Preparation of Warm Compacted and Sintered WC/45 Steel Composite and Its Wear-Resistance

Cheng Xiaole,Gao Yimin,Xing Jiandong,Tan Min Xi′an Jiaotong University, Xi′an  710049, China)  
The WC particles (0.076 mm~0.100 mm in size) are selected as reinforced phase, and 45 steel(carbon steel with 0.45%C) as matrix. The techniques of warm compaction are systematically investigated with powder metallurgy solid phase sintering method. The performance of sliding friction wear of the composites is tested on a pin on disk tester. The test results of warm compaction show that the composite sample containing 50%WC and 50% 45 steel possesses the perfect compaction density(9.436 2 g/cm~3) and the relative density reaches 91.6% under the condition of 140 ℃ compaction temperature, 320 kN stress, and lubricated with zinc stearate. The results of wear test show that the composite sample under the condition of warm compaction gains the best wear property, and the relative wear resistance is the 2.9 times of 15Cr cast iron, 2.6 times of 20Cr cast iron and 2.8 times of the composite sample under the condition of room temperature compaction. And the wear mechanism of particle composites is analyzed by SEM. .
【CateGory Index】: TB333
Download(CAJ format) Download(PDF format)
CAJViewer7.0 supports all the CNKI file formats; AdobeReader only supports the PDF format.
【References】
Chinese Journal Full-text Database 1 Hits
1 YE Jing1,YOU Xian-qing1,HUANG Man-ping2,MA Jian-guo2,LIU Bao1(1.School of Material Science and Engineering,Hefei University of Technology,Hehui 230009,China;2.Anhui Architectural Engineering College,Hefei 230023,China);The Latest Development of WC_P/Steel-based Compositesand Compound Roller[J];Rare Metals and Cemented Carbides;2008-03
【Citations】
Chinese Journal Full-text Database 1 Hits
1 South China University of Technology Zhang Shuangyi Li Yuanyuan;The changing of wall thickness The Mixing of Iron Powders and Polymer Additives in Warm Compaction[J];Metal Forming Technology;1999-03
【Co-citations】
Chinese Journal Full-text Database 6 Hits
1 LI Yuan\|yuan, XIANG Pin\|feng, XU Zheng, NI Dong\|hui, WU Yuan\|biao (Department of Mechatronic & Engineering,South China University of Technology Guangzhou\ 510640,China);The Densification Mechanism of Warm Compaction Technology[J];Materials Science and Engineering;2001-01
2 Wang Shanglin, Ngai Tungwai Leo, Chen Weiping, Pan Guoru, Li Yuanyuan (Guangdong Key Laboratory for Advanced Metallic Materials Research and Processing College of Mechanical Engineering, South China University of Technology, Guangzhou 510640,China);Warm compaction properties of the binder treated iron-base powder[J];Powder Metallurgy Technology;2005-03
3 LI Yuan-yuan, XIAO Zhi-yu, Tungwai Leo Ngai, ZHANG Wen, CHEN Wei-ping (College of Mechanical Engineering, South China University of Technology, Guangzhou 510640, China);Research and application into warm compaction technology[J];Journal of Guangdong Non-ferrous Metals;2004-01
4 XIANG Pin feng, LI Yuan yuan, LONG Yan, NI Dong hui, ZHANG Hua, WU Yuan biao (South China University of Technology, Guangzhou 510640, China);Effects of Polymeric Lubricant Adding Method on the Warm Compaction of Powder Metallurgy[J];Materials For Mechanical Engineering;2001-03
5 NING Hai-xia1,CHENG Xiao-le2(1.Suzhou Vocational University,215104 Suzhou,China;2.State Key Laboratory for Mechanical Behavior of Materials,Xi'an Traffic University,Xi'an 710049,China);Study on Powder Metallurgy Technology for WC Particles Reinforced Metal Matrix Composites[J];Coal Mine Machinery;2009-07
6 NING Haixia1,CHENG Xiale2(1. Suzhou Vocational University,Suzhou 215011,China; 2. State Key Laboratory for Mechanical Behavior of Materials,Xi'an Jiaotong University,Xi'an 710049,China);Preparation and Wear Resistance Research on 45 Steel Matrix Composite Reinforced by WC Particles[J];New Technology & New Process;2010-01
【Co-references】
Chinese Journal Full-text Database 10 Hits
1 YUAN Zhong-yue 1, ZHANG Zhong-ming 1, LI Chao-sheng 2, LIN You-dong 1 (1.Materials Science & Engineering Institute, Xi'an University of Technology, Xi'an 710048, China; 2.Hefei Institute of Solid Physics, SINICA, Hefei 230031, China);Microstructures of surface alloying layer prepared by evaporable pattern casting process[J];Ordnance Material Science and Engineering;2002-04
2 Zhang Liying(Material Science and Engineering School, UST Beijing, Beijing 100083, China)Huang Zhuo(General Research Institutefor Non-ferrous Metals,Beijing 100088,China)Wu Chengyi(Material Science and Engineering School, UST Beijing, Beijing 100083, Chin;Dissolving-precipitating Mechanism of WC Particle-reinforced High Speed Steel Composites Fabricated by Spray Forming[J];JOURNAL OF UNIVERSITY OF SCIENCE AND TECHNOLOGY BEIJING;1997-06
3 YANG Xia, CHEN Bangfeng, GUO Shiju Institute of Powder Metallurgy, University of Science and Technology Beijing, Beijing 100083, China;Eloctrostatic and Lubricant Performances of Compound Lubricants in P/M Elec-trostatic Die Wall Lubrication[J];Journal of University of Science and Technology Beijing;2004-04
4 Xu binshi; Liang Xiubing ;Ma Shining ;Liu Shican;Research on the Newly Developed High Velocity Arc Spray Gun[J];CHINA SURFACE ENGINEERIGN;1998-03
5 Shi Changxu Xu Binshi ZhangPing;Development of Surface Engineering in the 21st Century[J];China Surface Engineerign;2001-01
6 XU Bingshi LI Renhan LIANG Xiubing;Progress of Green Remanufacture Engineering[J];China Surface Engineerign;2001-02
7 XU Bin-shi ZHANG Wei LIU Shi-can MA Shi-ning XU Yi (National Key Laboratory For Remanufacturing Armored of Force Engineering,Beijing 100072);Smart Self-repairing Technology for Modern Equipment[J];China Surface Engineering;2004-01
8 HU Jun zhi 1, CHEN Xue rong 1, MA Shi ning 1, OU Zhong wen 2 (1. Department of Material Science and Engineering, Academy of Armored Force Engineering, Beijing 100072,China; 2.Logistical Engineering University of PLA,Chongqing 400041,China) [;Technical Optimization and Property Research on Intermetallic Matrix Composite Coating by High Velocity Arc Spraying[J];Surface Technology;2003-04
9 HE Xin, WANG Jun, SUN Bao-de(School of Materials Science and Engineering,Shanghai Jiaotong University,Shanghai 200030,China);Influence of Thermal Spray Techniques on Sliding Wear Behavior of Coatings[J];Surface Technology;2003-05
10 YUAN Zi-liang~1, MO Ya-wu~2 (1.Shaoyang College, Shaoyang 422004, China; 2.The College of Engineering in Hunan Agricultural University, Changsha 410128, China);Effect of Technological Parameter of Arc Spraying on Microstructures and Properties of Coating[J];Surface Technology;2005-03
【Secondary References】
Chinese Journal Full-text Database 4 Hits
1 MA Zhuang,WANG Wei,LI Zhichao(School of Material Science and Engineering,Liaoning Technical University,Fuxin 123000);Study on Properties of Ternary Boride Ceramic Coating by Solid Phase Reaction Method[J];Materials Review;2010-08
2 LI Xiu-qing,SONG Yan-pei(School of Material Science and Engineering,Henan University of Science and Technology,Luoyang 471003,China);Present situation and prospect of foundry techniques for bimetallic compound rolls[J];Materials Research and Application;2010-03
3 ZHANG Chun-you(Hunan Institute of Metallurgy and Materials,Changsha 410014,China);Research on the Cracking Mechanism of a Steel-bonded Carbide[J];Metal Materials and Metallurgy Engineering;2009-02
4 LI Wen-hu,XU Feng,AI Tao-tao,FENG Xiao-ming(School of Material Science and Engineering,Shaanxi University of Technology,Hanzhong 723003,China);Effects of heat treatment on microstructure and properties of Mo_2FeB_2 cermet synthesized by in situ liquid phase sintering[J];Transactions of Materials and Heat Treatment;2010-04
【Secondary Citations】
Chinese Journal Full-text Database 3 Hits
1 Han Fenglin(Beijing Powder Metallurgy Company, Beijing 100050);CHARACTERISTIC Of ANCORDENSE ̄(TM) WARM COMPACTION[J];POWDER METALLURGY TECHNOLOGY;1995-04
2 Guo Shiju,Lin Tao and Li Mingyi (University of Science and Technology Beijing,Beijing 100083);Equation for Predicting the Glass Transition Temperature of Binder Using for Warm Compaction Process[J];POWDER METALLURGY TECHNOLOGY;1997-02
3 S.St Laurent,F.Chagnon (Quebec Metal Powders Limited) Yan Xiaoxiong (Winlink Industrial Resource ltd.);Designing Robust Powder Mixes for Warm Compaction[J];POWDER METALLURGY TECHNOLOGY;1998-01
©2006 Tsinghua Tongfang Knowledge Network Technology Co., Ltd.(Beijing)(TTKN) All rights reserved