Aeronautical Materials,Beijing 100095,China);APPLICATION OF DC CURRENT METHOD FOR CRACK LENGTH MEASUREMENT IN HIGH TEMPERATURE[J];理化检验(物理分册);2006-09
7 CAO Yiping~1,LI Luming~1,HUANG Gang~1,DONG Jie~1,HAO Hongwei~1,XIE Yixue~2(1.Department of Mechanical Engineering,Tsinghua University,Beijing 100084,China;2.Wanjie Group Co.,Ltd,Zibo 255213,China);Fatigue crack detection based on electromagnetic testing[J];清华大学学报(自然科学版);2005-11
8 ZENG Hai-yun,DUAN Yi-xiong,WANG Ping-hua(CSR Zhuzhou Electric Locomotive Co.,Ltd.,Zhuzhou 412001,China);Method for ultrasonic testing of fatigue crack of 35CrMo axle[J];电力机车与城轨车辆;2005-06
9 Li Yaodong Huang Chengxiang Hou Li (College of Manufacturing Sci and Eng, SCU University, Chengdu 610065);DETECTING ACOUSTIC EMISSION SIGNALS FROM FATIGUE CRACK PROPAGATION[J];振动与冲击;2005-02
10 CHEN Zhen-chun,YANG Xian-shun;Fatigue crack of engineering crane and magnetic power inspection[J];建筑机械;2004-05
【Co-citations】
Chinese Journal Full-text Database 9 Hits
1 MENG Wenhua;ZENG Weichuan;GU Jingqing;CHEN Xu;LIU Jinglin;Wuxi Institute of Supervision & Testing on Product Quality;;Failure Analysis on Early Fatigue Fracture of a 10.9 Grade Bolt[J];理化检验(物理分册);2017-05
2 LIU Xin-yue;CHENG Cong-qian;LI Hui-fang;XU Jun;ZHAO Jie;School of Materials Science and Engineering,Dalian University of Technology;;Color-change Method to Detect and Characterize the Fatigue Damage Process of 304 Stainless Steel[J];理化检验(物理分册);2017-02
3 YANG Shu-kai;CHENG Cong-qian;HOU Yan;ZHAO Jie;PAN Shao-dong;School of Materials Science and Engineering,Dalian University of Technology;Suzhou Nuclear Power Research Institute;;Color-Change Inspection Application and Quality Control Strategy for Surface Passivation on Stainless Steel Equipment in Nuclear Power Plant[J];材料保护;2016-12
4 JI Bohai;YUANZHOU Zhiyuan;FU Zhongqiu;XIE Faxiang;College of Civil and Transportation Engineering, Hohai University;;Fatigue crack features in steel box girder by ultrasonic testing[J];中南大学学报(自然科学版);2016-06
5 YAO Bing-yin;ZHANG Zhi-bo;MA Jian-min;WANG Yu-xing;LU Zheng-xin;Xi'an Thermal Power Research Institute Co.,Ltd.;Xi'an University of Technology;;Causes Analysis on Fracture of High-strength Bolts for Fastening Wind Turbine Blades[J];理化检验(物理分册);2016-05
6 Gao Hongli;Zheng Huanbin;Jiang Wei;Qi Zicheng;Key Laboratory of Special Purpose Equipment and Advanced Machining Technology,Ministry of Education & Zhejiang Province,Zhejiang University of Technology;Ningbo Branch of China Academy of Ordnance Science;;Online Measuring Method of Fatigue Crack Growing Length Based on Image Processing Technology[J];中国机械工程;2016-07
7 SHI Yue;DONG Lihong;WANG Haidou;LI Guolu;LIU Shenshui;School of Materials Science and Engineering,Hebei University of Technology;National Key Laboratory for Remanufacturing,Academy of Armored Forces Engineering;;Research Progress of Acoustic Emission Technology in the Domain of Fatigue Failure[J];材料导报;2016-03
8 ZHENG Huanbin;LIU Hui;LIU Huan;ZHU Yalun;QI Zicheng;Key Laboratory of E&M ( Zhejiang University of Technology),Ministry of Education & Zhejiang Province;Ningbo Branch of China Academy of Ordnance Science;;Crack Image Acquisition System in Fatigue Crack Propagation Test[J];轻工机械;2015-06
9 Hou Youzhong;Jiang Jiandong;Zhu Chongfei;Cao Junci;Ye Jun;CSR Qingdao Sifang Co.,Ltd.;School of Electrical Engineering,Beijing Jiaotong University;Luoyang LYC Bearing Co.,Ltd.;;Detection and Analysis of Degraded Grease for EMU Axle Box Bearings[J];轴承;2015-10
【Secondary Citations】
Chinese Journal Full-text Database 10 Hits
1 WANG Rong,LI Ling(Shanghai Research Institute of Materials,Shanghai 200437,China);Failure Analysis on Fracture of Worm-gear Connecting Bolts[J];理化检验(物理分册);2012-06
2 XU Kaidong,LI Sihai,ZHANG Fangang(Zhejiang Provincial Special Equipment Inspection and Research Institute,Hangzhou 310022,China);Failure Analysis of Injector Platen Bolt Fracture[J];热加工工艺;2012-07
3 LEI Mingkai,WANG Kesheng,OU Yixiang,ZHANG Lei Surface Engineering Laboratory,School of Materials Science and Engineering,Dalian University of Technology, Dalian 116024;PLASMA-BASED LOW-ENERGY NITROGEN ION IMPLANTATION OF 2Crl3 MARTENSITIC STAINLESS STEEL USED IN PUMPS AND VALVES[J];金属学报;2011-12
4 WANG Jian-lin;CHEN Juan-hua;XU Jian-hua (The Power Station Auxiliary Equip.Plant,Shanghai Electric Power Generation Equipment Co.,Ltd.,Shanghai,200090,China);Acid Pickling & Passivation of Stainless Steel Equipment and its Quality Control-Technique[J];电站辅机;2011-03
5 WU Lu-ying1, PAN Bing-quan2, LIU Jun-quan1 (1. Corrosion Control and Surface Engineering Research Institute, South China University of Technology, Guangzhou 510640; 2. Guangdong Nan-fang Soda Ash Industrial Company Ltd. , Guangzhou 510760, Chi-na);Comparison of the Methods for Monitoring Passive Finns on Stainless Steel[J];材料保护;2009-08
6 HU Xiao-hui(China Airborne Missile Academy,Luoyang 471009,China);Failure Analysis of a 1Cr18Ni9 Steel Clamp Strip[J];失效分析与预防;2008-03
7 DING Chuan-fu,WANG Liang,LIU Jian-zhong(Beijing Institute of Aeronautical Materials,Beijing 100095,China);Investigation and Application of the dc-Electrical Potential Difference Method to Automatic Fatigue Crack Length Measurements[J];实验室研究与探索;2007-10
8 CHENG Xuequn1),LI Xiaogang1),DU Cuiwei1),YANG Lixia2)1)Materials Science and Technology School,University of Science and Technology Beijing,Beijing 100083,China2)School of Material Science & Chemistry Engineering,China University of Geoscience(Wuhan),Wuhan 430074,China;Electrochemical properties of passivation film formed on 316L stainless steel in acetic acid[J];北京科技大学学报;2007-09
9 FU Guo-ru, CHEN Rong, LV Feng-jun, LI Song-hang (Beijing Aeronautical Technology Research Center, Beijing 100076, China);Fracture Failure Analysis of a Fuel Pipe in an Aero-engines[J];失效分析与预防;2007-01
10 WANG Liang,DING Chuan-fu(Beijing Institute of Aeronautical Materials,Beijing 100095,China);Application of DC Current Method for Crack Length Measurement in High Temperature[J];航空材料学报;2006-03
©2006 Tsinghua Tongfang Knowledge Network Technology Co., Ltd.(Beijing)(TTKN) All rights reserved